Effects of Fe and Cr on corrosion behavior of ZrFeCr alloys in 500°C steam
Jun Wang,Hongyuan Fan,Ji Xiong,Hong Liu,Zhi Miao,Shihao Ying,Gang Yang
DOI: https://doi.org/10.1016/j.nucengdes.2010.11.014
IF: 1.7
2011-01-01
Nuclear Engineering and Design
Abstract:Research highlights Amount and size of SPP will effect the corrosion resistance of Zr alloy at 500 °C/10.3 MPa. Abstract A study of the corrosion behaviors of ZrFeCr alloy and the influence of microstructure on corrosion resistance are described by X-ray diffraction and scanning electron microscope in this paper. The results show that several ZrFeCr alloys exhibit protective behavior throughout the test and oxide growth is stable and protective. The best alloy has the composition Zr1.0Fe0.6Cr. Fitting of the weight gain curves for the protective oxide alloys in the region of protective behavior, it showed nearly cubic behavior for the most protective alloys. The Zr1.0Fe0.6Cr has the more laves Zr(Fe,Cr) 2 precipitate in matrix and it has the better corrosion resistance. The Zr0.2Fe0.1Cr has little precipitate, the biggest hydrogen absorption and the worst corrosion resistance. The number of precipitates and the amount of hydrogen absorption in Zr alloy plays an important role on corrosion resistance behaviors in 500 °C/10.3 MPa steam. 1 Introduction Zirconium alloys are generally used as cladding and structural materials in light and heavy water nuclear reactors due to their excellent neutron economy and corrosion resistance, and good mechanical properties under irradiation ( Charquet, 2001; Sabol, 2005; Mukherjee et al., 2002 ). In China, N18 and N36 alloys have been developed on the base of Zr–Sn and Zr–Nb systems to meet the requirements of higher fuel burn-up in pressurized water reactor (PWR) ( Li et al., 2007 ). But most of used and developed zirconium alloys are suitable for 360 °C, which cannot meet the need for future high temperature water/steam reactors. Fuel cladding and other core components are expected to operate at 450–550 °C and to be subjected to a potentially corrosive environment in reactor designed for the future. But little knowledge exists of the behavior of zirconium alloys and other materials under these conditions and several candidate alloys are currently being tested for possible use in these reactors ( Jeong et al., 2003 ). Earlier work indicated that some high alloying content Zr alloys showed promise for high temperature corrosion applications ( Jeong et al., 2006; Sabol et al., 2000 ). Some researchers reported that the ferritic–martensitic alloys, such as T91, HCM12A and HT-9, have poor corrosion resistance in 500 °C supercritical water (SCW) ( Ampornrat and Was, 2007; Was et al., 2007 ). As part of a research program to assess the corrosion behavior of Zr alloys under SCW, Motta et al. (2007) have performed extensive corrosion testing of model Zr alloys under SCW (2006). They reported that proper Fe and Cr additions induce protective oxide growth in Zr alloys, such that, from the corrosion point of view, Zr alloys should be considered as possible candidate materials for application in SCW reactors. The beneficial effect of Fe has been demonstrated by comparing the corrosion resistance of the binary Zr–Cr alloys with Zr–Cr–Fe ternary alloys when the latter proved superior ( Motta et al., 2007 ). Although the effects of some elements on properties of Zr alloys have been studied widely, this is mostly for the condition of 360 °C/18.6 MPa water. There have been few systemic reports on the effect of iron and chromium on the corrosion behaviors, hydrogen absorption and microstructural change of ZrFeCr alloys in hot steam. So this study focuses on the effect of component content on these properties in 500 °C steam. 2 Experimental methods The chemical compositions of the Zr alloys used in this study are shown in Table 1 . Button ingots of approximately 50 g were prepared by arc melting under an argon atmosphere and remelted at least five times to promote the homogeneity of the as-cast structure. The arc-melted ingots were β-solution treated at 1020 °C for 30 min in a vacuum furnace, hot-rolled after preheating to 610 °C for 10 min and cold-rolled three times to a final thickness of 1 mm. Between the rolling steps, the cold-rolled sheets were intermediate-annealed at 575 °C for 3 h to obtain the fully-recrystallized structure. The final cold-rolled sheets were annealed at 510 °C for 2.5 h to obtain the partially recrystallized metallurgical form. Table 1 lists the alloys prepared and used in this study, and the target compositions. The actual compositions were measured and did not vary from the target composition. Specimens for corrosion testing, measuring 30 by 20 by 0.8 mm, were cut from the manufactured strip, mechanically ground using 1200 grit SiC paper, and then pickled in a solution of 5 vol.% HF, 45 vol.% HNO 3 and 50 vol.% H 2 O. The corrosion tests were conducted in 500 °C/1500 psi (10.3 MPa) steam in a manner consistent with the ASTM Practice (G2-88). The corrosion behavior of the specimens was evaluated by measuring the weight gain as a function of exposure time. The hydrogen absorption of alloys was detected by a hydrogen instrument set. The phase transformation temperature of the test samples was measured using a NETZSCH DSC-404C differential scanning calorimeter (DSC), and a heatup/cooldown rate of 10 °C/min was adopted. 