A simple and highly effective process for the preparation of activated carbons with high surface area
Ying Li,Xuefeng Ding,Yupeng Guo,Lili Wang,Chunguang Rong,Yuning Qu,Xiaoyu Ma,Zichen Wang
DOI: https://doi.org/10.1016/j.matchemphys.2011.02.046
IF: 4.778
2011-01-01
Materials Chemistry and Physics
Abstract:Activated carbons with high surface area were prepared by phosphoric acid as activation agent and rice husks as precursors. It was found that the characteristics of the activated carbons were influenced not only by the preparation but also by the post-processing method. The high surface area of the activated carbons was prepared under the optimum condition (50% H 3 PO 4 with impregnation ratio of 5:1, activation temperature of 500 °C, activation time of 0.5 h, wash water temperature of 100 °C). SiO 2 content could affect the surface area of activated carbons, either. The lower SiO 2 content of the activated carbons, the higher pore volume the carbons had. The SiO 2 content was 11.2% when used the optimum condition. The explanation was that silicon element in rice husks reacted with H 3 PO 4 to form silicon phosphate (SiP 2 O 7 ), and it could be proved further by X-ray diffraction analysis, SiP 2 O 7 could be removed by post-process. Keywords Activated carbon Rice husk Phosphoric acid Silicon phosphate 1 Introduction Activated carbons are of interest due to their extensive surface area, high degree of surface reactivity, and favorable pore size distribution [1] . Among the various activation agents, phosphoric acid is a well-established agent for preparation of activated carbons, which has many advantages. Nowadays, the raw material of phosphoric acid activation, usually stone [2–6] , shell [7,8] , polymer [9] , wood [10–12] and coal [11,13] , is limitative or expensive, or nonrenewable, which restrict their application. Thus lignocellulosic agricultural wastes are investigated as precursors due to their renewability and huge amount. Rice husk, a by-product of the rice milling industry, with an annual output 40 million tons in China [14,15] , usually burned in open heaps as waste, can be used as the precursor of the activated carbon. However, due to the high ash content of rice husk, which is difficult to remove, activated carbon prepared from rice husk by H 3 PO 4 activation with desirable surface area and pore volume often contains two procedures: alkali-leaching process to remove SiO 2 followed by H 3 PO 4 activation, surface area and pore volume reach 1741 m 2 g −1 and 1.315 ml g −1 [16] . In this work, we prepared activated carbons with high surface area (1820 m 2 g −1 ) using rice husks as raw materials by H 3 PO 4 activation without alkali-leaching process. The mechanism of phosphoric acid activation was enriched through this research. The characteristics of the activated carbon were greatly influenced by post-processing method. To our best knowledge, the carbons washed by water with different temperatures had different surface area, pore volume and ash content, which was first discussed in our manuscript. The whole process was simple and economical, which not only enlarge the scope of the raw materials through H 3 PO 4 activation, but also make it possible to produce high surface area activated carbons in industry. 2 Experimental 2.1 Precursors Rice husk is obtained from a rice mill nearby Changchun city. Rice husk was washed thoroughly with distilled water to remove soil and dust, then dried at 100 °C overnight and porphyrized to 60 mesh before employment. 2.2 Preparation of activated carbons The precursors were impregnated with phosphoric acid solution (40–85 wt.%) with impregnation ratio of (the weight ratio of phosphoric acid to rice husk) 3:1–6:1, and stirred for at least 2 min at room temperature, then the mixtures were heated up to different temperatures: 300, 400, 500, 600 °C for 0.5–2 h. The products were washed with hot distilled water (100 °C) for several times until the filtrate was neutral, then dried at 120 °C for 12 h before further characterization. 2.3 Characterization 2.3.1 Nitrogen adsorption Pore structure analysis was performed using a Micromeritics ASAP 2010 Surface Analyzer through nitrogen adsorption at 77 K in the relative pressure range of 10 −6 –1 atm. Prior to the analysis, all the samples were degassed at 200 °C to 3 μm Hg under vacuum. Surface area was calculated by the Brunauer, Emmett, and Teller (BET) equation using the data obtained from nitrogen adsorption isotherm. The relative pressure range used for the calculation was 0.05–0.2. The single point total pore volume was obtained from the amount of nitrogen adsorbed at a relative pressure around 0.95. The pore size distribution was derived from the adsorption branches of the isotherms by the Density Functional Theory (DFT) method. 2.3.2 X-ray diffraction The crystal structures of samples were characterized by X-ray diffraction (XRD) (SHIMADZU XRD-6000 diffractometer employing Ni-filtered Cu Kα radiation, at a scanning rate of 6° min −1 with 2 θ ranging from 15° to 60°). 2.3.3 Transmission electron microscopy (TEM) The surface morphology of the as-prepared samples was examined by transmission electron microscope (JEOL 2000EX) operating at 200 kV and high-resolution transmission electron micrograph (HRTEM FEI TECNAI G2). HRTEM equipped with an energy dispersive X-ray (EDX) analyzer (Phoenix). 