Abstract:Poly (vinyl alcohol)/layered double hydroxide (PVA/LDH) composite films with different LDH contents have been fabricated through casting with an in situ hydrothermal treatment. Wide angle X-ray diffraction WAXD) results show the characteristic (003) diffraction reflection peak of LDH layers and the corresponding peak becomes stronger with the increase of LDH content, and the size of LDH layers can be tuned by the concentration of reactant. Lower reactant concentration leads to small size of LDH particles while higher concentration gives LDH particles with large size. LDH particles are homogeneously dispersed in PVA matrix as evidenced by SEM observations. The tensile strength and the elastic modulus of PVA films are improved by introducing LDH particles. With the LDH content of 1. 0 wt%, the tensile strength and elastic modulus of the corresponding composite films are improved by about 105. 4% and 133. 2%, respectively, compared with those of a neat PVA film. It is believed that most OH groups of PVA undergo interfacial H-bonding with the LDH layers and other PVA chains,which might be account for the improvement of mechanical properties. Interesting thing is that the in situ PVA/LDH composite aqueous solution shows lower viscosity than that of PVA aqueous solution and the viscosity decreases with LDH content, which is in strong contrast to that by traditional simple mixing. LDH layers are considered to shield the entanglement of PVA chains and thus lead to decreasing solution viscosity. Furthermore, the anti-absorbent of water for the composite films are also improved without losing transparency, while the improvement of gas barrier cannot be observed until the loading of LDH reaches to 3. 0 wt%.

Study on lignin/PVA composite film

Lignosulfonate as reinforcement in polyvinyl alcohol film: Mechanical properties and interaction analysis.

High Strength UV-Resistant Composite Film of Fe3+-Coordination Lignin/PVA

Colloidal Lignin Nanoparticles from Acid Hydrotropic Fractionation for Producing Tough, Biodegradable, and UV Blocking PVA Nanocomposite

Construction of multiple crosslinked networks for the preparation of high-performance lignin-containing cellulose nanofiber reinforced polyvinyl alcohol films

Performance of Water Absorption and Retention Material and Chemical Synthesis of Calcium Lignin Sulphonate with Acrylamide and Acrylic Acid

High Performance PVA/lignin Nanocomposite Films with Excellent Water Vapor Barrier and UV-shielding Properties

Improved Hydrophobic, UV Barrier and Antibacterial Properties of Multifunctional PVA Nanocomposite Films Reinforced with Modified Lignin Contained Cellulose Nanofibers

Facile Fabrication of High-Performance Composite Films Comprising Polyvinyl Alcohol as Matrix and Phenolic Tree Extracts

Strong, flexible and UV-shielding composite polyvinyl alcohol films with wood cellulose skeleton and lignin nanoparticles

Preparation and Properties Study of PVA/Bamboo Cellulose Composite Membrane

Studies on Poly (vinyl alcohol)/Layered Double Hydroxide in situ Composite Films

Surface-coated Fly Ash Reinforced Biodegradable Poly(vinyl Alcohol) Composite Films: Part 2-Analysis and Characterization

Preparation and properties of montmorillonoid/polyvinyl alcohol nanocomposite films

Properties of polyvinyl alcohol films reinforced by citric acid modified cellulose nanocrystals and silica aerogels

Rice straw cellulose microfiber reinforcing PVA composite film of ultraviolet blocking through pre-cross-linking

Influence of Ammonium Zirconium Carbonate on Properties of Poly(Vinyl Alcohol)/Xylan Composite Films

Transparent Nanocomposite Films of Lignin Nanospheres and Poly(vinyl alcohol) for UV-Absorbing

High‐strength Biodegradable Poly(vinyl Alcohol)/fly Ash Composite Films

Preparation and Characterization of Lignin-based Membrane Material

Effect of Loblolly Pine (Pinus taeda L.) Hemicellulose Structure on the Properties of Hemicellulose-Polyvinyl Alcohol Composite Film