3 Results and discussion 3.1 Corrosion behavior The corrosion behavior of the Zr–Fe–Cr alloys used in this study is shown in Fig. 1 . The corrosion kinetics of the Zr alloys was compared with each other and the influence of the alloying element on the corrosion resistance of ZrFeCr was examined. Under the corrosion condition employed in this study, Zr1.0Fe0.6Cr (2-2 alloy), with the highest alloying content, showed the best corrosion resistance (protective stable oxide, low rates, no breakaway) among the alloys tested. The corrosion resistance of the Zr-4 alloy, usually used in lower temperature water reactors, has the worst corrosion resistance. The Zr-4 alloy showed the typical nodule corrosion mechanism and breakaway behavior right from the start in 500 °C/10.3 MPa condition. The Zr0.2Fe0.1Cr (1-1 alloy), with the lowest alloying content, showed the typical nodule corrosion method in 500 °C/10.3 MPa too. Motta et al. (2007) reported the Zircaloy-4, pure Zr showed breakaway behavior right from the start in 500 °C SCW and steam. The type Zr0.4Fe0.6Cr (2-4 alloy) has a good corrosion resistance at the beginning of test. But in the following stage, all the three pieces of 2-4 alloy samples were delaminated and gray oxide dropped from the aperture. The corrosion resistance curve was estimated by the depth of oxide film. The recently developed Zr alloy in China, N18 (Zr–1.0Sn–0.35Fe–0.1Cr–0.35Nb alloy) showed poor corrosion resistance in this study. The corrosion resistance of Zr1.0Fe0.6Cr (2-2) showed better than that of N18. In general, the corrosion test results showed a range of corrosion behavior depending on the alloy composition. The corroded appearance of Zircaloy samples after autoclave corrosion at 500 °C/10.3 MPa is shown in Fig. 1 . The type of Zr0.2Fe0.1Cr (1-1 alloy) shows the typical nodule corrosion at 500 °C/10.3 MPa. The oxides of the samples were loose and white in color, and these have no-protective effect. After 50 h in the test, the oxide had broken away. However, the type of Zr1.0Fe0.6Cr (2-2 alloy) showed the typical uniform corrosion at 500 °C/10.3 MPa. Even after 1300 h at 500 °C/10.3 MPa, the stable oxide film was black and shine all are, which has more protective effect. 3.2 Microstructure characterization The typical microstructures of the alloys were found to consist mainly of recrystallized grains and a small portion of the worked structure, with a high density of dislocations. Fig. 2 shows the typical distribution of precipitates in a recrystallized grain of the alloys. It shows that the precipitates are randomly distributed within the grains and along the grain boundaries in both alloys. The 1-1 alloy (Zr0.2Fe0.1Cr) has a little amount of secondary precipitates, but 2-2 alloy (Zr–1.0Fe–0.6Cr) has a large amount of secondary precipitates. The EDS indicated the precipitate is Zr(Fe,Cr) 2 -type (in Fig. 2 d). The shapes of precipitates are diversiform. To study the second-phase particle (SPP) size and distribution more quantitatively, SEM investigations were performed. Samples in transverse section were etched to reveal the SPPs in secondary electron mode. The liner component was analyzed at 10 000 times magnification. A number of fields of view were randomly chosen to obtain at least 100 particles. From these fields of view, the particle diameters were determined by image analysis. The SPP data from the SEM analysis are summarized in Table 2 . The particle number density increased with increasing ∑(Fe + Cr) content from 0.313 particles per μm 2 at 0.3 wt% ∑(Fe + Cr) to about 3.923 particles per μm 2 at 1.6 wt% ∑(Fe + Cr). Fig. 3 shows the XRD profiles of 1-1 and 2-2 alloy after a recrystallization anneal at 580 °C. The figure indicates that the main phase of 1-1 alloy is α-Zr phase. The amount of secondary precipitate in Fig. 3 is so little that it cannot be detected, but the situation is different in the 2-2 alloy. There are α-Zr and a lot of secondary precipitates, which are identified as intermetallic Zr(Fe,Cr) 2 in XRD. This is compatible with the results of SEM and EDS. 3.3 Effects of alloying elements on corrosion behavior Fig. 4 shows the XRD profiles of Zr0.2Fe0.1Cr and Zr1.0Fe0.6Cr alloy after a certain term of super hot stream corrosion in 500 °C. The XRD results indicate the oxide of Zr0.2Fe0.1Cr alloy almost was monoclinic ZrO 2 . Compared with the Zr1.0Fe0.6Cr alloy, there are not only the diffraction peaks of monoclinic ZrO 2 , but also the peaks of tetragonal ZrO 2 and α-Zr matrix, which suggest that more alloy content can stabilize the tetragonal phase in the oxide. Previous research indicated more tetragonal phase, especial in superficial interface, was beneficial to corrosion resistance ( Jeong et al., 2003, 2006; Sabol et al., 2000 ). Judging by the Zr alloy corrosion resistance in this experiment, it can be suggested that more alloy content stabilized the tetragonal phase in the oxide film and increased the corrosion resistance of the Zr alloy, which agrees with Motta's reports ( Motta, 2006; Motta et al., 2007 ). The weight gain w (mg/dm 2 ) during the initial protective regime can be characterized by a law of the type: w = A t n where t is the exposure time (in days), n is a dimensionless constant, and A is a constant whose dimensions depend on the value of n . For each of the alloys tested, these constants were determined by least squares fitting of the weight gain curves. The calculated values of A and n and the sum content of (Fe + Cr) are shown in Table 3 . The results show that the values of n are in general higher during high temperature testing. Motta et al. (2007) reported there is not much difference in the calculated values of A and n at 500 °C among the different environments (such as steam, static SCW or dynamic SCW) for a given alloy. In general the values of A are much higher (30–35) than at 360 °C (for which values of about 7–10 exist), and for the precipitate-based alloys the value of n is close to being cubic ( n = 0.33–0.37) and is somewhat higher than the values calculated for 360 °C, which are of the order of 0.2–0.25 ( Yilmazbayhan et al., 2005 ). In contrast, the Zr-4 alloys exhibit a considerably higher value of n , near 1.6. The N18 alloy shows an intermediate value of n , at 0.73. This suggests that the alloying elements have an effect on the atomic transport in the oxide layer, likely by affecting the concentrations of oxygen vacancies that are responsible for transport of oxidizing species through the layer. When the ∑(Fe + Cr) is small, for instance 0.3 (in 1-1 alloy) and 0.32 (in Zr-4 alloy), the corrosion resistance is catastrophic, and the nodule corrosion mechanism occurs But when ∑(Fe + Cr) is moderate, for example 1.6 in 2-2 alloy, the corrosion resistance is the best of all test samples. With more ∑(Fe + Cr), the alloy atom will be precipitated from α-Zr matrix in rolling process and annealing treatment because Fe and Cr have poor solubility in the α-Zr phase. Charquet (2001) suggested the predominant factor is the number of precipitates in a Zr alloy in 500 °C/10.3 MPa. So the 2-2 alloy has more laves Zr(Fe,Cr) 2 precipitate in the matrix and has better corrosion resistance. The hydrogen absorption of Zr1.0Fe0.6Cr and Zr0.2Fe0.1Cr at 500 °C/10.3 MPa are 510 ppm and 