Abstract:The Ni-based IN792 superalloy is widely applied as a component in industrial turbines and aircraft engines due to its good high-temperature properties and excellent corrosion resistance. Since these components have to suffer from cyclic thermal and mechanical stresses during service, the high-temperature fatigue failure becomes one of the major factors affecting their service lives. Grain refinement has been considered as an effective way to improve the mechanical performance of superalloys. However, due to the complexity of alloy composition, microstructure and service condition, there is no unified theory about the influence of grain refinement on the fatigue performance and fracture mechanism of superalloys. In the present research, the IN792 superalloy with different grain sizes was manufactured. Then, fully reversed, strain-controlled, low-cycle fatigue (LCF) tests with four different total strain amplitudes were carried out on the alloy at 700 °C and 800 °C to clarify the effects of grain refinement on its LCF behavior. The results show that grain refinement improved the fatigue life significantly, which is mainly attributed to increasing the grain boundary content and refining MC carbides, eutectic structures and dendritic structures. During fatigue test under lower strain amplitude, the alloy exhibits a pronounced initial fatigue hardening followed by a continuous well-defined stability stage, which is caused by the formation of dislocation networks and coarsening of primary γ’ phases. However, during fatigue test under higher strain amplitude, the alloy exhibits continuous hardening response because the dislocations could shear primary γ’ phases, which could give rise to resistance to dislocation movement. In addition, the fracture surface observation shows that the fatigue fracture mode is mainly affected by the total strain amplitude. Under lower total strain amplitude, the fatigue microcracks mainly initiate at the porosities near the specimen surface, while under higher total strain amplitude, the fatigue microcracks tend to form at the interior of the specimen.

Effect of surface recrystallization on the low cycle fatigue behavior of directionally solidified superalloy DZ4 by in-situ SEM studies

Effect of Recrystallization on Low-Cycle Fatigue Behavior of DZ4 Directionally-Solidified Superalloy

In situ SEM studies of the low cycle fatigue behavior of DZ4 superalloy at elevated temperature: Effect of partial recrystallization

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

On the fatigue small crack behaviors of directionally solidified superalloy DZ4 by in situ SEM observations

In-situ scanning electron microscopy studies of small fatigue crack growth in recrystallized layer of a directionally solidified superalloy

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

On the Fatigue Short Crack Behaviors of Directionally Solidified Superalloy Dz4 by in Situ Sem Observations

The Analysis on the Low Cycle Fatigue Behavior of A Directionally Solidified Superalloy with Recrystallized Surface Layers

Effect of Surface Recrystallized Grains on the Fatigue Performance of Turbine Blade DZ4 Alloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Parametric Study of Cyclic Plasticity Behavior in a Directionally Solidified Superalloy with Partial Recrystallization by Crystal Plasticity Finite Element Simulation

Influence of Surface Recrystallization on the Low Cycle Fatigue Behaviour of A Single Crystal Superalloy

Effect of Local Recrystallized Grains on the Low Cycle Fatigue Behavior of a Nickel-Based Single Crystal Superalloy

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

Microstructure sensitivity of the low cycle fatigue crack initiation mechanisms for the Al 0.3 CoCrFeNi high entropy alloy: in-situ SEM study and crystal plasticity simulation

In-situ Observations of the Effects of Orientation and Carbide on Low Cycle Fatigue Crack Propagation in a Single Crystal Superalloy

Effects of Grain Refinement on the Low-Cycle Fatigue Behavior of IN792 Superalloys

Creep–fatigue Interaction Behavior of Nickel-Based Single Crystal Superalloy at High Temperature by In-Situ SEM Observation