Study on Influencing Factors of Photocatalytic Degradation of Methylene Blue by Nano-TiO2

Pu Xu,Shanmin Gao,Baibiao Huang,Ying Dai,Yanbin Xu,Shaoying Li,Xianjun Zhu
DOI: https://doi.org/10.3969/j.issn.1671-4776.2008.10.005
2008-01-01
Abstract:Nano-TiO2 particles were prepared by hydrolytic precipitation method using TiCl4 as the raw materials and then heat-treatment in ambient atmosphere at different temperatures for two hours.X-ray diffraction(XRD),transmission electron microscope(TEM)and UV-Vis absorbance spectroscopy were used to characterize the products.Because of the photocatalytic activity of nano-TiO2 prepared above,the methylene blue was degraded by photo-catalysis using halogen tungsten light.The effects of heat-treatment temperature,pH value,adding H2O2 at different pH values of aqueous solutions on the degradation process were studied.For TiO2 particles prepared by the hydrolytic precipitation method,with the increase of calcining temperature,the crystal structure changes gradually from anatase to rutile,the particle size increases and the absorption profile shifts to longer wave to some degree.XRD results indicate that anatase nano-TiO2 starts to transform into rutile structure at the temperature of 600 ℃,and completes this transformation at 1 000 ℃.The nano-TiO2 calcined at 800 ℃ with anatase and rutile mixed phase exhibits better photocatalytic activity than pure anatase and rutile nano-TiO2 particles,and the methylene blue solution is degraded by 97% after 90 min illumination under 300 W halogen tungsten light.
What problem does this paper attempt to address?