5700 ppm, respectively, detected by a Hydrogen instrument set. Table 4 shows the effect of hydrogen absorption ( H a ) on α-Zr phase to β-Zr phase transformation temperature ( T α–β ). In the annealed condition, the α → β transformation point is 837.4 and 835 °C of 0.1Cr0.2Fe and 1.0Cr0.6Fe, respectively. After corrosion in certain term in hot stream, the hydrogen absorption amount is 5700 ppm in 0.2Fe0.2Cr alloy (after 50 h in 500 °C/10.3 MPa), and the α → β transformation point was shifted to 572.5 °C form 837.4 °C in annealed condition. But in 1.0Fe0.6Cr, the hydrogen absorption amount is 780 ppm after 1300 h at 500 °C/10.3 MPa, and the α → β transformation point was shifted to 796.4 °C. The amount of hydrogen absorption of the specimen containing fine precipitates was smaller than that of the specimen containing coarse ones ( Hatano et al., 1997 ). Rudling and Wikmark (1999) suggested that large intermetallics or clusters of small precipitates could form the sites of high hydrogen flux through the oxide film. If diffusion in the metal is not sufficient to disperse the incoming hydrogen, precipitation of hydrides occurs close to the interface. Nodules are formed due to accelerated corrosion resulting from the hydride formation. The Zr1.0Fe0.6Cr cladding alloy contains the smaller precipitates, so has the more corrosion resistance. It is possible that the particle number density or volume fraction of precipitates has sufficient influence in all of the ZrFeCr alloys to avoid breakaway. The fact that the alloy with the lowest alloying element content exhibits the earliest transition, indicates that differences in precipitate distribution could play a role in stabilizing the oxide layer against breakaway. 4 Conclusions A comparative study has been conducted to address the issue of susceptibility of ZrFeCr alloys to uniform corrosion in a 500 °C/10.3 MPa stream. Four model alloys were corrosion tested for periods up to 1300 h in 500 °C/10.3 MPa and a wide range of corrosion behavior was observed. Several ZrFeCr alloys exhibited protective behavior throughout the test and oxide growth was stable and protective. The best alloy had the composition Zr1.0Fe0.6Cr. Fitting of the weight gain curves for the protective oxide alloys in the region of protective behavior showed nearly cubic behavior for the most protective alloys. The oxides were also characterized to determine the oxide structures associated with protective and non-protective behavior and the preliminary conclusions are that the protective oxides have some tetragonal phase and non-protective oxide does not. The number of precipitates and the amount of hydrogen absorption in Zr alloy play important roles in corrosion resistance behavior in a 500 °C/10.3 MPa steam. The Zr1.0Fe0.6Cr has more laves Zr(Fe,Cr) 2 precipitate in its matrix and has better corrosion resistance. The Zr0.2Fe0.1Cr contains little precipitate, and has the worst corrosion resistance. Acknowledgements This work was carried out with the financial support from The Key Nuclear Fuel and Nuclear Materials Laboratory of China, PRC , under Grant Contract No. 9140C7004040603 . And the author (J.W.) would like to thank Prof. Zhao Wenjin of The Key Nuclear Fuel and Nuclear Materials Laboratory of China and Prof. Yao Meiyi of Shanghai Univ. for their valuable discussions during the course of the research. References Ampornrat and Was, 2007 P. Ampornrat G.S. Was Oxidation of ferritic–martensitic alloys T91, HCM12A and HT-9 in supercritical water J. Nucl. Mater. 371 2007 1 17 Charquet, 2001 D. Charquet Influence of precipitate density on the nodule corrosion resistance of Zr–Sn–Fe–Cr alloys at 500 °C J. Nucl. Mater. 288 2001 237 240 Hatano et al., 1997 Y. Hatano R. Hitaka M. Sugisaki M. Hayashi Influence of size distribution of Zr(Fe,Cr)2 precipitates on hydrogen transport through oxide film of zircaloy-4 J. Nucl. Mater. 248 1997 311 314 Jeong et al., 2003 Y.H. Jeong H.G. Kim D.J. Kim B.K. Choi J.H. Kim Influence of Nb concentration in the α-matrix on the corrosion behavior of Zr– x Nb binary alloys J. Nucl. Mater. 323 2003 72 80 Jeong et al., 2006 Y.H. Jeong S.Y. Park M. Lee B.K. Choi J.H. Baek J.Y. Park J.H. Kim H.G. Kim Out-of-pile and in-pile perfomance of advanded zirconium alloys (HANA) for high burn-up fuel J. Nucl. Sci. Technol. 43 2006 977 983 Li et al., 2007 Q. Li B. Zhou M. Yao W. Liu Y. Chu Corrosion behavior of zirconium alloys in super critical water at 550 °C/25 MPa 15th International Symposium on Zirconium in the Nuclear Industry June 25–28, Sunriver, Oregon, USA 2007 Motta, 2006 Motta, A.T., 2006. Advanced corrosion-resistant zirconium alloys for high burnup and generation 4 applications. International Nuclear Energy Research Initiative (I-NERI-2006 Annual Report). Available from: http://www.nuclear.gov . Motta et al., 2007 A.T. Motta A. Yilmazbayhan M.J. Gomes da Silva R.J. Comstock G.S. Was J.T. Busby E. Gartner Q. Peng Y.H. Jeong J.Y. Park Zirconium alloys for supercritical water reactor applications challenges and possibilities J. Nucl. Mater. 371 2007 61 75 Mukherjee et al., 2002 P. Mukherjee P. Barat S.K. Bandyopadhyay P. Sen S.K. Chottopadhyay S.K. Chatterjee M.K. Mitra Characterisation of microstructural parameters in oxygen irradiated Zr–1.0%Nb–1.0%Sn–0.1%Fe J. Nucl. Mater. 305 2002 169 174 Rudling and Wikmark, 1999 P. Rudling G. Wikmark Effect of additives on the susceptibility of zirconium alloys to nodular corrosion J. Nucl. Mater. 256 1999 44 Sabol, 2005 G.P. Sabol ZIRLO – an alloy development success J. ASTM Int. 2 2005 2942 Sabol et al., 2000 G.P. Sabol R.J. Comstock U.P. Nayak Effect of dilute alloy additions of molybdenum, niobium, and vanadium on zirconium corrosion G.P. Sabol G.D. Moan Zirconium in the Nuclear Industry, Twelfth International Symposium, ASTM STP 1354 2000 ASTM International West Conshohocken, PA 525 Was et al., 2007 G.S. Was P. Ampornrat G. Gupta S. Teysseyre E.A. West T.R. Allen K. Sridharan L. Tan Y. Chen X. Ren C. Pister Corrosion and stress corrosion cracking in supercritical water J. Nucl. Mater. 371 2007 176 201 Yilmazbayhan et al., 2005 A. Yilmazbayhan A.T. Motta H.G. Kim Y.H. Jeong J.Y. Park R. Comstock Proceedings of the 12th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors Snowbird, Utah, TMS 2005 201 210
What problem does this paper attempt to address?
