Abstract:Journal of Composite Materials, Ahead of Print. One of the primary challenges faced by sandwich composites is facesheet-core debonding, which can be mitigated through various techniques such as z-pinning and stitching through the thickness. This study investigates the impact of stitching on the bending behavior of sandwich composites comprising E-glass composite facesheets and a polyurethane foam core, employing experimental, numerical, and analytical methods. Specimens were stitched at three stitch spacings of 0.5, 1, and 2 cm, with a stitch pitch of 0.8 cm and stitch seam angles of 0°, 90°, 0/90°, ±45°, 45°/90°, and ±60°. Analysis of facesheet bending stress, core shear stress, and bending rigidity of stitched specimens was conducted through three-point bending tests and compared with unstitched specimens. Results indicate that reducing stitch spacing, thereby increasing stitch density, improves bending strength, and the best bending behavior observed at ±45° stitch seam angles. Damage assessment revealed fractures and depression of the foam, wrinkles on the upper facesheet, and buckling failure of resin columns. Additionally, a theoretical model predicted bending rigidity, showing good agreement (4%–15%) with experimental data. Finite element analysis using the ABAQUS program validated the experimental results, suggesting numerical modeling as a viable method for predicting flexural properties of stitched foam core sandwich composites.

Mechanical Behavior Tests of Composites Stitched Sandwich Panels

Effects of stitching parameters on the flexural properties of stitched foam core sandwich composites

Shear Stiffness Prediction of Stitched Composite Sandwich Structure with Foam Core

Mechanical performance of stitched foam-filled honeycomb sandwich panels

Experiment and Analysis on Mechanical Properties of Stitched Laminates

Edgewise compressive test and analysis for lattice web reinforced composite sandwich panels with foam core

Investigation and prediction of laminate quality and interlaminar mechanical performance of the tufted sandwich composites with different core structures

Mechanical Properties Test and Failure Analysis of Composite Foam Sandwich Structure in Ramp-Down Zone

Experimental research on shear property of foam core sandwich composite panels with enhanced interface

Experimental and Numerical Studies on Core Stiffened Sandwich Composite Panel

Experimental study on the compression-after-impact behavior of foam-core sandwich panels

Mechanical behaviours of composite sandwich panel with strengthened pyramidal truss cores

Mechanical Behavior of Sandwich Panels with Hollow Al-Si Tubes Core Construction

Effect of stitching angle on mechanical properties of stitched sandwich panels

EFFECT OF MESO-STRUCTURE CHARACTERISTICS ON MECHANICAL PROPERTY OF STITCHED COMPOSITES

Mechanical Properties and Damage Failure of Carbon Fiber Reinforced Polymer Composite Sandwich Structure with Square Honeycomb Core Using the Interlocking Method

Mechanical Behaviors of Carbon Fiber Composite Sandwich Columns with Three Dimensional Honeycomb Cores under In-Plane Compression

Mechanical Behavior of Carbon Fiber Reinforced Polymer Composite Sandwich Panels with 2-D Lattice Truss Cores

An Experiment Study on the Failure Mechanisms of Woven Textile Sandwich Panels under Quasi-Static Loading

Experimental Investigation of 3d Sandwich Structure with Core Reinforced by Composite Columns

Experimental Investigation of Interlaminar Fracture Toughness of CFRP Composites with Different Stitching Patterns