Abstract:The Pb0.4Sr0.6TiO3 (PST) thin films with the perovskite phase were fabricated successfully on ITO/glass substrates by the sol-gel method with rapid thermal processing (RTP) above 500degreesC. The crystalline phase structures and the surface morphologies of the thin films were measured through XRD, SEM and AFM respectively. Results show that both the formation of the perovskite and contents of the crystalline phase in this PST thin film are dependent on the preparing process and the activity of ions in the formation of the crystalline phase. By RTP, high active ions obtained in the gel decomposition directly form the crystalline phase, and consequently, much more contents of the crystalline phase can be obtained even at a relatively lower temperature. 14% more contents of crystalline phase appear in RST thin film at 600degreesC by RTP than by heat treatment at 600degreesC for a long time. The lowest temperature of forming of the proveskite phase in sol-gel derived PST thin film is approximately 500degreesC by RTP, which is 50degreesC lower than that by heat treatment for a long time. The surface morphology of the thin film is related to the heat treatment processing. By RTP the surface morphology of the thin film keeps the original state, where the actual smooth exhibits the noncrystalline thin film and the hill-like protuberance shows the well crystalline one. Due to etching under the oxygen atmosphere at high temperature, the thin film calcined for a long time contributes the morphology with uniformly dispersed micro conical cylinders all over the surface on the basis of the original smooth or hill-like surface state.

Effect of Heat Treatment Temperature on the Formation of Ag Nanoparticles in Ag-Pbtio3 Composite Thin Films

Low-Temperature Preparation of Ag-TiO2 Composite Films and Their Properties

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Formation of Silver Nano Particles in Percolative Ag‐PbTiO 3 Composite Dielectric Thin Film

Preparation and characterization of heat-assisted PbS/TiO 2 thin films

Sol-Gel Preparation and Optical Properties of Ag Nanoparticle/TiO2 Composite Films

Two Stage Formation of Silver Nanoparticles in PZT Thin Films Controlled by Re-Nucleation Through Transition Phase of Ag-Pb Alloy

Tailoring the Light Absorption of Ag-PZT Thin Films by Controlling the Growth of Hexagonal- and Cubic-Phase Ag Nanoparticles

Formation of Ag Nanoparticles in Percolative Ag–PbTiO3 Composite Thin Films Through Lead-Rich Ag–Pb Alloy Particles Formed As Transitional Phase

Preparation of Silver Dispersed Pbtio3 Film by Sol-Gel Method

Effect of Ag concentration and annealing on the optical properties of Ag nanoparticle composite films

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

TiO2–Ag Nanocomposites by Low‐Temperature Sol–Gel Processing

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

Effect of dispersed Ag on the dielectric properties of sol–gel derived PbTiO3 thin films on ITO/glass substrate

Influences of Heat Treatment on the Structure of PMNT Thin Films Derived by Sol-Gel Process

Effects of Heat Treatment on the Microstructures of AuCuPtPdNiRh Alloys

Effects of heat treatment on the formation of sol-gel derived Pb0.4Sr0.6TiO3 thin films

The Effect of Heat Treatment on Bistable Ag-TCNQ Thin Films

Ag Nanoparticle Dispersed Pbtio3 Percolative Composite Thin Film with High Permittivity