-
Effect of Nb and Cu on α/β Phase Transition Temperature and Corrosion Behavior of New Type Zirconium Alloys
Wei LUO,Jun WAGN,Ji XIONG,Shi-hao YING,Xiao-xue YANG,Tai-ping ZHANG
DOI: https://doi.org/10.3969/j.issn.0258-0926.2012.01.019
2012-01-01
Abstract:The microstructure and the performance of corrosion resistance of Zr-Nb-Cu alloys have been investigated in the superheated steam of 500℃/10.3MPa.The results showed that the alloy Zr-1.0Nb-0.05Cu possessed the best corrosion resistance,which was far superior to that of Zr-4 and N18.The second phase par-ticles which contain Nb,Fe and Cr formed in Zr-Nb-Cu alloys,which was a factor that affected the corrosion resistance of Zr alloys.During heating up of Zr-Nb-Cu alloys in the DSC experiment,the corrosion induced hydride dissolved and hydrogen solutionizing in the matrix.When the temperature reached to α/β phase tran-sition temperature(about 550℃),β phase transformation occurred.The addition of Nb element can decrease the temperature of hydrogen-induced β phase transformation,and the increasing of Cu content can reduce the hydrogen absorbing amount,and improve the corrosion resistance of the alloy significantly.
-
Corrosion of New Zirconium Claddings in 500 °C/10.3 MPa Steam: Effects of Alloying and Metallography
Jing-Jing Liao,Zhong-Bo Yang,Shao-Yu Qiu,Qian Peng,Zheng-Cao Li,Ming-Sheng Zhou,Hong Liu
DOI: https://doi.org/10.1007/s40195-018-0857-7
2018-01-01
Abstract:With the aim of improving corrosion resistance of rod cladding for in-service and accident conditions, six new zirconium alloys (named N1–N6) have been designed. The contents of Sn and Nb were optimized for better behavior at high-temperature pressurized water, and Fe, Cr, V, Cu or Mo elements were added to the alloys to adjust the corrosion behavior. The current work focused on the rapid corrosion behavior in 500 °C/10.3 MPa steam for up to 1960 h, aiming to test the corrosion resistance at high temperature. The structure of matrix and properties of second-phase particles (SPPs) were characterized to find the main differences among these alloys. All the six alloys exhibited better corrosion resistance than N36, and N1 was shown to have the best performance. A careful analysis of the corrosion kinetics curves revealed that Cr was beneficial for severe condition. Elements Fe, Cr, V, Cu or Mo aggregated into SPPs with different concentrations and structures. This was demonstrated to be the main reason for different corrosion resistance. Due to good processing control, all alloys had a uniform structure and a uniform distribution of SPPs. As for N4, N6 and N36, the existing of large-size SPPs (450 nm) might be a contributing factor of the relatively poor corrosion resistance.
-
Corrosion of Zr-Sn-X (X: Fe, Ni or Cr) Ternary Alloy in High Pressure Steam at High Temperature
H. Maki,M. Inagaki,M. Izumiya
DOI: https://doi.org/10.3323/JCORR1991.42.354
1993-06-15
Abstract:Effects of the addition of Fe, Ni, or Cr to Zr-Sn binary alloy and material processings on corrosion resistance in high temperature,, high pressure steam were investigated in order to make clear the correlation between corrosion resistance of Zr alloy and electrical characteristics of oxide film. The increase of Fe or Ni content in Zr-Sn alloy improved the corrosion resistance, whereas with the increase of Cr content, improvement of corrosion resistance was not remarkable. Corrosion resistance was also improved by the heat treatment which depresses the precipitation and the growth of intermetallic compounds containing Fe, Ni, or Cr. From the facts that the increase of Fe or Ni content and the heat treatment to improve the corrosion resistance decrease the electrical conductivity of the oxide film formed on Zr alloys, electrical conductivity of oxide film is considered to be the rate-determining factor in oxidation of Zr alloys in high temperature, high pressure steam.
Engineering,Materials Science
-
Enhanced Mechanical Properties and Wear Resistance of FeCrAl Alloys at ~ 300°C and Higher Temperatures
Evan J. Dolley,Wanming Zhang,Gilad Zorn,Tommy Sand,Raul B. Rebak
DOI: https://doi.org/10.1007/s11837-024-06540-3
2024-04-24
JOM
Abstract:Abstract Worldwide, light water reactors (LWRs) have been using zirconium (Zr)-based alloys for the cladding of the uranium dioxide fuel for more than 6 decades. Zr alloys oxidize rapidly in the presence of water and steam at temperatures > 450°C; therefore, they do not respond well to scenarios of loss of coolant accidents. There is a global effort by nuclear materials technologists to find more robust or stronger cladding materials for LWRs. One option is to use an iron-chromium-aluminum (FeCrAl) alloy since they have excellent resistance to high temperature oxidation and superior mechanical properties at LWR operation temperatures. Results show that (1) FeCrAl alloys have better mechanical properties than Zr alloy and are orders of magnitude more resistant to creep at temperatures higher than LWR normal operation conditions. (2) FeCrAl alloys have better resistance to fretting wear than Zr alloys at the normal operation conditions of LWRs.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mineralogy,mining & mineral processing
-
Effect of Cr/Al Atomic Ratio on the Oxidation Resistance in 1200°C Steam for the CrAlSiN Coatings Deposited on Zr Alloy Substrates
Han Zhu,Haiyong Liu,Feng Huang,Jun Yi,Fangfang Ge
DOI: https://doi.org/10.1007/s11837-019-03839-4
2019-10-15
JOM
Abstract:Cr-based physical vapor deposition coatings have been considered as having the potential to enhance the accident tolerance of Zr alloy fuel claddings. Comparative studies on the high-temperature oxidation behavior were conducted on the Zr alloy coupons that were coated with magnetron-sputtered CrAlSiN quaternary coatings with various Cr/Al atomic ratios. It has been found that the oxidation resistance and the external scale are closely associated with the Cr/Al atomic ratio. A Cr/Al ~ 3.1 coating provided effective protection for its Zr alloy substrate in 1200°C steam for 6 h, where a dense and homogeneous Cr2O3/α-Al2O3 bilayer scale was evidenced in the whole process. However, for Cr/Al ~ 1.3 and the Cr/Al ~ 0.6 coatings, their oxidation resistance was greatly degenerated, because of the forming of brittle α-Al2O3-rich scales. The results demonstrate that the Cr/Al atomic ratio is crucial to the protective capability of CrAlSiN coatings for Zr alloy coupons in high-temperature steam.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy
-
Corrosion Properties of Cr Coating Deposited on Nuclear Fuel Cladding
Hyun-Gil Kim,Y. Jung,D. Park,Jung-Hwan Park,Young-ho Lee,Byoung-Kwon Choi
Abstract:Zirconium alloys have been used as primary materials for fuel cladding which protect the nuclear fuel from the outside in the nuclear power system. Zirconium alloys have very low absorption cross-section of thermal neutrons, high hardness, ductility, and corrosion resistance [1]. However, they had problems with nuclear reactor safety as they reacted violently with steam at high temperature, producing large amounts of hydrogen and heat, and having low mechanical strength at high temperature. Moreover, a massive hydrogen explosion by zirconium-steam interaction occurred at the Fukushima Daiichi nuclear power plant. The development of accident-tolerant fuel cladding has been widely studied since the Fukushima nuclear reactor accident [2]. Ideas and new concepts have been proposed for accident-tolerant fuel cladding to prevent hydrogen explosion by inhibiting reaction with steam in the accident environment. Therefore, the ATF research was actively carried out in the early development period to replace zirconium alloys using materials such as SiC, FeCrAl, etc., which have oxidation resistance better than zirconium [3,4]. However, the phenomenon of dissolution in cooling water under normal operating conditions was observed, and some materials had lower economic feasibility because the neutron absorption cross-section area was larger than zirconium. To overcome these problems, many researches are underway to take both stability and economy by coating the surface of zirconium cladding. By applying coating technology to zirconium cladding, it is easy to obtain corrosion resistance without a change in the base materials. Recently, Terrani et al. reported the oxidation resistance of Fe-based alloys for protecting zirconium alloys from the rapid oxidation in a high-temperature steam environment. Kim and co-workers also reported the corrosion behavior of Cr-coated zirconium alloy using a plasma spray and laser beam scanning [5]. In the present work, Cr anti-oxidation coating was fabricated on a commercial Zircaloy-4 cladding using cathodic arc ion plating (CAIP) because cathodic arc ion plated films tend be denser and have better adhesion characteristics than films produced using other method [6]. The Cr system was selected because of its good corrosion resistance. The microstructures of arc ion plated Cr coating were characterized. The oxidation behavior of the coating was analyzed. . 2. Experimental CAIP is well recognized method of producing protective coatings due to its high ionization efficiency and excellent film adhesion. It is a promising method for depositing oxidation-resistant coatings on nuclear fuel claddings. Pure Cr coating was deposited on the Zircaloy-4 using the CAIP with Cr target (99.59% purity). Figure. 1 shows the CAIP system which was designed to coat protective film onto the surface of a nuclear cladding. The substrates were cleaned ultrasonically in acetone and an ethanol solution, and the substrates were then mounted in a vacuum chamber. The chamber was evacuated to a pressure of 1 x 10 Torr, and heated simultaneously to 1473 K to remove the residual gas adsorbed on the chamber wall and substrates. Prior to the deposition, the substrates were sputter cleaned using Ar ions under -400V negative bias voltage for 5 min. Cr ion bombardment was applied to remove contaminants and ensure good adhesion of deposited coatings. The deposition of Cr was carried out in an Ar atmosphere with a pressure of 20mTorr. In order to study the effects of negative bias voltage, different negative bias voltages ranging from -25 to -100V were applied. After deposition, the coatings were polished to reduce the influence of the roughness, as well as for more precise measurements.
Engineering,Materials Science,Physics
-
Improved oxidation resistance of Cr/FeCrAl coating on Zr alloy in high-temperature steam environment
Xiaoling Yang,Baifeng Luan,Lijun Chen,Jinlong Wu,Pengzhou Zhu,Hongling Zhou,Haibo Ruan,Weijiu Huang,Chao Sun,Shaoyu Qiu
DOI: https://doi.org/10.1016/j.surfcoat.2023.129992
IF: 4.865
2023-09-08
Surface and Coatings Technology
Abstract:A new bi-layer Cr/FeCrAl coating was successfully fabricated on the Zr-4 plates through multi-arc ion plating in order to take advantage of the two materials of FeCrAl and Cr. The high-temperature steam oxidation behavior of the Cr/FeCrAl-coated Zr-4 at 1000–1200 °C was investigated and compared with that of bare and single-layer FeCrAl-coated Zr-4. Various analytical techniques including scanning electron microscopy with energy dispersive spectroscopy (SEM/EDS), X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used for the microstructural and compositional analysis of the as-deposited and oxidized samples. Results indicated that the FeCrAl-coated Zr-4 could only withstand up to 1000 °C because of the severe FeZr interdiffusion. Whereas the introduction of the Cr interlayer effectively prevented fast FeZr interdiffusion and consequently improves the overall oxidation resistance of the Zr substrate below 1200 °C steam environment. After 1100 °C steam oxidation, the weight gain of the Cr/FeCrAl-coated Zr-4 was about 8 times and 2 times lower than that of the uncoated and FeCrAl-coated Zr-4 alloys, respectively. These facts make possible the use of FeCrAl coating on Zr cladding which has excellent high-temperature mechanical properties and oxidation resistance.
