Abstract:Czochralski (CZ) silicon is a base material for manufacturing integrated circuits (ICs). The mechanical strength of CZ silicon determines the processing limitations and often dominates the issues related to packaging and failure of ICs. With the ever-smaller feature size of ICs, the scaling of device dimensions may indirectly lead to increase the stress in silicon substrate, thus increasing the probability of generating dislocations. Consequently, improving the mechanical strength of CZ silicon is of significance for increasing the manufacturing yield of ICs. In this work, we propose a strategy of co-doping germanium (Ge) impurity and nitrogen (N) impurity into CZ silicon to achieve better mechanical strength. In order to explore the feasibility of such a strategy, we comparatively investigate the room-temperature hardness and dislocation gliding behaviors in the temperature range of 600–1200 ℃ in the conventional CZ silicon, Ge-doped CZ silicon, N-doped CZ silicon, as well as N and Ge co-doped CZ silicon. The significant experimental results are described as follows. 1) Ge-doping, N-doping or co-doping of Ge and N hardly influences the hardness and therefore the dislocation gliding behavior at room temperature. 2) The suppressing effect of N-doping on the dislocation gliding is remarkable at 600–1000 ℃ and becomes weakened at the temperatures higher than 1100 ℃, while Ge-doping hardly affects the dislocation gliding at 600–900 ℃ but exhibits a strong suppressing effect on the dislocation gliding at 1000–1200 ℃. 3) Co-doping Ge and N impurities into CZ silicon can take the complementary advantages of both Ge- and N-doping to suppress the dislocation gliding at 600–1200 ℃. It is believed that N-doping can result in the formation of N-O complex-related pinning agents within the dislocation cores to suppress the dislocation gliding at 600–1000 ℃. For Ge-doping, it is supposed that Ge-O complexes acting as the pinning agents can form near the front of a single dislocation when the temperature is as high as 1000 ℃ and above. In a word, it is verified in this work that co-doping Ge and N into CZ silicon can further improve the mechanical strength at the processing temperatures of ICs fabrication.

Flow Pattern Defects in Germanium-Doped Czochralski Silicon Crystals

On the Assumed Impact of Germanium Doping on Void Formation in Czochralski-Grown Silicon

Characterization of a Czochralski Grown Silicon Crystal Doped with 1020 Cm‐3 Germanium

Micro-defects in Ge doped Czochralski grown Si crystals

Grown-in Defects in Heavily Phosphorus-Doped Czochralski Silicon

Germanium effect on void defects in Czochralski silicon

Crystal-originated Particles in Germanium-Doped Czochralski Silicon Crystal

Germanium in Czochralski Silicon

Electron Irradiation Induced Defects In Germanium-Doped Czochralski Silicon Substrates And Diodes

On the Impact of Heavy Doping on Grown-In Defects in Czochralski-Grown Silicon

Delineation of Flow Pattern Defects in Heavily Boron-doped Czochralski Silicon Wafer

Germanium Doping of Si Substrates for Improved Device Characteristics and Yield

Characterization of a Czochralski grown silicon crystal doped with 10 20 cm-3 germanium

Ge-vacancy Pair in Ge-doped Czochralski Silicon

High temperature nucleation of oxygen precipitates in Germanium-doped Czochralski silicon

Grown-In Defects in Heavily Boron-Doped Czochralski Silicon

Denuded Zone Formation in Germanium Codoped Heavily Phosphorus-Doped Czochralski Silicon

Mechanical Strength of Czochralski Silicon Crystal: Effects of Co-Doping Germanium and Nitrogen

Defects in Ge-doped Cz-Si Annealed under High Stress

Effects of Co-Doping Nitrogen and Germanium on Dislocation Gliding in Czochralski Silicon: Implication for Improving Mechanical Strength

Effect of Germanium Codoping on the Grown‐In Oxide Precipitates in Nitrogen‐Doped Czochralski Silicon