Abstract:A facile and versatile approach for the synthesis of ultrahigh molecular weight poly(methyl methacrylate) (PMMA) at mild conditions was developed. Certain organic halides combined with a catalytical amount of palladium nanoparticles (Pd NPs) were found to be very effective in initiating polymerizations of methyl methacrylate (MMA), methyl acrylate, vinyl acetate and other vinyl monomers. An ultrahigh molecular weight PMMA with a number-average molecular weight of 4.65 × 106 Da and a weight-average molecular weight of 8.08 × 106 Da was synthesized at 70 °C using 2-bromoisobutyric acid ethyl ester (EBiB) as an initiator in the presence of catalytical amount (10.1 ppm) of Pd NPs. A kinetic investigation found that the orders of polymerization with respect to EBiB, Pd NP and MMA were 0.23, 0.50, and 0.58, respectively. Proton nuclear magnetic resonance (1H NMR) combined with matrix-assisted laser desorption ionization time of flight mass spectroscopy (MALDI-TOF) and gel permeation chromatography (GPC) were used to prove that the macromolecular chain had an end-group of EBiB residue. The electron spin resonance (ESR), transmission electron microscope (TEM), and X-ray photoelectron spectroscopy (XPS) results reveal that the reaction of EBiB with Pd NPs caused a bromo atom (Br) transfer from EBiB to Pd NPs and resulted in the generation of EBiB residue radical to initiate the polymerization of MMA and the formation of PdIIBr2 on the surface of Pd nanoparticles.

Polymerization of methyl methacrylate with a homogeneous neodymium catalyst: Nd(naph)3-BuLi

Polymerization of Methyl Methacrylate Catalyzed by Novel Nd Complex with Schiff Base Without of Any Cocatalyst

Styrene polymerization with ternary neodymium-based catalyst system: effects of catalyst preparation procedures

Neutral Pd(II) and Ni(II) Acetylide Catalysts for the Polymerization of Methyl Methacrylate

Anionic Polymerization of Alkyl Methacrylates Initiated by Nbucu(Ncy2)Li

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Polymerization of Methyl Methacrylate with Achiral 4B Group Metallocene Compounds

Facile Synthesis of Ultrahigh Molecular Weight Poly(Methyl Methacrylate) by Organic Halides in the Presence of Palladium Nanoparticles

Bulk and Solution Polymerization of Methyl Methacrylate by Novel Dinuclear Titallocene Catalyst

Isospecific Polymerization Of Methyl-Methacrylate Initiated By Chiral Zirconocenedimethyl/Ph(3)Cb(C6f5)(4) In The Presence Of Lewis-Acid

The Use Of Epsilon-Caprolactone As A Polymerizable Solvent For The Atom Transfer Radical Polymerization Of Mma At Low Temperature

Polymerization of Methyl Methacrylate Using Organocalcium Compounds

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Polymerization of N-phenylmaleimide with rare earth coordination catalysts

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Polymerization Of Methyl Methacrylate With A New Rare-Earth Coordination Catalyst

ANCHORING OF AZO INITIATOR AND GRAFTING OF POLY(METHYL METHACRYLATE) ONTO NANAOMETER SILICA

Neutral Pd(Ii) and Ni(Ii) Acetylide Complexes As Single-Component Initiators for Polymerizations of Butyl Methacrylate and Acrylates

The Use of Organic Catalysts in Reversible-deactivation Radical Polymerization (RDRP) of Methyl Methacrylate with in situ Formed Alkyl Iodide Initiator

Nitroxide-mediated polymerization of methyl methacrylate by 4,4′-dimethoxydiphenyl-based alkoxyamine

Stereospecific Polymerization of Methacrylates with Dimethylsilylene-bridged Zirconocene Catalysts