physics, applied,materials science, coatings & films
-
Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions
Yun Wang,Yanfeng Wang,Shaopeng Wang,Juanjuan Geng,Changwei Zhang,Yongqing Zhao,Weidong Zeng
DOI: https://doi.org/10.1016/j.ceramint.2024.02.185
IF: 5.532
2024-02-01
Ceramics International
Abstract:Chromium (Cr) coating is a potential candidate material for improving the oxidation resistance and extending rail service life of zirconium (Zr) alloys used in nuclear fuel cladding materials. This study investigates the effect of temperature on the effectiveness of Cr coating on Zr-4 alloy deposited using arc ion plating, revealing the microstructure evolution mechanism of Cr coating in high temperature steam environments. The research results indicate that the oxidation of the Cr coating is slow at 900-1000 °C and that the surface oxide layer, to some extent, hinders the diffusion of oxygen from the outside to the inside. However, at higher temperatures, the oxidation rate of the Cr coating is accelerated, and large bubbles and voids are formed at the interface between the Cr2O3 layer and the residual Cr layer, resulting in the fracture of the oxide layer. At this time, the protective performance of the Cr coating is completely lost. Note that the simultaneous inward diffusion of oxygen and outward diffusion of Zr trigger the occurrence of redox reactions, generating a ZrO2 network. Changes in steam temperature significantly affect the oxidation behavior of Cr coating. As a driving force, temperature accelerates the diffusion of oxygen to the substrate. Conversely, the formed zirconia network also promotes the failure of the Cr coating.
materials science, ceramics
-
Isothermal experiments on steam oxidation of magnetron-sputtered chromium-coated zirconium alloy cladding at 1200 °C
Dong Wang,Ruhao Zhong,Yapei Zhang,Peng Chen,Yicong Lan,Jian Yu,G.H. Su,Suizheng Qiu,Wenxi Tian
DOI: https://doi.org/10.1016/j.corsci.2022.110544
IF: 7.72
2022-09-01
Corrosion Science
Abstract:The isothermal steam oxidation behavior of chromium-coated zirconium alloy cladding at 1200 °C is studied. The cladding substrate is Zr-1 Nb alloy with outer diameter of 9.5 mm and thickness of 0.57 mm. The Cr coating is prepared by magnetron sputtering method with thickness of about 11 μm. The oxidation durations are 300 s~14,400 s. After oxidation, blisters are formed on the surface due to the compressive stress in coating, and the coating surfaces are porous or exhibit a morphology with ravines and granular crystals. A four-layer structure (Cr2O3, Cr, Zr(Cr,Fe)2 and Zr from outside to inside) is formed in the early stage of oxidation. However, Zr4+ can migrate into Cr coating through grain boundaries and reacts with Cr2O3. The redox reaction between Zr and Cr2O3 leads to the coating failure, resulting in the oxidation of Zr alloy substrate. Due to selective oxidation, a certain thickness of Cr coating is retained during the thickening of outer ZrO2. The emergence of outer ZrO2 layer is significantly delayed by Cr coating, and Cr coating is able to reduce the growth rate of outer ZrO2 layer. Therefore, Cr coating has a protective effect in 1,200 °C steam environment and can improve the oxidation resistance of Zr alloy cladding.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Effect of Cr and Y on the microstructure and mechanical properties of Fe-Cr-Al alloys during corrosion-aging in superheated steam at 500 °C
Shaohan Wang,Haoyu Wang,Xuefeng Dai,Shitong Xu,Xiaodong Lin,Lijuan Hu,Yaoping Xie,Meiyi Yao
DOI: https://doi.org/10.1016/j.matchar.2023.113454
IF: 4.537
2023-11-06
Materials Characterization
Abstract:The α-α' phase separation of Fe-Cr-Al alloys during long-term service at 475–500 °C may lead to the increase of strength and hardness and the decrease of plasticity, which will limit the application of Fe-Cr-Al alloys as accident tolerant fuel (ATF) cladding material. The mechanical behavior and microstructure evolution of Fe-12Cr-5Al, Fe-12Cr-5Al-0.01Y, Fe-20Cr-5Al and Fe-20Cr-5Al-0.02Y (wt%) alloys in 500 °C superheated steam for 2000 h have been investigated by tensile test, Vickers hardness measurement, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), three-dimensional atom probe (3DAP) and thermodynamic calculations. Results show that increasing the Cr content may refine the grain and improve tensile strength of the alloy, while adding trace Y has negligible effect on the grain size and tensile strength of the alloy; the corrosion-aging hardening of 20CrY and 20Cr alloys is attributed to the α-α' phase separation, which is closely related to the high content of Cr in the alloy. The addition of trace Y promotes the nucleation and growth of α' phase in alloys with the content of 20%Cr during the corrosion-aging process but has insignificant influence on the mechanical properties of the alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
-
Influence of Zr on grain orientation, texture, and mechanical properties in hot- and warm-rolled FeCrAl alloys
Wenbo Liu,Zhe Liu,Wei Luo,Huiqun Liu,Qing Wang,Ruiqian Zhang
DOI: https://doi.org/10.1016/j.matchar.2021.111602
IF: 4.537
2022-01-01
Materials Characterization
Abstract:Iron–chromium–aluminum (Fe–Cr–Al) alloys have great potential application as an accident-tolerant fuel cladding material in light-water reactors. It has excellent processing ability, resistance to steam oxidation at high temperatures (HTs), and irradiation swelling-resistance. It is necessary to improve the room- and high-temperature mechanical properties and reveal the strengthening mechanism. In this study, we analyzed the effect of Zr on the microstructure and room- and high-temperature tensile properties of hot- and warm-rolled FeCrAl alloys. The results show that the Laves phase could be effectively stabilized by Zr addition, and the proportion of low-angle grain boundaries increased. Moreover, the yield strength at room and high temperatures of the samples after Zr addition were improved, owing to the precipitation and sub-grain boundary strengthening by Zr. In addition, Zr changed the grain orientation, but had no relevance to the number of easier activated slip systems. The movable dislocation cannot slip during high-temperature tensile tests because of the pinning effect of the dynamic precipitated Laves phase, which could be the reason for the decrease in elongation at high temperatures.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
-
Effect of steam on high temperature oxidation behaviour of alumina-forming alloys
B. A. Pint,K. A. Unocic,K. A. Terrani
DOI: https://doi.org/10.1179/0960340914z.00000000058
2015-01-01
Materials at High Temperatures
