MICROSTRUCTURE AND MECHANICAL PROPERTY OF Ti-80%Ni ALLOY PREPARED BY LASER SOLID FORMING

Xu Xiaojing,Lin Xin,Huang Weidong,Wang Liang
DOI: https://doi.org/10.3724/sp.j.1037.2010.00190
IF: 1.797
2010-01-01
ACTA METALLURGICA SINICA
Abstract:Ti-80%Ni alloy was prepared by laser solid forming(LSF) under different processing parameters.The microstructure of the alloy consists ofη-TiNi_3 phase under low scanning rate v and power P.With the increase of scanning rate,TiNi(B2)+ηeutectic appeared,and with the increase of laser power,ηlaths were broken into bulks and distributed along certain orientation,and(TiNi(B_2)+η) devoiced eutectic+inter-lath(TiNi(B2)+η) eutectic appeared.The higher the power is,the finer theηbulks are.And the enhanced power leads to a growing up of(TiNi(B2)+η) eutectic volume fraction. The microstructure became much fine with increasing v and P,while the volumn fraction of hard-brittleηlath decreased,as a result,the laser formability and plasticity of Ti-80%Ni both increased.