Well-Adhered Ti Alloying Layer on NiTi Alloy: Surface Ni Content, Corrosion Resistance, and Cytocompatibility
Jie Gao,Yongbing Xin,Jin Bai,Hongjun Hei,Shengwang Yu,Bing Zhou,Ke Zheng,Yong Ma
DOI: https://doi.org/10.1007/s11665-023-09107-6
IF: 2.3
2024-01-24
Journal of Materials Engineering and Performance
Abstract:In this paper, well-adhered Ti surface alloying layers were deposited on NiTi alloy using plasma surface alloy technology for inhibiting the out diffusion of Ni and improving its biological properties. The effect of deposition time on the microstructure, Ni content on the surface, the corrosion resistance, the hydrophilicity, the protein adsorption, and the cell adhesion properties were investigated and compared. The results show that Ti alloying layers deposited for different times were not pure Ti layers but consists of alternatively distributed Ti-riched regions and near-pure Ti regions, which contains α -Ti, NiTi 2 and newly formed NiTi phases. Under the combined action of titanium atom deposition and nickel atom diffusion, the Ni content on the surface of NiTi alloy decreased obviously. Among the Ti alloying layers deposited at 1, 2, and 3 h, the Ti alloying layer prepared at 2 h has the highest surface Ni content 10.88 at.%, while that prepared at 3 h has the lowest Ni content of 5.92 at.%. Due to the surface Ti alloying layer, the corrosion resistance of NiTi in DMEM solution is increased by 1 order of magnitude. Among them, the NiTi sample with Ti alloying layer deposited for 3 h has the highest corrosion resistance. The sample with Ti alloying layer deposited for 1 h had the lowest absorbed protein and the highest adhered osteoblasts. However, considering the long-term implantation of NiTi alloy, the Ti alloying layer deposited for 3 h with the least Ni content, the best corrosion resistance in DMEM solution, as well as the second cytocompatibility has the best application potential.
materials science, multidisciplinary