Abstract:Alternative light water reactor fuel cladding materials are being investigated to replace Zircaloy for enhanced accident tolerance, which involves oxidation resistance to steam environments at ≧1200°C for short times. As chromia-forming alloys and Ni-containing alloys are both undesirable for this application, the focus has been on FeCrAl, although NiAl was used to evaluate the effect of steam oxidation at 1600°C for this study. For commercial and model FeCrAlY alloys, a critical Cr–Al composition was identified for 1 bar isothermal steam (100% H2O) oxidation resistance at 1200°C, which differed for exposures in Ar–50%H2O at the same temperature. Alloys with lower Cr and Al contents were not able to form a protective alumina scale under these conditions. To simulate the accident scenario, exposures were also conducted in steam with the temperature rising 5°C min−1 to 1500°C for the most oxidation resistant alloys. Using thermogravimetry, the maximum use temperature for candidate alloys was determined for different Cr and Al contents. Minor additions such as Y and Ti appeared to be beneficial for oxidation resistance. Similar to prior studies, alumina scales formed in air and in steam appeared to have only subtle differences in microstructure.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Effect of Al and Cr Content on Air and Steam Oxidation of FeCrAl Alloys and Commercial APMT Alloy
Kinga A. Unocic,Yukinori Yamamoto,Bruce A. Pint,Kinga A. Unocic,Yukinori Yamamoto,Bruce A. Pint
DOI: https://doi.org/10.1007/s11085-017-9745-1
IF: 2.2
2017-03-09
Oxidation of Metals
Abstract:AbstractTo develop the next generation of accident-tolerant fuel cladding for light-water nuclear reactors, wrought FeCrAlY alloys with varying amounts of Cr and Al and commercial Kanthal APMT alloy were evaluated for short-term (4 h) oxidation resistance in steam and air at 1200–1475 °C. Model alloys with lower Cr contents and higher Al contents were evaluated as lower Cr contents are desirable for radiation damage resistance during operation. As expected, a synergistic effect was found between the Cr and Al contents to enable protective Al2O3 formation under these conditions. Characterization of the alumina scales formed in steam found that the scale morphology was affected by the alloy Y content and detailed scanning transmission electron microscopy (STEM) detected Y segregation along scale grain boundaries at 1200 °C. However, after 4 h at 1475 °C, Y and Hf were not segregated to the oxide grain boundaries formed on APMT and the scale had a single layer structure. Compared to oxidation in air, STEM characterization of the outer scale showed differences in the Fe and Cr distributions in steam.Graphical Abstract
metallurgy & metallurgical engineering
-
Experimental kinetic study of interdiffusion behavior and intermetallic compound Zr(Fe,Cr)2 formation at the Cr/Zry4 interface under elevated temperatures
Bo Li,Huilong Yang,Reuben Holmes,Lijuan Cui,Sho Kano,Hiroaki Abe
DOI: https://doi.org/10.1016/j.jnucmat.2023.154595
IF: 3.555
2023-10-01
Journal of Nuclear Materials
Abstract:Interdiffusion behavior at the Cr-Zr interface under elevated temperatures in Cr-coated Zr-based accident tolerant fuel cladding is a key phenomenon for understanding its microstructural stability during the reactor's long-term operation. The interdiffusion behavior of the Cr/Zircaloy-4 (Zry4) diffusion couple and microstructural evolution at the interface were studied under vacuum conditions in the temperature range 973 K to 1323 K. Results show that interdiffusion results in the formation of a Zr(Fe,Cr)2 intermetallic compound layer irrespective of the annealing temperature. Segregation of Fe in the Zr(Fe,Cr)2 interlayer is confirmed, which is enhanced by annealing temperature within the α-Zr phase temperature regime and dropped greatly within the β-Zr temperature regime. The kinetic growth model for Zr(Fe,Cr)2 is found to follow the parabolic law in both α-Zr and β-Zr phase regions, and the diffusion activation energy (Q) of Cr in Zr(Fe,Cr)2 is determined as 7.23 × 10 4 J m o l − 1 for α-Zr phase annealing. Extrapolation of the diffusion coefficients measured within the α-Zr phase predicts a much lower value within the β-Zr phase compared to the experimental result, indicating that the α→β(Zr) phase transformation promotes the growth rate of Zr(Fe,Cr)2 interlayer formation, likely due to the enhancement in both diffusion ability and solubility of Cr in β-Zr relative to α-Zr. The insights obtained in this study will help to improve the understanding of the cladding's microstructure stability and its related degradation behaviors during practical application.
materials science, multidisciplinary,nuclear science & technology
-
Effect of Y on the corrosion behavior of Fe22Cr5Al3Mo alloy in 500 °C super-heated steam
Rongrong Sun,Meiyi Yao,Jie Zhang,Haoyu Wang,Xiaodong Lin,Wenhuai Zhang,Yunlong Qiu,Jian Yang,Guoguang Cheng,Jianxin Dong
DOI: https://doi.org/10.1016/j.corsci.2021.110022
IF: 7.72
2022-03-01
Corrosion Science
Abstract:Fe22Cr5Al3Mo-xY (x = 0, 0.15%, mass fraction) alloys were fabricated and corroded in 500 ℃/10.3 MPa super-heated steam using a static autoclave. The results show that the oxide films present a four-layer structure consisting of Fe oxide, Cr oxide, mixed oxide region, and Al oxide from outside to inside. There is α-(Fe, Cr) in Al2O3 layer near the oxide/metal interface. The addition of Y can delay the formation of the large iron oxide particles and increase the ratio of Cr2O3 film thickness to the thickness of the flat oxide film area, thus improving the corrosion resistance of the alloys.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Effect of Final Annealing Temperature on Corrosion Resistance of SZA-6 Zirconium Alloy Cladding Tubes
S. Qiu,Zhuqing Cheng,J. Qiu,B. Gao,Z. Yang,Z. Wu,Hong Liu,J. Liao
DOI: https://doi.org/10.4028/WWW.SCIENTIFIC.NET/MSF.944.488
2019-01-01
Materials Science Forum
Abstract:The corrosion resistance of SZA-6 zirconium alloy(Zr-0.5Sn-0.5Nb-0.3Fe-0.015Si) cladding tubes finally annealed at 480°C, 510°C and 560°C were studied by static autoclave in 360°C/18.6 MPa pure water and 360°C/18.6 MPa/0.01 mol/L LiOH aqueous solution. The microstructure of the samples before and after corrosion were analyzed by EBSD, TEM and SEM. The results showed that the corrosion weight gains of the three SZA-6 alloy samples were lower than that of Zr-4 alloy after 500 days corrosion in both hydrochemical mediums. After long-term corrosion, the corrosion weight gains of SZA-6 alloy in pure water and LiOH aqueous solution increased obviously with the final annealing temperature, while the corrosion weight gain of unstressed Zr-4 alloy was higher than that of recrystallized under the same condition. With the increase of the final annealing temperature, the high-angle grain boundaries in the alloy larger than 15° became more and recrystallization degree also increased. The Second Phase Precipitates (SPPs) were fine, uniform, and dispersively distributed with an average diameter of about 120 nm. Although the size and distribution of the SPPs were similar, the Nb/Fe ratio in the SPPs increased. The long-term corrosion weight gain of zirconium alloy was related to the number of parallel cracks in the oxide film and the uneven growth degree of the oxide film on the interface of the oxide film/matrix. The corrosion resistance of the alloy in two hydrochemical mediums was related to the degree of recrystallization and the content of Nb in the SPPs. Increasing the final annealing temperature would promote the formation of fine and uniform recrystallized grains, which was benefit to the corrosion resistance, but at the same time it would reduce the content of solid solution Nb in the αZr matrix, which in turn would be detrimental to the corrosion resistance.
