Abstract:When two surfaces in static contacts are subjected to combined loads applied in the normal and tangential directions, or just a normal load for dissimilar materials, microscopic slip would take place at certain areas of the contact region even though the contacting bodies remain still without macroscopic movement. The micro-slip is considered a major cause of fretting wear for the materials in contacts under alternating dynamic load or vibration, referred as the fretting contacts in this study. The fretting contact problem was solved using a semi-analytical method (SAM), in which analytical relations between a unite stress and corresponding surface displacement were obtained on the basis of Green functions. The contact pressure and shear tractions were then calculated by minimizing the complementary energy, and by a numerical procedure based on Conjugate Gradient Method (CGM) and Fast Fourier Transform (FFT) technique. The algorithm is very effective since the meshes are applied to the positions just in the contact areas of interest, which saves the computing time. The fretting contacts of dissimilar materials were studied and the effects of surface roughness were analyzed. Results show that the coupled effects of shear traction and material dissimilarity make the traction distributions quite different with the solutions from similar materials. The solutions under dynamic load depend on the path or history of the loading process, but the stress distributions and load-displacement curves will quickly converge to a periodic stability after several load cycles.

Status of Test Methods for Contact Materials Fretting Wear Characteristics

Experimental Research on Fretting Wear Characteristics of Au-Plated Copper Contacts Used in Electrical Connectors

Understanding the Fretting Failure Mechanisms in Gold-Plated Contact Materials

Mechanical behavior and fatigue life estimation on fretting wear for micro-rectangular electrical connector.

Review of Fretting Wear for Electrical Connector

Fretting Behavior of Gold-Plated Contact Materials Used in High-Frequency Vibration and Different Temperature Environment

Research on Fretting Regimes of Gold-Plated Copper Alloy Electrical Contact Material under Different Vibration Amplitude and Frequency Combinations

Fretting Behavior of Au Plated Copper Contacts Induced by High Frequency Vibration

Study of fretting wear mechanisms of complete contacts

Numerical Study of Coupled Electrical-Thermal-Mechanical-Wear Behavior in Electrical Contacts

Literature Review on Fretting Wear and Contact Mechanics of Tribological Coatings

Fretting wear behavior of brass/copper-graphite composites as a contactor material under electrical contact

Effects of Current Load on Wear and Melt Erosion of Electrical Contacts under Fretting Condition

Finite Element Simulation of Fretting Wear Behaviors under the Ball-on-flat Contact Configuration

A comparative study on the electrical contact behavior of CuZn40 and AgCu10 alloys under fretting wear: Effect of current load

Fretting Wear Behavior and Damage Mechanisms of Inconel X-750 Alloy in Dry Contacts

A New Automated Test Equipment for Measuring Electrical Contact Resistance of Real Size Rivets

Review on testing methods of tooth surface friction of the gear system

A Numerical Solution For Fretting Contacts

Experimental Investigation and Numerical Simulation on the Role of Sphere Indenter in Measuring Contact Resistance of Flat Rivets.

Experimental and finite element analysis for evaluating influence of contact pressure on fretting fatigue mechanisms of A319‐T6 cast aluminum alloy