Growth and Properties of ZnO Nanorod with UV-Light

Ya-qing BIE,Ying-bo YE,Zi-min ZHAN,San-jing LIN,Dong ZHENG,Yin-shu WANG
DOI: https://doi.org/10.3969/j.issn.1003-353X.2007.08.009
2007-01-01
Abstract:ZnO nanorods of average diameter 17 nm were fabricated in solution of zinc acetate and hexamethylene tetramine on glass and Si substrates with ZnO seeds preformed by annealing method.The nanorod structure,morphology and preferential ordered array were characterized by X-ray diffraction(XRD) and scan electron microscope(SEM).Emission of the nanorods was measured by photoluminescence(PL) spectroscopy.Influences of seeds,substrates and substrate placed style on nanorod diameter,preferential ordered array and photoluminescence properties were studied.The nanorod diameters were dependent on the initial state of substrates,and seeds preformed could decrease the rod diameter dramatically and improve the ordered arrangement,but the nanorod properties were independent on the type of substrates once ZnO seeds were preformed on the substrates,and the nanorods had strong UV emission.The nanorod morphology and array would be affected by the placed style of the substrates.The nanorods grown on the upright placed substrate show smaller diameter and better uniformity and ordering.
What problem does this paper attempt to address?