Abstract:ZnO nanorods were grown on ITO substrates with different concentration of electrolyte by electrodeposition method. Microstructure, surface topography, photoluminescence Spectra, Raman spectra and water contact angle of the thin films were measured. The XRD results show all samples are hexagonal wurtzite and the intensity of diffraction peaks at (002) preferred orientation are strengthen as electrolyte concentration increase from 0.005 to 0.03 M. As the concentration increases, the average diameter, density and inclination of the ZnO nanorods increased. Room temperature photoluminescence spectras of the ZnO nanorods show a narrow UV band centering at about 377 nm and broad visible emissions around 600 nm and the UV peak intensity revealed a remarkable decreased. Raman spectras exhibit three peaks which are located at 439 cm(-1), 562 cm(-1) and 1095 cm(-1). All samples change from hydrophobicity to hydrophilic after one hour ultraviolet (UV) irradiation. (C) The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org. All rights reserved.

Photoluminescence Properties of ZnO Nanorods Prepared under Low Temperature

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Low Temperature Synthesis and Optical Properties of Small-Diameter ZnO Nanorods

Temperature-Dependent Photoluminescence of Zno Nanorods Prepared by A Simple Solution Route

Preparation and photoluminescence of ZnO nanorods

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Hydrothermal Preparation and Photoluminescence Property of Co-Doped ZnO Nanorods

Photoluminescence Properties of Co-doped ZnO Nanorods Array Fabricated by the Solution Method

Preparation and characterization of ZnO nanorods

Photoluminescence of Ga-doped ZnO Nanorods Prepared by Chemical Vapor Deposition

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Low temperature growth and properties of ZnO nanorod arrays

Nitrogen-doped ZnO nanorods prepared by hydrothermal diffusion

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Optical Properties of Na-Doped Zno Nanorods Grown by Metalorganic Chemical Vapor Deposition

Photoluminescence and Low-Threshold Lasing of ZnO Nanorod Arrays.

A Novel Low-Temperature Method to Grow Single-Crystal Zno Nanorods

Synthesis and Luminescent Property of Single-Crystal Zno Nanobelts by A Simple Low Temperature Evaporation Route