The preparation of rigid hybrid silicone resins by combining carbon nanomaterial loading nanoparticles
Shengjie Guan,Fan Wu,Qian Wu,Zhichao He,Jing Jiang,Yudong Huang,Li Liu
DOI: https://doi.org/10.1002/pc.26854
IF: 5.2
2022-08-17
Polymer Composites
Abstract:we obtained the well‐dispersed CNTs and graphene loading nano particles (Mo, Ru, Pt) by ultrasonic dispersion and reducing action of ethylene glycol. The new type nano materials would act the reinforcement of silicone resins and catalyst between silicone resins and rigid aromatic compound. The general experimental procedure of the rigid hybrid silicone resins and composites,which was nano particles functionalization, mixing with resin, composite material preparation. A series of carbon nanotubes and graphene loading nanoparticles (Mo, Ru, and Pt) were synthesized by the ethylene glycol reduction, in addition, the nanomaterials went through the silanization process by (3‐aminopropyl)triethoxysilane in order to obtain the perfect consistency and dispersibility. The characterization results were then exhibited by X‐ray photoelectron spectroscopy, Raman spectroscopy, scanning electron microscopy, and transmission electron microscopy tests. Furthermore, the nanomaterials modified silicone resins were obtained by combining methyl phenyl silicone resins, nanocarbon material and HOOBt. The differential scanning calorimetry, sol–gel time and thermogravimetric analysis tests showed the preferable improvement of heat‐resistant quality. Then the silicone resin matrix composites were manufactured by molding process and went through a thermal decomposition process. The ILSS, bending strength and modulus results showed that the hybrid modified silicone resin composites had the leading trend (361.4 MPa, 190.3 MPa, 13.5 GPa, etc.) at all temperature stages. This experimental scheme of carbon nanomaterial loading nanoparticles and hybrid modified silicone resins would have a competitive advantage in exotic material field.
materials science, composites,polymer science