3 Results and discussion 3.1 Characteristics of activated carbons Fig. 1 shows the TEM and HRTEM images of the activated carbons. It can be clearly conformed the nature of the amorphous structure from Fig. 1 a. The structure of the activated carbon was turbostratic with a pore structure consisting of inter-connected nanochannels, which were formed by the disordered packing of turbostratic carbon sheets and clusters [17] . Most pore size is smaller than 1 nm from HRTEM image ( Fig. 1 b). According to the IUPAC (International Union of Pure and Applied Chemistry) classification, the isotherms in this work were classified into type IV, H4. Fig. 2 shows adsorption/desorption isotherms of nitrogen at 77 K of activated carbons. It illustrates that the existence of microporous structure where pore filling occurs at low relative pressures. The presence of adsorption hysteresis loop indicates the presence of mesoporosity according to type IV, and the porous carbon contains slit-shaped pores according to H4. In this work, 2 and 50 nm were taken as the boundary sizes between micro and mesopore, and meso and macropore, respectively. From Fig. 3 , we can see that the pore diameter of the prepared activated carbon contain 1.3–2.4 nm, 2.7–4.5 nm, 6.8 nm and 9.7–11.0 nm, respectively, which indicates the porous carbon have micro and mesopore structure. 3.2 Effect of different factors on activated carbons 3.2.1 Influence of activation temperature The BET surface areas and pore volumes of activated carbons prepared at different activation temperatures using the impregnation ratio of 4:1, activation time of 1.5 h are summarized in Fig. 4 a and b . The concentration of H 3 PO 4 was 50, 60 and 85%, respectively. As seen in Fig. 4 a and b, the BET surface areas and pore volumes of activated carbons increase gradually with activation temperature increasing from 300 to 500 °C, then decrease with further increasing in the final activation temperature. With activation temperature of 300 °C, the activation extent of rice husk was relatively low demonstrated by the small surface area. With increasing temperature to 600 °C, violent gasification reactions might cause part of the pore structure to be destroyed by collapsing which caused the small surface area [18] . From Fig. 5 we can see the pore volume declined when the temperature increased to 600 °C, which could be deduced from the collapsing of pores. So the optimum temperature for activation was 500 °C. The ash content is shown in Fig. 4 c and Table 1 . The yield of activated carbon was calculated based on the weight of rice husk on a dry basis from the following equation: Yield of activated carbon ( wt . % ) = Weight of activated carbon Weight of rice husk Ash content of rice husk was around 18%, the yield of activated carbons was about 40%, so the ash content of activated carbons should be around 32% theoretically, but it decreased when the activation temperature was 400 or 500 °C, which could be explained that silicon element existed in rice husk reacted with H 3 PO 4 to form phosphate in this temperature range, and most of the phosphate could be removed by post-processing. However, as the temperature increased to 600 °C, the ash content of activated carbon became higher, which was due to the decreasing of the product yield. Fig. 6 shows the XRD patterns of activated carbons. As seen in Fig. 6 , all diffraction peaks are similar to those of silicon phosphate (SiP 2 O 7 ) and the diffraction data is in good agreement with JCPDS file no. 22-1320. As seen from Fig. 7 , the EDX shows the activated carbons have the element of C, Si, P, O, which prove further the existence of silicon phosphate in activated carbons. 3.2.2 Influence of activation time Fig. 8 a and b shows the BET surface areas and pore volumes of activated carbons prepared at different activation times with other factors are fixed at 500 °C, impregnation ratio of 4:1. The concentration of H 3 PO 4 was 50, 60 and 85%, respectively. As observed from Fig. 8 , the BET surface area and pore volume of activated carbon reach maximum value when the activation time is 0.5 h. The ash content of activated carbons increased with the increase of activation time, which was due to the soluble silicon compound may convert to other format that could deposit into the pores of activated carbons. It blocked the pores and resulted in the surface area decreasing and ash content increasing. From Fig. 9 we can deduce that when the duration time extending to 1.5 h, the pore diameter of 6.5–7.0 nm and 10–12 nm decreased rapidly. For the activated carbon prepared at 500 °C, 50% H 3 PO 4 impregnation ratio of 4:1, reaction time of 0.5 h, the BET surface area and pore volume reached 1712 m 2 g −1 and 1.968 ml g −1 , the ash content was 11.7%. 3.2.3 Influence of the concentration of H 3 PO 4 and impregnation ratio The effect of the different concentration of H 3 PO 4 on the surface area and pore volume of activated carbon were investigated at impregnation of 4:1 and reaction temperature of 500 °C. 40% H 3 PO 4 was also used as the activation agent, but the characteristics of the activated carbons were worse than 50% H 3 PO 4 as the activation agent. 50% H 3 PO 4 was better than others with the activation time of 0.5 h. When used 85% H 3 PO 4 , pore volume was larger and the surface area was smaller than the activated carbons produced by 50% H 3 PO 4 . The reaction was rigorous when using 85% H 3 PO 4 , caused some of the pores combining together and produced poor pore size distribution, therefore, the pore volume was large. The reaction was relatively moderate when using 50% H 3 PO 4 , resulting in narrow micropore size distribution and high surface area. The carbons with the highest surface area were obtained when the raw materials were impregnated with 50% H 3 PO 4 and then activated at 500 °C for 0.5 h, different impregnation ratios were used to find the optimum condition with other parameters constant. As seen from Fig. 10 , the optimal impregnation ratio for activation agent: rice husk is 5:1 (g/g). The BET surface area was 1820 m 2 g −1 , pore volume was 2.01 ml g −1 and ash content was 11.2%. Excessive impregnation was detrimental to activation, which was because H 3 PO 4 as flame retardant prevented the porosity development. Moreover, the excess of H 3 PO 4 and phosphates blocked the pores of the activated carbons. 