Research on reaction characteristics and mechanisms of Al-ZnO system powder
Wenzhen Yu,Yimin Gao,Yiran Wang
DOI: https://doi.org/10.1016/j.matchemphys.2023.128359
IF: 4.778
2023-09-03
Materials Chemistry and Physics
Abstract:The inadequate bonding strength between ceramic and steel and microstructure defects caused by heat dissipation make it difficult to enhance the composite's performance. Hence, the utilization of self-exothermic Al-ZnO system powder to increase the melt temperature and synthesize interfacial transition layers has emerged as a novel solution to change bonding interfaces. In this study, the reaction characteristics and mechanism were analyzed, as well as the influence of temperature, reaction atmosphere, weight ratio, and particle size on the Al-ZnO system powder. Additionally, the influence factor for the exothermic characteristic and the moderating method for the powder system were investigated. The main conclusions are that when the powder composition ratio is closer to the equilibrium stoichiometry and the particle size is larger, the self-exothermic reaction heat release decreases, the reaction stability improves, and the intermetallic reaction becomes more apparent. Moreover, no reaction is observed when Al particles beyond 40 μm. The reaction products are significantly influenced by different reaction atmosphere environments, while the reaction point remains less affected. The Al-ZnO system powder exhibits a wide moderating capability, with effective reaction point ranging from 599 °C to 1200 °C. Additionally, the reaction exotherm is adjustable between 200~1720 J/g.
materials science, multidisciplinary