Abstract:This study addressed different materials to coat iron oxide, after using co-precipitation to synthesize. During synthesizing iron oxide, FeSO4•7H2O as a single raw material , was emphasized as a precursor salt. In advance, FeSO4•7H2O was oxidized into trivalence by using hydrogen peroxide, allocated Fe(Ⅱ)and Fe(Ⅲ) mole ratio as one to two, and synthesized ferric ferrous oxide nanoparticle by sodium hydroxide co-precipitation, which TX-100 was a protective agent to disperse uniformly. Depend on the morphology of several nanopartical types through the processing, separation of precursor salt solution and NaOH solution in pump by adding TX-100 solution would get Fe3O4 ratio more evenly. Besides during the experiment, variety loading of NaOH and dispersant, using two- stage method to add NaOH as well, rod and particle mixure would obtain. XRD, SQUID, HRTEM and SEM were used to analyze the particle size, uniformity, Magnetic, and Crystal structure. Also, intend to find the relation among synthesis and properties, and continue to work on electrodes for battery application to seek the optimal performance corresponded to synthesis conditions. Preparation of Fe3O4@Ag was took AgNO3 and C6H12O6, the reductant, into Fe3O4 solution. Different mole ratio of AgNO3 and Fe3O4 were mix- coated. Through the process, surface modifier makes coating completely and uniformly. Later, same analysis entailed to Fe3O4@Ag product powder. The purpose was to examine its completely coating, thickness, and magnetism.

Study on the Synthesis of Cyanex 301-Modified Fe2O3 Nanoparticles

Influence of Different Preparation Methods on Crystallisation and Morphology of Fe2o3 Nanoparticles

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

A Study of Modified Fe3O4 Nanoparticles for the Synthesis of Ionic Ferrofluids

Preparation and Characterization of Nanoized Fe3O4 Magnetic Particles Modified by Silane

Synthesis of Fe3O4 Nanoparticles by Co-precipitation and Micro-reactor Method

Synthesis of Fe3+-modified SnO2 nanoparticles by hydrothermal method

Synthesis and Characterization of Fe3O4 Nanoparticles by a Solvothermal Method

The study of novel Fe3O4@γ-Fe2O3 core/shell nanomaterials with improved properties

Preparation and characterization of Fe3O4 nanoparticles via a hydrothermal process with propanediol as the solvent

Preparation of Composite Nanoparticles of Fe-Zn Bioxide Using Surface Modification and Their Subsequent Characterization

Study on the Synthesis and Application of Core-Shell Structured Nanoparticles of Fe3O4

The Structure of Modified Fe-Ni Bioxide Composite Nanoparticles Using Fe(NO 3 ) 3

Synthesis of Water-Soluble Fe<sub>3</sub>O<sub>4</sub> Nanopowder and Its Cr(VI) Adsorption Properties

Synthesis of Water-soluble Fe3O4 Nanocrystals with a Phase-transfer Method

Surface modification and characterization of γ-Fe2O 3 nanoparticles synthesized by chemically-induced transition

Research on Modification of Fe3O4 Magnetic Nanoparticles with Two Silane Coupling Agents

Synthesis and characterization of Fe3O4/SiO2 core-shell nanoparticles in reverse micelles

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Synthesis and characteristics of Fe3+-doped SnO2 nanoparticles via sol–gel-calcination or sol–gel-hydrothermal route