3.2.4 Influence of the post-processing temperature The post-processing temperature had great influence on the characteristic of the activated carbon. The carbons (prepared at 500 °C, 50% H 3 PO 4 impregnation ratio of 5:1, reaction time of 0.5 h) washed by the water with different temperature had different surface area, pore volume and ash content. As seen in Table 2 , the ash content is high when the wash water is below 40 °C. As this study showed before that the silicon element could react with H 3 PO 4 to form SiP 2 O 7 . SiP 2 O 7 had a good solubility in hot water, but could not dissolve in cold water. If it could not be removed it deposited onto the carbons again, resulted in the low surface area and pore volume. Thus, the activated carbons characteristics were greatly improved by changing the post-processing temperature. 4 Conclusions This study had shown that rice husk could be used as raw material for preparation of activated carbons with high surface area and uniform pore size. The activated carbons contained micropores and mesopores. The pore diameter of the prepared activated carbon contain 1.3–2.4 nm, 2.7–4.5 nm, 6.8 nm and 9.7–11.0 nm, respectively. The ash content decreased when the optimum condition was used to prepare activated carbons. It could be deduced that silicon element in rice husks reacted with H 3 PO 4 to form silicon phosphate (SiP 2 O 7 ), and proved further the existence of SiP 2 O 7 in activated carbons by XRD analysis, SiP 2 O 7 had a good solubility in hot water, but was difficult to dissolve in cold water. Activated carbons with different surface areas and pore volumes were obtained when we changed reaction factors such as activation temperature, activation time and impregnation ratio. The post-processing temperature had a great influence on the characteristics of the activated carbons. These results provided us with a good method for preparation of activated carbon with rice husk and gave us a further understanding of the formation mechanism of carbon materials. This method could be extended to variety of materials such as rice bran and other husk shells. Acknowledgements This research was supported by the financial support of the China National Key Technology R&D Programme under Contract no. 2008BAE66B00 and Jilin Provincial Environmental Protection Department under Contract no. 200917 . References [1] Y. Guo D.A. Rockstraw Carbon 44 2006 1464 1475 [2] A.M. Puziy O.I. Poddubnaya R.P. Socha J. Gurgul M. Wisniewski Carbon 46 2008 2113 2123 [3] A.M. Puziy O.I. Poddubnaya A. Martínez-Alonso A. Castro-Muñiz F. Suárez-García J.M.D. Tascón Carbon 45 2007 1941 1950 [4] M. Molina-Sabio F. Caturla F. Rodríguez-Reinoso Carbon 33 1995 1180 1182 [5] M. Soleimani T. Kaghazchi Bioresour. Technol. 13 2008 5374 5383 [6] M. Molina-Sabio F. Rodríguez-Reinoso F. Caturla M.J. Sellés Carbon 33 1995 1105 1113 [7] A. Ahmadpour D.D. Do Carbon 35 1997 1723 1732 [8] W.C. Lim C. Srinivasakannan N. Balasubramanian J. Anal. Appl. Pyrolysis 2 2010 181 186 [9] A.M. Puziy O.I. Poddubnaya A. Martínez-Alonso F. Suárez-García J.M.D. Tascón Carbon 40 2002 1493 1505 [10] M. Jagtoyen F. Derbyshire Carbon 36 1998 1085 1097 [11] W.H. Lee P.J. Reucroft Carbon 37 1999 15 20 [12] P. Patnukao P. Pavasant Bioresour. Technol. 99 2008 8540 8543 [13] H. Teng T. Yeh L. Hsu Carbon 36 1998 1387 1395 [14] T. Li T. Wang Mater. Chem. Phys. 112 2008 398 401 [15] H. Zhang X. Zhao X. Ding H. Lei X. Chen D. An Bioresour. Technol. 101 2010 1263 1267 [16] T.H. Liou S.J. Wu J. Hazard. Mater. 171 2009 693 703 [17] T. Wang S. Tan C. Liang Carbon 47 2009 1880 1883 [18] H.O. Gyu R.P. Chong Fuel 81 2002 327 336
What problem does this paper attempt to address?
-
Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation
Yanping Guo,David A. Rockstraw
DOI: https://doi.org/10.1016/j.micromeso.2006.10.006
IF: 5.876
2006-01-01
Microporous and Mesoporous Materials
Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.
-
Effect of Two-Stage Process on the Preparation and Characterization of Porous Carbon Composite from Rice Husk by Phosphoric Acid Activation
L. John Kennedy,J. Judith Vijaya,G. Sekaran
DOI: https://doi.org/10.1021/ie034093f
2004-03-13
Abstract:Activated carbon composite prepared from rice husk using phosphoric acid activation has been studied through precarbonization of the precursor followed by chemical activation. This method can produce carbons with micro- and mesoporous structure. The ratio of chemical activating agent to precarbonized carbon was fixed at 4.2. The surface area, pore volume, and pore size distribution of carbon composite samples activated at three different temperatures (700, 800, and 900 °C) were measured using nitrogen adsorption isotherms at 77 K. The pore-opening and pore-widening effects occurred simultaneously during the process, as evidenced by scanning electron micrographs. The X-ray diffraction curve revealed the evolution of crystallites of carbon and silica during activation at higher temperature. The FTIR spectrum also provided evidence for the presence of silica in the carbon composite. The proper choice of the preparation conditions had an influence on the micropore and mesopore volumes of the activated carbon composite, which were 0.1187 and 0.2684 cm3/g, respectively. The production yield was observed to decrease with increasing activation temperature.
