Mechanical Property of Induction Brazing TiAl-based Intermetallics to Steel 35crmo Using AgCuTi Filler Metal

P He,JC Feng,W Xu

DOI: https://doi.org/10.1016/j.msea.2005.11.005

IF: 6.044

2006-01-01

Materials Science and Engineering A

Abstract:TiAl-based intermetallics joined by vacuum induction brazing using Ag–Cu35.2–Ti1.8 filler alloy at 850–970°C for 1–10min was investigated. The optimum brazing parameters are as follows: brazing temperature is 870–880°C, brazing time is 4–6min. The maximum tensile strength of the joint is 320MPa for the specimen induction brazed at for 870°C for 5min, and at this time, the thickness of Al–Cu–Ti intermetallic compound layer is about one third of that of the whole interface. Interfacial microstructure of TiAl/Ag–Cu–Ti/35CrMo joint brazed at 870°C for 5min is instable at 400°C. The instantaneous high temperature strength is 248MPa at 400°C, the fracture location of joint is mainly at Al–Cu–Ti intermetallic compound layer, the fracture pattern of brazed joint deviate from transcrystalline crack at room temperature into intergranular crack.