Abstract:In the present study, a novel combustion method was proposed to synthesize nanomaterials, and nano-sized MnOx was prepared by this method as example. Being different from the traditional solution combustion synthesis method, a cigarette butt (CB, a typical municipal solid waste), rather than the pure soluble organics (e.g., glycine, urea, citric acid, etc.), was used as the fuel. In this process, the cellulose acetate-based cigarette butt also acted as the support or template, because the manganese nitrate in the solution will be adsorbed and dispersed uniformly on the surface of the cellulose acetate filters. After burning the impregnated cigarette butts, the nano-sized MnOx was obtained. Both smoldering and flaming combustion with different ignition temperatures were considered in the combustion synthesis process. Thermogravimetric (TG) analysis was conducted to study the combustion behavior of the pure and manganese nitrate-loaded cigarette butts. XRD, FE-SEM, TEM, XPS, H2-TPR and N2 adsorption–desorption were conducted to detect the physical and chemical characteristics. The product obtained via this combustion method was main in the Mn3O4 phase. The prepared nanoparticles with different ignition temperatures have a uniform particle size distribution (40–50 nm). The MnOx synthesized by smoldering showed better porosity than the flaming-combustion-synthesized MnOx. The H2-TPR and XPS characterization showed that both of the catalysts synthesized by either the smoldering or flaming combustion process, possessed similar redox properties. The nano-MnOx catalyst was applied for the selective catalytic reduction of NO, and the results suggested that MnOx synthesized by smoldering had more stable activity.

Preparation, Characterization and Application of a New Kind of Mesoporous Composite

Synthesis of Si/O/C/N Quaternary Composite Aerogels with Micro/mesoporous Structures and Their Selective Adsorption Property for Volatile Carbonyl Compounds in Cigarette Smoke

The application of the composite porous materials to reduce the harmful compounds in mainstream smoke

Generalized and High Temperature Synthesis of a Series of Crystalline Mesoporous Metal Oxides Based Nanocomposites with Enhanced Catalytic Activities for Benzene Combustion

Preparation and Characterization of Mesoporous CuO/ZSM-5 Catalysts for Automotive Exhaust Purification

Selective reduction of HCN and phenol in mainstream cigarette smoke using metal-doped oxide material with porous structure

CuO/MnO X Composites Obtained from Mn-MIL-100 Precursors As Efficient Catalysts for the Catalytic Combustion of Chlorobenzene

Co-nanocasting Synthesis of Mesoporous Cu–Mn Composite Oxides and Their Promoted Catalytic Activities for Gaseous Benzene Removal

Preparation and characterization of Cu–Mn composite oxides in N 2 O decomposition

Preparation and Characterization of Hierarchically Porous SiO2@C@MnO2 Monoliths

A Novel Porous Ceramic Membrane Supported Monolithic Cu-Doped Mn–Ce Catalysts for Benzene Combustion

Nanosized mesoporous manganese oxides: Synthesis, characterization, catalytic combustion of toluene

Facile Preparation and Efficient MnxCoy Porous Nanosheets for the Sustainable Catalytic Process of Soot

Study on selective reduction of Benzo(a)Pyrene from cigarette smoke by mesoporous materials

Significant Removal of Harmful Compounds in Mainstream Cigarette Smoke Using Carbon Nanotubes Mixture Prepared by Catalytic Pyrolysis

Nanoporous CeO2-Decorated Cu-SmMn2O5 Composite Mullite Oxide Catalyst for Toluene Oxidation

Flaming combustion and smoldering of active impregnated cigarette butts: A novel method for synthesis of nanostructured MnOx catalysts for NOx reduction

Preparation of Self-Modeling Composite Material and Its Selective Adsorption Towards Crotonaldehyde in Mainstream Cigarette Smoke

Preparation, Electrocatalytic and Photocatalytic Performances of Nanoscaled CuO/Co 3 O 4 Composite Oxides

Cu-Mn-Ce Mixed Oxides Catalysts for Soot Oxidation and Their Mechanistic Chemistry

The Preparation Of Nio/Sba-15 Composites And Their Catalytic Properties