engineering, chemical
-
Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation
Yun Chen,Shang-Ru Zhai,Na Liu,Yu Song,Qing-Da An,Xiao-Wei Song
DOI: https://doi.org/10.1016/j.biortech.2013.07.002
IF: 11.4
2013-01-01
Bioresource Technology
Abstract:A coupling of low-temperature sulfuric acid-assisted carbonization and H3PO4 activation was employed to convert NaOH-pretreated rice husks into activated carbons with extremely high surface area (2028 m(2) g(-1)) and integrated characteristics. The influences of the activation temperature and impregnation ratio on the surface area, pore volume of activated carbons were thoroughly investigated. The morphology and surface chemistry of activated carbons were characterized using N-2 sorption, FTIR, XPS, SEM, TEM, etc. The adsorption capacity of resulting carbons obtained under optimum preparation conditions was systematically evaluated using methylene blue under various simulated conditions. The adsorption process can be well described by both Langmuir isotherm model and the pseudo-second order kinetics models; and the maximum monolayer capacity of methylene blue was ca. 578 mg g(-1). (C) 2013 Elsevier Ltd. All rights reserved.
-
Comparing specific capacitance in rice husk-derived activated carbon through phosphoric acid and potassium hydroxide activation order variations
Nasser A. M. Barakat,Mohamed S. Mahmoud,Hager M. Moustafa
DOI: https://doi.org/10.1038/s41598-023-49675-0
IF: 4.6
2024-01-19
Scientific Reports
Abstract:This manuscript investigates the influence of the chemical activation step order and process parameters on the specific capacitance of activated carbon derived from rice husk. The chemical activation was performed either before or after the carbonization step, using phosphoric acid (H 3 PO 4 ) and potassium hydroxide (KOH) as activating agents. For activation before carbonization, the carbonization process was conducted at various temperatures (600, 750, 850, and 1050 °C). On the other hand, for activation after carbonization, the effect of the volume of the chemical agent solution was studied, with 0, 6, 18, 21, 24, and 30 mL/g of phosphoric acid and 0, 18, 30, 45, 60, and 90 mL/g of 3.0 M KOH solution. The results revealed that in the case of chemical activation before carbonization, the optimum temperature for maximizing specific capacitance was determined to be 900 °C. Conversely, in the case of chemical activation after carbonization, the optimal volumes of the chemical agent solutions were found to be 30 mL/g for phosphoric acid (H 3 PO 4 ) and 21 mL/g for potassium hydroxide (KOH). Moreover, it was observed that utilizing phosphoric acid treatment before the carbonization step leads to an 21% increase in specific capacitance, attributed to the retention of inorganic compounds, particularly silica (SiO 2 ). Conversely, when rice husks were treated with KOH after the carbonization step, the specific capacitance was found to be doubled compared to treatment with KOH prior to the carbonization step due to embedding of SiO 2 and KHCO 3 inorganic constituents. This study provides valuable insights into the optimization of the chemical activation step order and process parameters for enhanced specific capacitance in rice husk-derived activated carbon. These findings contribute to the development of high-performance supercapacitors using rice husk as a sustainable and cost-effective precursor material.
multidisciplinary sciences
-
Synthesis and evaluation of activated carbon from rice husks for removal of humic acid from water
E. Menya,P. W. Olupot,H. Storz,M. Lubwama,Y. Kiros
DOI: https://doi.org/10.1007/s13399-020-01158-2
IF: 4.05
2020-11-26
Biomass Conversion and Biorefinery
Abstract:Activated carbon was synthesized from the New Rice for Africa (NERICA) rice husk variety, followed by its evaluation for removal of humic acid from water. Product values of carbon yield, C and total specific surface area, as,BET were employed as the performance criterion. The best physically activated carbon resulted from char activation at 800 °C for 10 min, leading to as,BET and C×as,BET values of 756.8 and 402.7 m2 g−1, respectively. The best chemically activated carbon resulted from 30 wt% H3PO4 activation of rice husk at 400 °C for 30 min, leading to as,BET and C×as,BET values of 2258.4 and 1058.7 m2 g−1, respectively. Despite the higher as,BET value, the maximum adsorption capacity of the best chemically activated carbon (5.3 mg g−1) was found lower than 8.9 and 27.2 mg g−1 exhibited by the chemically activated carbons prepared at 500 and 600 °C, respectively. The best adsorption conditions included carbon dose of 0.5 g, solution pH of 2, and contact time of 60 min. The adsorption capacity of the prepared activated carbons (27.2 mg g−1) was comparable to that of the commercial activated carbon (30.40 mg g−1). The analyses of the adsorption isotherms and kinetics revealed that the experimental data fits well the Langmuir isotherm model, as well as the pseudo-second-order kinetic model. The latter suggests that the adsorption of humic acid onto the activated carbon was controlled by the chemisorption process. Overall, the study revealed that the NERICA rice husk variety has good prospects for preparation of activated carbons for humic acid adsorption.
energy & fuels,engineering, chemical
-
Preparation and pore characterization of activated carbon from Ma bamboo (Dendrocalamus latiflorus) by H3PO4 chemical activation
Su-Ling Liu,Ya-Nan Wang,Kun-Tsung Lu
DOI: https://doi.org/10.1007/s10934-014-9792-9
2014-03-12
Journal of Porous Materials
Abstract:High specific surface area activated carbon materials have been produced from the naturally occurring Ma bamboo (Dendrocalamus latiflorus) using phosphoric acid (H3PO4) as the activating agent. The effects of different sizes of raw materials, H3PO4 concentrations, and activation temperatures on the specific surface area, pore morphology, and mass yield of activated carbon are presented. A high specific surface area for activated carbon derived from Ma bamboo was achieved under the optimized conditions of 45 wt% H3PO4 impregnation concentration, activation temperature of 400 °C, and a holding time of 120 min. Chemical activation of Ma bamboo by H3PO4 is a useful technique for obtaining activated carbon with desired pore size distributions and pore morphologies from low cost precursors and at low activation temperatures.
