Abstract:Mordenite and ZSM-5 seeds could grow on the surface of an asymmetric α-Al2O3 support using an identical organic-free aluminosilicate solution under the same hydrothermal conditions. It suggests that the phase of zeolite can be controlled by varying the type of seed. Continuous mordenite and ZSM-5 membranes were prepared by the secondary growth method using corresponding seeds under appropriate conditions. The water content in the secondary growth mixture strongly influenced the growth of zeolite crystals. ZSM-5 seeds grew at a smaller rate and showed a habit of thin hexagonal plate in a concentrated mixture, while the crystals with a habit of rectangular parallelepiped were formed from a diluted secondary growth mixture. ZSM-5 crystals had poor intergrowth in the former case, whereas the crystals were highly intergrown in the latter case. ZSM-5 crystals in either membrane have a random orientation. In contrast to ZSM-5 zeolite, the crystal orientation in the secondary grown mordenite membranes strongly depended on the water content in the secondary growth mixture. The crystals in the mordenite membrane developed in a diluted secondary growth mixture were oriented with the (150) face parallel to the support surface, whereas the crystals in the membrane grown in a concentrated mixture were oriented with the (002) face parallel to the support surface. These results suggest that the crystal orientation in mordenite membranes can be manipulated only by changing the water content in a secondary growth mixture. The formation of the preferred crystal orientation in the secondary grown mordenite membrane is discussed in terms of an “evolutionary selection” process.

Seeded growth of beta zeolite membranes using zeolite structure-directing agent

The control of phase and orientation in zeolite membranes by the secondary growth method

Preparation of Zeolite NaA Membranes on Macroporous Alumina Supports by Secondary Growth of Gel Layers

Seeded Synthesis of Small Polycrystalline NaY Zeolite Membrane Using Zeolite Structure-Directing Agent and Its Pervaporation Performance

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Studies on the Preparation of Beta Zeolite Membrane on Porous α-Al2O3 Tubes

A Facile Preparation of High Flux NaA Zeolite Membranes by Direct Secondary Growth of Wet Gel Layer

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Preparation of Asymmetric Zeolite NaA Membrane Layers by Vapor Phase Transfer and Seeded Growth Method

Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting–rubbing seeding method: Role of wetting agent

SYNTHESIS AND CHARACTERIZATION OF A-TYPE ZEOLITE MEMBRANES ON ALUMINA PARTICLES SURFACE

Seeded Secondary Growth Synthesis of Zif-8 Membranes Supported on Alpha-Al2o3 Ceramic Tubes

Mechanism of Seeding in Hydrothermal Synthesis of Zeolite Beta with Organic Structure-Directing Agent-Free Gel

Influences of Seeds on the Properties of Zeolite NaA Membranes on Alumina Hollow Fibers

Synthesis of Naa Zeolite Membrane on Seeded Substrate and Its Characterization

A novel method for preparation of ZSM-5 zeolite membrane on porous α-Al2O3 tubes

Preparation of NaA Zeolite Membrane on Macroporous α-Al2O3 Support by Two-Step-Seeding Method

Synthesis and Characterization of (h0l) Oriented High-Silica Zeolite Beta Membrane

Dense A-Type Zeolite Membrane Synthesized by Seeding

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

ZSM-5 Zeolite Membranes Prepared on Porous Α-Al2o3 Tube from a Template-free Crystallization Gel