Abstract:Anatase/rutile mixed-phase TiO2 nanoparticles were synthesized through a simple sol-gel route with further calcination using inexpensive titanium tetrachloride as a titanium source, which effectively reduces the production cost. The structural and optical properties of the prepared materials were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and UV-vis adsorption. The specific surface area was also analyzed by Brunauer−Emmett−Teller (BET) method. The anatase/rutile mixed-phase TiO2 nanocomposites containing of rod-like, cuboid, and some irregularly shaped anatase nanoparticles (exposed {101} facets) with sizes ranging from tens to more than 100 nanometers, and rod-like rutile nanoparticles (exposed {110} facets) with sizes ranging from tens to more than 100 nanometers. The photocatalytic activities of the obtained anatase/rutile mixed-phase TiO2 nanoparticles were investigated and compared by evaluating the degradation of hazardous dye methylene blue (MB) under ultraviolet light illumination. Compared to the commercial Degussa P25-TiO2, the mixed-phase TiO2 nanocomposites show better photocatalytic activity, which can be attributed to the optimal anatase to rutile ratio and the specific exposed crystal surface on the surface. The anatase/rutile TiO2 nanocomposites obtained at pH 1.0 (pH1.0-TiO2) show the best photocatalytic activity, which can be attributed to the optimal heterojunction structure, the smaller average particle size, and the presence of a specific exposed crystal surface. The enhanced photocatalytic activity makes the prepared anatase/rutile TiO2 photocatalysts a potential candidate in the removal of the organic dyes from colored wastewater.

Photocatalytic Activity of Pure Rutile Particles Derived from A Photo-Assisted Sol-Gel Method

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Synthesizing and Comparing the Photocatalytic Properties of High Surface Area Rutile and Anatase Titania Nanoparticles

The Preparation of Rutile TiO<sub>2</sub> Nanopowders, Phase Transformation and Their Photocatalysed Properties

Highly Active Rutile TiO 2 for Photocatalysis

Preparation of nano rutile titania powders with high photocatalytic properties

Preparation of Coral-like Rutile Titania with Enhanced Photocatalytic Activity under UV and Visible Light

Facile Synthesis and Photocatalytic Property of Bicrystalline TiO2/rectorite Composites

Synthesis and Properties of Nano-Rutile Tio2 Photocatalysts

Properties and Photocatalytic Activity of Rutile TiO$lt;inf$gt;2$lt;/inf$gt; Nanosheets

Facile Formation of Anatase/Rutile TiO2 Nanocomposites with Enhanced Photocatalytic Activity

Facile Formation of Anatase/Rutile TiO<sub>2</sub> Nanocomposites with Enhanced Photocatalytic Activity

Microstructure and Photocatalytic Activity of Natural Rutile from China for Oxidation of Methylene Blue in Water

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Synthesis of nanocrystalline rutile titania by Co-thermal hydrolysis of TiCl4 and TiCl3 solutions

Photocatalytic Activity of Titania Prepared by Sol-Gel Method for Air Cleaning

Preparation and Photocatalytic Activity of TiO2 with Different Crystal Structures

Photocatalysis of V-bearing rutile on degradation of halohydrocarbons

Photocatalytic activity of TiO 2 prepared at low temperature by a photo-assisted sol-gel method

Well-designed Submicron Rutile Pigment Heterophase Junction Photocatalyst Via Sol-Gel Method for Organic Pollutants Removal

Microemulsion-mediated solvothermal synthesis and photocatalytic properties of crystalline titania with controllable phases of anatase and rutile.