materials science, multidisciplinary,chemistry, physical, applied
-
Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons
Kun-Quan Li,Ye Li,Zheng Zheng,Da-Zhi Sang
DOI: https://doi.org/10.13227/j.hjkx.2013.01.042
2013-01-01
Abstract:High surface area activated carbons were prepared with Spartina alterniflora and cotton stalk as raw materials and KOH as activating agent. Effects of materials type, impregnation ratio, activation temperature and heat preservation time on the yield, elemental composition and adsorptive capacity of activated carbon were studied. The properties and pore structure of the carbons were characterized with nitrogen adsorption, powder X-ray diffractometry (XRD), infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). Main pore characteristics of activated carbons were analyzed by BET equation, Horvath-Kawazoe BET method and DFT method. The considerable preparation conditions are obtained as follows: impregnation ratio of 3: 1, an activation temperature of 800 degrees C and an activation time of 1.5 h. The BET surface area of activated carbon prepared from Spartina alterniflora reached 2 825 m2 x g(-1) when its total pore volume, yield, iodine number and methylene blue adsorption were 1.374 cm3 x g(-1), 16.36%, 1797 mg x g(-1) and 495 mg x g(-1) respectively under above conditions. The activated carbon from cotton stalk was prepared with BET surface area of 2 135 m2 x g(-1), total pore volume of 1.038 cm3 x g(-1), yield of 11.22%, methylene blue adsorption of 1 251 mg x g(-1), and iodine number of 478 mg x g(-1), respectively. The methylene blue adsorption and iodine number are much higher than the national first level for activated carbon. The Langmuir maximum adsorption capacities of 2,4-dinitrophenol on the two carbons were 932 mg x g(-1) and 747 mg x g(-1), respectively, which are superior to ordinary activated carbon and activated carbon fiber.
-
The effect of micro wave power on the characterization of activated carbon from rice husk
Yuli Patmawati,Sitti Sahraeni,Amalia Bachtiar,Alwathan
DOI: https://doi.org/10.1063/5.0015795
2020-01-01
Abstract:The production of rice husk in East Kalimantan reached 80,020.4 tons/year. Despite their vast production, rice husk is considered undesirable because has less economic value. The use of rice husk is still limited for kitchen utensils, animal feed, etc. Besides improving its economic and usage values, processing rice husk into activated carbon becomes alternative way of utilization of abundant amount of rice husk. This study aims to determine the effect of micro-wave power on the characteristics of activated carbon produced from rice husk. Activated rice husk-based activated carbon is synthesized using a microwave-assisted chemical activation method. Rice husk which has been prepared -100+120 mesh is carbonized at 500°C for 2 h. Chemical activation was carried out using 10% concentration of Potassium Hydroxide (KOH) for 20 h. Micro wave irradiation is carried out at 180, 378, 468, 657, 792 and 900 watt of output power for 20 minutes. Furthermore, proximate analysis and iodine adsorption number analysis were used to investigate the characteristics of activated carbon produced such as moisture content, ash content, volatile matter, fixed carbon and iodine adsorption number. The quality requirements for activated carbon refers to Indonesian National Standard (SNI 06-3730-1995). The best results were obtained at 792 watt of output power with the characteristics of activated carbon; moisture content, ash content, volatile matter, fixed carbon and iodine absorption number respectively as follows 12.15%, 9.44%, 7.82%, 70.59% and 468.16 mg/g. Activated carbon is a well known material that is used extensively in industrial purification and chemical recovery operations. It the mostly widely used adsorbents and it offers an attractive and inexpensive option for removal of several solutes from aqueous solutions
-
PREPARATION OF ACTIVATED CARBON WITH HIGH SPECIFIC SURFACE AREA FROM CORN COB
Cao Qing,U Yong-kang,Bao Wei-ren,XIE Ke-chang
DOI: https://doi.org/10.3321/j.issn:0253-2417.2005.01.016
2005-01-01
Abstract:A simple,feasible route for utilizing agricultural waste corn cob to prepare activated carbon of high specific surface area has been studied,using KOH as activating agent.The results show that the formation of micro-pore with high specific surface area can be influenced by many factors such as carbonization temperature,heating rate,activating time and the proportion of m (KOH)/m C,the optimal conditions of which are 850 ℃ for activating temperature,450-600 ℃ for carbonization temperature,1.2 h for activating time,3∶1-5∶1 for m (KOH)/m C when the heating rate is 30 ℃/min.In addition,the activating way can also obviously affect the specific surface area of the activated carbon.The structure of activated carbon prepared has narrow pore size distribution and nearly no hysteresis phenomenon is observed.