Engineering,Materials Science
-
Microstructure evolution and oxidation behavior of bi-layer CrAl-Mo coated Zircaloy-4 in steam at 1200 o C and 1300 o C
Chaowen Zhu,Pengcheng Li,Chen Chen,Junhua Tian,Song Zeng,Yan Meng,Huahai Shen,Xiaochun Han,Haibin Zhang
DOI: https://doi.org/10.1016/j.corsci.2022.110632
IF: 7.72
2022-09-09
Corrosion Science
Abstract:CrAl alloys have shown excellent oxidation resistance in high temperature steam environment and enhanced wear resistance. However, thin film CrAl on zircaloy substrate can only tolerate up to 1200 o C steam because of the fast diffusion between zirconium and the coating. In this study, Mo was introduced as a buffer layer which significantly reduced the diffusion rate. The bi-layer CrAl-Mo coated Zircaloy-4 alloy was prepared by magnetron sputtering method without further treatment. CrAl-Mo coatings with three different compositions (Cr/Al atomic ratios of 96/04, 84/16 and 68/32) were prepared to investigate the role of Al in the high temperature oxidation of the CrAl system. The bi-layer CrAl-Mo coatings show excellent performance up to 1300 o C. Dense and protective α-Al 2 O 3 layers are formed on the surface or underneath the chromia (Cr 2 O 3 ) layer, which is dominated by the aluminum concentrations. A systematic investigation of the oxidation behavior of CrAl coatings with representative Al contents at 1200 o C and 1300 o C is presented in this paper.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Xe20+ ions irradiation and autoclave corrosion coupled with steam oxidation behaviors of FeCrAlMoSiY-coated Zr claddings
Yuhang Li,Fanping Meng,Peng Li,Fangfang Ge,Bingsheng Li,Feng Huang
DOI: https://doi.org/10.1016/j.surfcoat.2022.128166
IF: 4.865
2022-03-01
Surface and Coatings Technology
Abstract:Surface-modified Zr alloys by protective coatings are being developed as the most viable near-term accident tolerant fuel (ATF) claddings. Herein, an amorphous FeCrAlMoSiY coating was deposited on Zr alloys by magnetron sputtering. The key performance of specimens in terms of ion irradiation, autoclave corrosion, and high-temperature steam oxidation were studied using X-ray diffractometer (XRD), atomic force microscopy (AFM), and scanning electron microscopy (SEM). We found that the surface of the irradiated coating became more compact with a lower surface roughness than the as-deposited coating. Meanwhile, the hardness and indentation modulus decreased slightly after irradiation. After 30 days autoclave corrosion, a continuous spinel FeCr2O4 scale was formed on the surface, and the residual coating had the same composition and ~76% in thickness of that of the as-deposited coating. During the 1200 °C steam oxidation of that corroded sample, the protective α-Al2O3 scale was formed underneath the FeCr2O4 layer, along with the formation of a diffusion barrier at the coating-substrate interface. These findings highlight the potential of the FeCrAlMoSiY coating considered as a protective coating for ATF claddings.
physics, applied,materials science, coatings & films
-
Influence of composition and heating schedules on compatibility of FeCrAl alloys with high-temperature steam
Chongchong Tang,Adrian Jianu,Martin Steinbrueck,Mirco Grosse,Alfons Weisenburger,Hans Juergen Seifert
DOI: https://doi.org/10.1016/j.jnucmat.2018.09.026
2018-12-05
Abstract:FeCrAl alloys are proposed and being intensively investigated as alternative accident tolerant fuel (ATF) cladding for nuclear fission application. Herein, the influence of major alloy elements (Cr and Al), reactive element effect and heating schedules on the oxidation behavior of FeCrAl alloys in steam up to 1500°C was examined. In case of transient ramp tests, catastrophic oxidation, i.e. rapid and complete consumption of the alloy, occurred during temperature ramp up to above 1200°C for specific alloys. The maximum compatible temperature of FeCrAl alloys in steam increases with raising Cr and Al content, decreasing heating rates during ramp period and doping of yttrium. Isothermal oxidation resulted in catastrophic oxidation at 1400°C for all examined alloys. However, formation of a protective alumina scale at 1500°C was ascertained despite partial melting. The occurrence of catastrophic oxidation seems to be controlled by dynamic competitive mechanisms between mass transfer of Al from the substrate and transport of oxidizing gas through the scale both toward the metal/oxide scale interface.
Materials Science
-
Corrosion Behavior of Nb-doped FeCrAl Alloy in 500°C Steam
Zhaolin Shi,Xinyi Pang,Kun Zhang,Miao Song,Donghai Du,Zhao Shen,Hui Wang
DOI: https://doi.org/10.1016/j.corsci.2024.112036
IF: 7.72
2024-04-06
Corrosion Science
Abstract:The corrosion behavior of Fe-13Cr-4Al-2.2Mo, a candidate cladding material for accident tolerant fuel, doped with varying concentrations of Nb (0, 0.5, 1.0, and 1.5 wt%), was investigated under conditions of 500°C/10.3 MPa superheated steam. Upon exposure, a triple-layer oxide film comprising outer, inner, and diffusion oxide layers was formed. The results indicate that the addition of Nb significantly enhances the corrosion resistance of this alloy by reducing the thickness and porosity of the oxide film. The enhanced volume diffusion rate of Al and Cr, facilitated by the solid solution Nb, along with the inhibited inward diffusion of oxidant ions along grain boundaries owing to Laves phase precipitates, contributed to the enhanced corrosion resistance of the Nb-doped Fe-13Cr-4Al-2.2Mo alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering