Abstract:An understanding of the support effect is fundamental for guiding the rational design of heterogeneous catalysts. Herein, the role of pore structure on metal dispersion and catalytic performance was comprehensively investigated using Ni/Al2O3 catalysts. Three different Al2O3 supports, including Al2O3 microspheres prepared in microchannels and two commercially available Al2O3 supports named Sample 1 and Sample 2, were used and the Ni/Al2O3 catalysts were prepared by wetness impregnation method. X-ray diffraction, transmission electron microscopy, H2 temperature-programmed reduction, X-ray photoelectron spectroscopy, N2 adsorption-desorption, and H2 pulse chemisorption analyses combined with a sintering kinetic model were used to investigate the effect of the support pore structure. The narrow pore size distribution (3-15 nm) of Al2O3 microspheres and Sample 1 led to a uniform NiO dispersion for the calcined catalysts. Moreover, the high specific surface area (291 m2/g) and large pore volume (1.0 mL/g) of the Al2O3 microspheres were beneficial for the deposition of NiO particles inside mesopore to obtain a stronger metal-support interaction. Owing to the smaller NiO nanoparticles and stronger metal-support interaction, the reduced Ni/Al2O3 microspheres exhibited an average Ni particle size of 10.2 nm under 36 wt% nickel loading, whereas the average Ni particle size loaded on Sample 1 and Sample 2 were 12.6 nm and 13.2 nm, respectively. The optimized CO2 conversion of 87.0% at 300 degrees C under atmospheric pressure was attributed to the large pore volume and uniform Ni dispersion of Ni/ Al2O3 microsphere catalysts while the same value for Sample 1 and Sample 2 catalysts was 81.5% and 55.0%, respectively. This work provides valuable guidelines for designing effective CO2 methanation support and proves the potential application of Al2O3 microspheres for CO2 methanation.

Effect of nitric acid treatment of cordierite support on structure of monolithic catalysts for dimethyl oxalate synthesis

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Effects of Pore Structure on Methanol Selectivity in Carbon Monoxide Hydrogenation

Effect of Chemical Treatment of Activated Carbon As a Support for Promoted Dimethyl Carbonate Synthesis by Vapor Phase Oxidative Carbonylation of Methanol over Wacker-type Catalysts

Effect of acid/alkali treatment on the structure and catalytic performance of 3DOM CeCo0.7Mn0.3O3 catalyst

Cordierite and citric acid regulate crystal structure of manganese oxide for effective selective catalytic reduction of nitrogen oxide

Effects of the Support Brønsted Acidity on the Hydrodesulfurization and Hydrodenitrogention Activity of Sulfided NiMo/Al 2 O 3 Catalysts

Enhancement of SCR Activity and Mechanical Stability on Cordierite Supported V2O5-WO3/TiO2 Catalyst by Substrate Acid Pretreatment and Addition of Silica

Effect of Pore Structure on Ni/Al2O3 Microsphere Catalysts for Enhanced CO2 Methanation

Preparation of macroporousα-Al2O3 support and its application in preparing catalyst for CO coupling reaction

Effect of specific surface area and pore diameter of support on acidity and catalytic performance of Nb2O5/α-Al2O3

Preparation and catalytic activities of Lanthanum strontium manganite based catalysts supported on honeycomb ceramics

Study on the mechanism of acid treatment La0.8Sr0.2Mn0.8Cu0.2O3 to improve the catalytic activity of formaldehyde at low temperature

Effect of Support Pore Structure on Hydrodesulfurization Performance of Catalyst

EFFECT OF CALCINATION TEMPERATURE ON THE STRUCTURE AND CATALYTIC PERFORMANCE OF THE CU-MCM-41 CATALYSTS FOR THE SYNTHESIS OF DIMETHYL CARBONATE

Effect of TiO2-Al2O3 support surface properties on active phase structure and hydrodenitrogenation performances of the corresponding NiWS supported catalysts

Influence of Different Supports on the Physicochemical Properties and Denitration Performance of the Supported Mn-based Catalysts for NH3-SCR at Low Temperature

Nitric Acid-Pretreated Natural Halloysite Nanotubes As Ni Nanoparticle Catalyst Supports for CO2 Methanation

Preparation of Supported Alkaline Catalysts and Their Applications to Transesterification and Carbonylation of Methanol and Diethylamine

Effect of Surface Properties of Activated Carbon on CO Oxidation over Supported Wacker-type Catalysts