-
Synthesis of Rice Husk Activated Carbon by Fermentation Osmotic Activation Method for Hydrogen Storage at Room Temperature
Shengming Cheng,Xingxing Cheng,Mudassir Hussain Tahir,Zhiqiang Wang,Jiansheng Zhang
DOI: https://doi.org/10.1016/j.ijhydene.2024.03.092
IF: 7.2
2024-01-01
International Journal of Hydrogen Energy
Abstract:In the present study, an innovative method of fermentation osmotic activation was employed to produce activated carbon derived from rice husk. The fermentation procedure dismantles the robust lignin present on the rice husk surface, thereby liberating amorphous SiO 2 , enhances osmotic activation, and promotes pore development. Following the high -temperature osmosis treatment utilizing a KOH solution, a significant portion of the amorphous SiO 2 on the husk ' s surface is successfully dissolved and removed, leading to the formation of numerous carbon skeletons. This procedure culminates in the production of activated carbon characterized by a high specific surface area and substantial pore volume, attributed to the role of K ions during carbonization. The sample DFRO1-AC exhibited the most effective hydrogen gravimetric storage capacity of 1.21 wt% at room temperature (25 degrees C) and 80 bar pressure, featuring a BET specific surface area of 2270 m 2 /g. Compared to other activated carbons used for hydrogen storage, our materials demonstrate superior hydrogen storage capacity and employ renewable agricultural waste, indicating high feasibility and broad application prospects.
-
Designing microporous activated carbons from biomass for carbon dioxide adsorption at ambient temperature. A comparison between bagasse and rice by-products
Phuoc Hoang Ho,Vivian Lofty,Altaf Basta,Philippe Trens
DOI: https://doi.org/10.1016/j.jclepro.2021.126260
IF: 11.1
2021-04-01
Journal of Cleaner Production
Abstract:<p>Pulping in agro-waste processes are known to affect the chemical constituents of the materials obtained. In this study, activated carbons (ACs) were prepared using precursors based on rice straw, rice husks and bagasse. The composition of these precursors was first determined in order to study the influence of the components of each of these precursors on the sorption properties of the ACs obtained. The ash content was determined by calcination of the precursors as the main component present in ashes is silica, which is known to play a role on sorption processes. The surface chemistry of the ACs was assessed by ammonia thermo-desorption (NH<sub>3</sub>-TPD), before being tested for carbon dioxide capture. ACs obtained from bagasse were capable of capturing up to 14 wt % at atmospheric pressure and 25 °C, regardless of the pulping process applied to the precursor. Rice-husks based AC gave a similar result when the precursor was pulped with a 12% soda solution. Rice straw based ACs were less interesting in terms of CO<sub>2</sub> capture. These differences were rationalized in terms of composition and textural properties.</p>
environmental sciences,green & sustainable science & technology,engineering, environmental
-
Simultaneous Synthesis of Silica Polymorphs and Activated Carbon from Rice Husk
Sri Yani Purwaningsih,Agus Riyanto,Silmi Machmudah,Herbi Enstein Sentosa,Suminar Pratapa
DOI: https://doi.org/10.1007/s12633-024-02881-5
IF: 3.4
2024-02-17
Silicon
Abstract:Rice husk is an agricultural waste rich in carbon and silica contents. So far, no studies have been reported that simultaneously transform it into polymorph silica and activated carbon. This study aims to analyze the thermal event and identify the phase, functional groups, and microstructure of the silica and activated carbon derived from a rice husk. Silica precursor was prepared by the sol-gel route followed by calcining at temperatures of 500–1100 °C with a rise of 200 °C. The residue from the silica preparation was transformed into activated carbon through impregnation, followed by carbonation at 650 °C. Thermal analysis results expose that crystallization of silica occurs at around 900 °C, while the formation of active carbon occurs at lower than 832 °C. XRD analysis revealed that silica calcined at 500 and 700 °C is amorphous, while samples calcined at 900 and 1100 °C are crystalline, with the major and minor phases being cristobalite and tridymite, respectively. The FTIR analysis strengthened this analysis, which detected the presence of Si–O–Si bending vibrations in the sample calcined at 900 °C or more, indicating a phase transition from amorphous to crystalline. A morphological change to a denser structure accompanies this phase transformation. On the other hand, processing the rice husk residue resulted in activated carbon with an amorphous structure and highly porous. The formation of activated carbon was confirmed by the FTIR analysis, which detected the appearance of the C = C group, a characteristic of this substance.
materials science, multidisciplinary,chemistry, physical
-
Physicochemical Properties of Carbons Prepared from Pecan Shell by Phosphoric Acid Activation
Yanping Guo,David A. Rockstraw
DOI: https://doi.org/10.1016/j.biortech.2006.06.027
IF: 11.4
2007-01-01
Bioresource Technology
Abstract:Activated carbons were prepared from pecan shell by phosphoric acid activation. The pore structure and acidic surface groups of these carbons were characterized by nitrogen adsorption, Boehm titration and transmittance Fourier infrared spectroscopy (FTIR) techniques. The characterization results demonstrated that the development of pore structure was apparent at temperatures ⩾250°C, and reached 1130m2/g and 0.34cm3/g, respectively, at 500°C. Impregnation ratio and soaking time at activation temperature also affected the pore development and pore size distribution of final carbon products. At an impregnation ratio of 1.5, activated carbon with BET surface area and micropore volume as high as 861m2/g and 0.289cm3/g was obtained at 400°C. Microporous activated carbons were obtained in this study. Low impregnation ratio (less than 1.5) and activation temperature (less than 300°C) are favorable to the formation of acidic surface functional groups, which consist of temperature-sensitive (unstable at high temperature) and temperature-insensitive (stable at high temperature) two parts. The disappearance of temperature-sensitive groups was significant at temperature ⩾300°C; while the temperature-insensitive groups are stable even at 500°C. FTIR results showed that the temperature-insensitive part was mostly phosphorus-containing groups as well as some carbonyl-containing groups, while carbonyl-containing groups were the main contributor of temperature-sensitive part.
-
Biomass-Based Activated Carbon and Activators: Preparation of Activated Carbon from Corncob by Chemical Activation with Biomass Pyrolysis Liquids
Ping Feng,Jie Li,Huan Wang,Zhiqiang Xu
DOI: https://doi.org/10.1021/acsomega.0c03494
IF: 4.1
2020-09-09
ACS Omega
Abstract:Pyrolysis liquids are the main products in biomass pyrolysis, and the strong acidity limits its utilization. Likewise, activators are required in the process of preparing biomass-based activated carbon, and current activators are usually chemical agents and not sustainable. Both issues are addressed with the new concept of using acidic pyrolysis liquids as the activator of biomass-based activated carbon. In the present research, corncob-based activated carbon was prepared with phosphoric acid and pyrolysis liquids (bio-oil and wood vinegar) as activators. The effects of activation temperature and the types of activators on the structure and surface chemical properties of activated carbon were investigated. Results show that the adsorption performance and specific surface area of activated carbon prepared with bio-oil are not as good as that prepared with phosphoric acid and wood vinegar, but its yield is relatively high. Some alkali and earth alkaline metals remain on the activated carbon prepared by bio-oil and wood vinegar. At 450 °C, the surface area and pore volume of activated carbon prepared with bio-oil and wood vinegar were much smaller than the ones prepared with phosphoric acid. Increasing the activation temperature may improve the performance of activated carbon. The specific surface area of activated carbon prepared with wood vinegar as the activator can reach 384.35 m<sup>2</sup>/g at an activation temperature of 850 °C, which is slightly inferior to that prepared with phosphoric acid as the activator. However, the adsorption amount of methylene blue exceeds the activated carbon prepared with phosphoric acid. This shows that wood vinegar can be used as an activator to prepare biomass-based activated carbon to achieve sustainability of the entire preparation process of biomass-based activated carbon.This article has not yet been cited by other publications.
chemistry, multidisciplinary
-
Preparation of Nanoporous Carbon from Rice Husk with Improved Textural Characteristics for Hydrogen Sorption
Bakhytzhan Lesbayev,Nurgali Rakhymzhan,Gaukhar Ustayeva,Yerkebulan Maral,Meiram Atamanov,Moldir Auyelkhankyzy,Ayazhan Zhamash
DOI: https://doi.org/10.3390/jcs8020074
2024-02-11
Journal of Composites Science
Abstract:This study proposes a method to control the pore-forming process by performing preliminary mechanical activation of the initial rice husk before carbonization. Preliminary mechanical activation of the initial rice husk leads to the loosening of the intercellular substance and its partial depolymerization, thereby increasing the availability of its internal structure for pore formation during carbonization and chemical activation. Using the method described above, nanoporous carbon was obtained with a Brunauer–Emmett–Teller (BET)-calculated specific surface area of 2713 m2/g, a micropore specific surface area calculated by using the Dubinina–Radushkevich (D-R) method of 3099 m2/g, and a total pore volume calculated by using the Barett–Joyner–Halenda (BJH) method of 1.625 cm3/g. Due to these characteristics, the adsorption capacity in the obtained sample was for hydrogen 3.7 wt.% at a temperature of −190 °C and a pressure of 9 kgf/cm2, which is 29.7% higher than the adsorption capacity of nanoporous carbon obtained based on rice husk without mechanical activation. The composite “carbon–platinum” NC-2/Pt10%, at a temperature of 20 °C and a pressure of 9 kgf/cm2, showed an increase in sorption capacity of 27% compared to pure nanoporous carbon NC-2, which is explained by the emergence of the spillover effect.
-
Preparation of High Surface Area Activated Carbon from Spent Phenolic Resin by Microwave Heating and KOH Activation
Song Cheng,Libo Zhang,Shengzhou Zhang,Hongying Xia,Jinhui Peng
DOI: https://doi.org/10.1515/htmp-2016-0042
2018-01-26
High Temperature Materials and Processes
Abstract:Abstract The spent phenolic resin is as raw material for preparing high surface area activated carbon (HSAAC) by microwave-assisted KOH activation. The effects of microwave power, activation duration and impregnation ratio (IR) on the iodine adsorption capability and yield of HSAAC were investigated. The surface characteristics of HSAAC were characterized by nitrogen adsorption isotherms, FTIR, SEM and TEM. The operating variables were optimized utilizing the response surface methodology (RSM) and were identified to be microwave power of 700 W, activation duration of 15 min and IR of 4, corresponding to a yield of 51.25 % and an iodine number of 2,384 mg/g. The pore structure parameters of the HSAAC, i. e., Brunauer–Emmett–Teller (BET) surface area, total pore volume, and average pore diameter were estimated to be 4,269 m 2 /g, 2.396 ml/g and 2.25 nm, respectively, under optimum conditions. The findings strongly support the feasibility of microwave-assisted KOH activation for preparation of HSAAC from spent phenolic resin.
