Abstract:Mg–Zn–Y–Nd alloy was prepared by casting and hot extrusion. The microstructure and mechanical properties of OM, SEM, XRD, TEM, and tensile tests were investigated with casting and hot extruded alloys. The results demonstrate that in a casting Mg–Y–Nd–Zr alloy, the α-Mg matrix is separated into the cell structure by a discontinuously distributed coarse Mg24Y5/α-Mg eutectic structure and fine Mg12Nd particles. TEM analysis shows that the Mg12Nd and Mg24Y5 phases have the orientation of \( {\left[001\right]}_{{\mathrm{Mg}}_{12}\mathrm{Nd}}//{\left[0221\right]}_{\upalpha -\mathrm{Mg}} \), and \( {\left[111\right]}_{{\mathrm{Mg}}_{24}{\mathrm{Y}}_5}//{\left[0001\right]}_{\upalpha -\mathrm{Mg}} \) and \( {\left(10\overline{1}\right)}_{{\mathrm{Mg}}_{24}{\mathrm{Y}}_5}//{\left(10\overline{1}0\right)}_{\upalpha -\mathrm{Mg}} \), respectively. The hot extrusion separates the Mg24Y5/α-Mg eutectic structure into fragments and aligns fragmentary Mg24Y5 particles along the extrusion direction. The interaction of hot extrusion and strengthening particles refines the α-Mg matrix greatly. Moreover, large strains result in the stacking faults of the matrix. As compared to the casting alloy, the hot-extruded one exhibits high yield strength, ultimate tensile strength, and elongation, which should be ascribed to the grain fineness, optimum distribution of strengthening particles and multiple substructures.

Effect of Pouring Temperature on Microstructures and Mechanical Properties of Mg-5Al-0.5Y-0.5Nd Alloy

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Effects of Mould Structure and Pouring Temperature on Mechanical Properties of Mg-6Al-2.4Y Alloy

Effects of Y and Nd combined addition on mechanical properties of Mg-6Al alloy

Influence of pouring temperature on solidification behavior, microstructure and mechanical properties of sand-cast Mg-10Gd-3Y-0.4Zr alloy

Microstructures and Mechanical Properties of As-Cast Mg–5Al–0.4Mn–xNd (x = 0, 1, 2 and 4) Alloys

Effects of Y and Nd on Microstructure and Properties of Mg-5Al Alloy

Effect of Grain Size on the Microstructure and Mechanical Properties of Mg-4Y-3Nd-0.5Zr Alloy

Effects of Minor Y Addition on Microstructure and Mechanical Properties of Mg-Nd-Zn-Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Hot Extrusion Effect on the Microstructure and Mechanical Properties of a Mg–Y–Nd–Zr Alloy

Microstructure and Mechanical Properties of Mg-7Zn-3Al Alloy with Nd and Y Additions

Microstructure and High-Temperature Mechanical Properties of Mg-6Al Magnesium Alloy Containing Yttrium

Effects of Al and Y Addition on Microstructures and Mechanical Properties of As‐Cast Mg–14Li Based Alloy

Microstructures and mechanical properties of Mg–2Y–1Mn–1–2Nd alloys fabricated by extrusion

Effect of Al on Microstructure and Mechanical Properties of Mg-10Li-3Zn-1Y Alloys

Effects of Nd on Microstructure Mechanical Properties of Mg-10Gd-3Y-0.5Zr Alloy

Effect of Y content on microstructure and mechanical properties of as-cast Mg–8Li–3Al–2Zn alloy with duplex structure

Effect of Heat Treatment on Microstructure, Mechanical Properties and Fracture Behaviors of Sand-Cast Mg-4Y-3Nd-1Gd-0.2Zn-0.5Zr Alloy

Effects of Y on Microstructure and Mechanical Properties of Extruded Mg-5Al-1Ca Magnesium Alloys

Microstructure and mechanical properties of Mg–4Al–4Nd–0.5Zn–0.3Mn alloy