Abstract:Good gas permeability is an essential factor for the smooth operation and high performance in the lower part of the blast furnace. Under the present low carbon blast furnace smelting conditions, the coke layer is thinner, and the proportion of the molten metal in the coke layer is significantly higher, resulting in a major reduction in gas permeability, which seriously affects blast furnace operations. Also, the lower thickness of the coke layer weakens the process of solid-liquid carbon dissolution when the molten iron passes through the coke layer, which reduces the carbon content of the molten iron and further deepens the erosion of the refractory by the unsaturated molten iron. The carbon dissolution in the molten iron in a blast furnace core was measured by a high-temperature vacuum wettability test tool that analyzed the interface wetting activity between Fe−C melts with specific carbon mass fraction (3.8%, 4.3%, 4.8%) and 99.9% of high temperatures graphite plates. Besides, the scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the graphite substrate’s carburizing morphology and carburizing distances. The results show that, with the increase of carbon content, the interface contact angle becomes bigger. The contact angle decreases with time, and eventually reaches a steady-state during the melting process, and the Fe−C melt with saturated carbon cannot be wet. The scanning electron microscopy analysis shows that a spherical cap-like depression is created by a cross-section of the Fe−C melt and the graphite substrate, and the radius and volume of the depression decrease with increasing carbon content. The study of the EDS scanning analysis shows that the amount of dissolved carbon atoms in the graphite substrate penetrates the Fe−C melt and decreases with increasing initial carbon concentration. The smaller the carburizing effect, the better the wetting is conducive to carbon mass transfer. It is found that by measuring carburizing of the carbon atoms in the graphite substrate into the Fe−C melt by calculating the surface energy reduces the surface energy between the two. Thus, the surface tension decreases and the melt spreads slowly with contact angle gradually decreasing during melting.

Effect of Temperature on CH4/CO Carburization Process of Hydrogen‐Based Direct Reduced Iron Pellets

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Iron Carburization In Co-H-2-He Gases, Part I: Experiment

Reduction kinetics of iron oxide pellets with H2 and CO mixtures

Effect of Mixed Charging of Nut Coke and Sinter on Hydrogen-Rich Smelting Process of Blast Furnace

Study on the reduction of Fe2O3 pellets by CO-CO2 and H2-H2O: Reaction kinetics and pore network model

Investigation of reduction behavior of various iron ores in a hydrogen-rich reducing atmosphere

Effect of Hydrogen Concentration in Reducing Gas on the Changes in Mineral Phases during Reduction of Iron Ore Sinter

Effect of blast furnace coke graphitizing its high temperature metallurgical properties

Practice and Theoretical Analysis about Effect of H2 Content on Ironmaking Process

Effect of reduction and carburization pretreatment on iron catalyst for synthesis of light olefins from CO hydrogenation

Experimental Study on Impact of Iron Coke Hot Briquette As an Alternative Fuel on Isothermal Reduction of Pellets under Simulated Blast Furnace Conditions

Reduction of Iron‐Ore Pellets Using Different Gas Mixtures and Temperatures

Effect of different forms of carbon on the reduction behaviour of iron ore-carbonaceous material composite pellets in multi-layer bed rotary hearth furnace (RHF)

Direct Reduction of Iron Ore Pellets by Using CO/CO2 and CO Gases

The Influence of Nitrogen on Hydrogen Reduction of Iron Ore Pellets

Effect of pressure on direct reduction of mineral iron carbonate with hydrogen

Effect of carburization protocols on molybdenum carbide synthesis and study on its performance in CO hydrogenation

Structure Characteristics and Removal Behavior of the Deposited Carbon on Ni-Al2O3 Catalyst for CO2 Reforming of CH4

Hydrogen-based direct reduction of industrial iron ore pellets: Statistically designed experiments and computational simulation

Investigation of methane decomposition and carburization with iron: the combination of a ReaxFF molecular dynamics simulation and experimental work