materials science, multidisciplinary
-
Study of the Enhancements of Porous Structures of Activated Carbons Produced from Durian Husk Wastes
Tongsai Jamnongkan,Nitchanan Intaramongkol,Nattharika Kanjanaphong,Kemmika Ponjaroen,Wasana Sriwiset,Rattanaphol Mongkholrattanasit,Piyada Wongwachirakorn,Kun-Yi Andrew Lin,Chih-Feng Huang
DOI: https://doi.org/10.3390/su14105896
IF: 3.9
2022-05-13
Sustainability
Abstract:The idea of generating high-value practical materials, such as activated carbons, from agricultural wastes as a raw material has been a quite important trend recently due to its positive contributions to the environment and resource savings from biomass. In this paper, activated carbons prepared from durian husk waste by the KOH chemical activation method are studied. We focus on the effects of stages of the activating temperature on their properties. The optimum conditions for activation were a KOH/char ratio of 1:2 at the first and second activation process at the temperatures of 400 and 800 °C, respectively. The characterization results of Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and Brunauer–Emmett–Teller (BET) surface area showed that the obtained activated carbons have a high surface area and small pore size. The adsorption/desorption isotherms of the obtained activated carbons showed type I and type II isotherms. The chemical structure of obtained activated carbons did not show any variation in the surface functional groups. A feasible method to produce the activated carbons with a high surface area and high adsorption capability from durian husk waste was eventually demonstrated.
environmental sciences,environmental studies,green & sustainable science & technology
-
Effect of Co-solution of Carbon Precursor and Activating Agent on the Textural Properties of Highly Porous Activated Carbon Obtained by Chemical Activation of Lignin With H3PO4
Imane Moulefera,Francisco J. García-Mateos,Abdelghani Benyoucef,Juana M. Rosas,José Rodríguez-Mirasol,Tomás Cordero
DOI: https://doi.org/10.3389/fmats.2020.00153
2020-05-21
Frontiers in Materials
Abstract:This work analyzes the effect of co-solution of carbon precursor and activating agent on the textural and surface chemistry properties of highly nanoporous activated carbons obtained by chemical activation of Alcell lignin with phosphoric acid. The success of this methodology highlights the possibility of directly using the liquors produced in organosolv process (Alcell) to prepare activated carbons by chemical activation with phosphoric acid. Co-solutions of lignin and phosphoric acid were submitted to a two steps thermal treatment, which consisted of a first oxidative treatment in air at 200°C, followed by a thermal treatment in N2 at 400°C, where activation of the oxidized lignin with phosphoric acid took place. A lignin-derived activated carbon with very high apparent surface area (2550 m2/g) and pore volume (1.30 cm3/g) was obtained with an initial phosphoric acid to lignin mass ratio of 2. Up to now, this is one of the highest values of apparent surface area reported not only for activated carbons prepared from lignin, but even for porous carbons prepared by chemical activation of other lignocellulosic materials with phosphoric acid. The use of lignin and phosphoric acid co-solution provided larger and more homogeneous effective interactions between the carbon precursor and the activating agent, by the formation of phosphate esters in the lignin matrix, which seems to be a key factor in the subsequent treatments: promoting crosslinking reactions in the carbonaceous matrix during the oxidative treatment in air at 200°C and enhancing the development of a wide porosity during the following activation thermal treatment.
materials science, multidisciplinary
-
Mechanism of Biomass Activation and Ammonia Modification for Nitrogen-Doped Porous Carbon Materials.
Kaixu Li,Wei Chen,Haiping Yang,Yingquan Chen,Sunwen Xia,Mingwei Xia,Xin Tu,Hanping Chen
DOI: https://doi.org/10.1016/j.biortech.2019.02.039
IF: 11.4
2019-01-01
Bioresource Technology
Abstract:The effect of chemical activation and NH3 modification on activated carbons (ACs) was explored via two contrasting bamboo pyrolysis strategies involving either two steps (activation followed by nitrogen doping in NH3 atmosphere) or one step (activation in NH3 atmosphere) with several chemical activating reagents (KOH, K2CO3, and KOH + K2CO3). The ACs produced by the two-step method showed relatively smaller specific surface areas (similar to 90% micropores) and lower nitrogen contents. From the one-step method, the ACs had larger pore diameters with about 90% small mesopores (2-3.5 nm). Due to a promotion effect with the KOH + K(2)CO(3 )combination, the AC attained the greatest surface area (2417 m(2) g(-1)) and highest nitrogen content (3.89 wt%), endowing the highest capacitance (175 F g(-1)). The balance between surface area and nitrogen content recommends KOH + K(2)CO(3 )activation via the one-step method as the best choice for achieving both greener production process and better pore structure.
-
Conversion of rice husks into carbonaceous materials with porous structures via hydrothermal process
Sayaka Sugie,Hirotaka Maeda
DOI: https://doi.org/10.1007/s11356-024-34217-6
IF: 5.8
2024-07-08
Environmental Science and Pollution Research
Abstract:Abstract Carbonaceous materials hydrothermally produced using waste biomass have small specific surface areas (SSA) and poor porosity properties. In this study, we prepare a novel carbonaceous material with excellent porosity properties by suppressing the formation of a secondary char phase (spheres) and promoting biomass hydrolysis by controlling the hydrothermal conditions. Rice husk powders, as the starting material, are hydrothermally treated using acidic solvents of different types and concentrations at 180 °C. The surfaces of the samples hydrothermally prepared using the acidic solvents have no spheres. In the case of 0.1–0.2 mol L −1 hydrochloric acid (HA), the amorphous carbonaceous materials contain numerous mesopores and exhibit a larger SSA (approximately 100 m 2 g −1 ) than those prepared using acetic acid and distilled water. An increase in the hydrothermal temperature reduces the porosity properties of the materials. Finally, the high-porosity amorphous carbonaceous material showed excellent trimethylamine adsorption ability.
environmental sciences