Abstract:Currently, activated coke is widely used in the removal of multiple pollutants from industrial flue gas. In this paper, a series of novel FexLayOz/AC catalysts was prepared by the incipient wetness impregnation for NH3-SCR denitrification reaction. The introduction of Fe-La bimetal oxides significantly improved the denitrification performance of activated coke at mid-high temperature, and 4% Fe0.3La0.7O1.5/AC exhibited a superior NOx conversion efficiency of 90.1% at 400 °C. The catalysts were further characterized by BET, SEM, XRD, Raman, EPR, XPS, FTIR, NH3-TPD, H2-TPR, et al., whose results showed that the perovskite-type oxide of LaFeO3 and oxygen vacancies were produced on the catalysts’ surfaces during roasting. Fe-La doping enhanced the amount of acid sites (mainly Lewis and other stronger acid sites) and the content of multifarious oxygen species, which were beneficial for NOx removal at mid-high temperature. Moreover, it was investigated that the effect of released CO from activated coke at mid-high temperature on the NOx removal through the lifetime test, in which it was found that a large amount of CO produced by pyrolysis of activated coke could promote the NOx removal, and long-term escaping of CO on the activated coke carrier did not have a significant negative impact on catalytic performance. The results of the TG-IR test showed that volatile matter is released from the activated coke while TG results showed that the weight loss rate of 4% Fe0.3La0.7O1.5/AC only was 0.0015~0.007%/min at 300–400 °C. Hence, 4% Fe0.3La0.7O1.5/AC had excellent thermal stability and denitrification performance to be continuously used at mid-high temperature. Finally, the mechanisms were proposed on the basis of experiments and characterization results.

Investigation of water resistant performance of activated carbon supported tungstophosphoric acid in the process of flue gas denitration

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Nitrogen Doping of Activated Carbon Loading Fe2O3 and Activity in Carbon-Nitric Oxide Reaction

Experimental study on integrated desulfurization and denitrification of low-temperature flue gas by oxidation method

Investigation of modified carbon-based catalyst on low-temperature selective reduction of flue gas denitration performance

Removal of NOX Using Hydrogen Peroxide Vapor over Fe/TiO2 Catalysts and an Absorption Technique

Performance on desulfurization and denitrification of one-step produced activated carbon for purification of sintering flue gas

Denitration catalyst containing tungsten tin manganese cerium composite oxide as well as preparation and application of denitration catalyst

Influences of Water Vapor and CO2 on NOx Removal by Plasma-facilitated Selective Catalytic Reduction

Denitration catalyst with tungstovanadophosphoric heteropolyacid as precursor and preparation method of denitration catalyst

Effect of Nitrogen Doping on the Reduction of Nitric Oxide with Activated Carbon in the Presence of Oxygen

Regeneration of the Waste Selective Catalytic Reduction Denitrification Catalyst by Nitric Acid Washing

Experimental Analysis of Desulfurization and Denitrification Effect of Activated Carbon Fiber Modified by Low Temperature Plasma

Study on the Denitrification Performance of FexLayOz/activated Coke for NH3-SCR and the Effect of CO Escaped from Activated Coke at Mid-High Temperature on Catalytic Activity.

Effect of Original Activated Carbon Support and the Presence of NOx on CO Oxidation over Supported Wacker-type Catalysts

Revealing the Key Role of Acidic Oxygen-Containing Groups on Activated Carbon for Low-Temperature NH3-SCR Denitration

SELECTIVE REDUCTION DENITRIFICATION OF FLUE GAS BY USING CATALYST Ag/Al2O3 AND REDUCING AGENT C3H6

Research on deeply modified Fenton sludge for the selective catalytic reduction of NO x : Promotion mechanism of acidification reorganization

Coupling mechanism of activated carbon mixed with dust for flue gas desulfurization and denitrification

Low temperature denitration and synergetic desulfurization active carbon catalyst and preparation method thereof

Effect of Na 2 CO 3 , HF, and CO 2 Treatment on the Regeneration of Exhausted Activated Carbon Used in Sintering Flue Gas