Abstract:This article aims to produce NiTi shape memory alloys, which show superelasticity and shape memory effect, as well as good biocompatibility and corrosion properties, in open and porous sizes ranging from 100-500 μm, which are required for use as implants. This structure of pores is necessary to allow tissue growth and fluid flow inside the implants. Many powder metallurgy methods have been used in producing porous NiTi shape memory alloys. However, the packaging pressure used in these methods has not successfully created the desired pore distribution, shape, and size. The methods by which it can be produced are costly in terms of cost. In the study, production was carried out by sintering the powder mixture poured into molds without pressure with the help of binder polymers. This sintering process was carried out in an argon atmosphere for 1 hour at temperatures 1050, 1125, and 1200 °C. The study shows that pressureless loosen sintering can produce porous NiTi alloys, which is the more straightforward method. The pore distribution and proportions were examined. Homogeneous distribution and pores in desired sizes are created. It has also been determined that the binder polymer has a space-retaining effect. It was determined at which temperature the alloy sintered at different temperatures contained the desired B2 austenite phase for superelasticity. Austenite start and finish temperatures were determined for the alloy produced at each sintering temperature. As a result of this research, it was determined which phase was denser at which temperature, and the phase transformation temperatures were found. The exact temperature measurements can be calculated by changing the sintering time parameter. In addition, the change in phase transformation temperatures can be measured by heat treatment after sintering. Porous NiTi alloys can be used as dental and medical implants thanks to their excellent biocompatibility and corrosion resistance. This method will decrease production costs, and more people will have access to this material. In general, the mechanism of sintering methods is joining the points in contact with the packaging pressure by necking. In this study, the combination of the grains with the polymer without packaging pressure with the thermal expansion mechanism reveals the originality of the study.

High Porosity and High-Strength Porous NiTi Shape Memory Alloys with Controllable Pore Characteristics

Gradient Porosity and Large Pore Size NiTi Shape Memory Alloys

High Porosity and Large Pore Size Shape Memory Alloys Fabricated by Using Pore-Forming Agent (nh4hco3) and Capsule-Free Hot Isostatic Pressing

Preparation of High-Porosity Niti Alloys by Powder Sintering with Nacl Pre-Forming

High-strength porous NiTi shape memory alloys with stable cyclic recovery properties fabricated using elemental powders

Pore Formation Mechanism and Characterization of Porous NiTi Shape Memory Alloys Synthesized by Capsule-Free Hot Isostatic Pressing

Control of porosity and superelasticity of porous NiTi shape memory alloys prepared by hot isostatic pressing

Space-holder engineered porous NiTi shape memory alloys with improved pore characteristics and mechanical properties

Pore structures of high-porosity NiTi alloys made from elemental powders with NaCl temporary space-holders

Porous NiTiNb alloys with superior strength and ductility induced by modulating eutectic microregion

Microstructure and Mechanical Properties of Porous NiTi Alloy Prepared by Integration of Gel-Casting and Microwave Sintering

Superelastic Porous NiTi with Adjustable Porosities Synthesized by Powder Metallurgical Method

Preparation and characterization of porous NiTi alloys synthesized by microwave sintering using Mg space holder

Microstructure, mechanical properties and superelasticity of biomedical porous NiTi alloy prepared by microwave sintering.

INVESTIGATION OF THE EFFECT OF SINTERING TEMPERATURES ON THE PRODUCTION OF POROUS NITI ALLOY BY LOOSEN SINTERING METHOD

High Damping Capacity in Porous Niti Alloy with Bimodal Pore Architecture

Effect of Pore Sizes on the Microstructure and Properties of the Biomedical Porous NiTi Alloys Prepared by Microwave Sintering

Pore Control in Porous NiTi Alloy Produced by Combustion Synthesis Method with the Utilization of Space Holders

Stucture and Properties of Porous NiTi Shape Memory Alloys Fabricated by Low Pressure Sintering

Superior tensile and recovery properties of hydride-dehydride elemental NiTi alloys homogenized using high-temperature sintering

Lightweight NiTi Shape Memory Alloy Based Composites with High Damping Capacity and High Strength