Abstract:The basic types of damage in composites are matrix cracking, fiber breakage, debonding of interface and delamination. Macroscopically, such damage will lead to stiffness reduction. Macroscopic continuum damage mechanics (CDM) has shown that stiffness loss based on such damage can be quantatively related to strains that are easily measured in composites. In this paper an investigation has been conducted to analyse the inter-relationship between stiffness loss and applied strain due to transverse cracking in crossply laminated composites under uniaxial tensile loading. A modified shear-lag model is proposed that assumes a thin interlaminar adhesive layer between two neighbouring layers transferring not only interlaminar shear stress but also interlaminar normal stress. The stress distribution, taking into account the thermal residual stresses around the transverse cracks, is solved by this model which rigorously satisfies the stress equilibrium equations, boundary conditions and the traction continuity at interfaces between layers. The stiffness reduction is determined as a function of crack density and is in good agreement with the experimental data. The assumptions of cracking at fixed load and at fixed strain are utilized to predict the progression of transverse cracking and stiffness loss as functions of applied stress or applied strain.

On Inter-Relationships of Elastic Moduli and Strains in Crossply Laminated Composites