Abstract:Silica aerogels generally exhibit poor mechanical properties, which seriously restrict their commercial use and makes it necessary to reinforce their structures to obtain materials strong enough to withstand mechanical stresses. The incorporation of polymers into silica aerogels is a promising approach due to the enhancement in mechanical strength afforded and the possibility of imparting the hydrophobicity of the polymers to the resulting aerogels. However, the processes typically employed to prepare polymer-reinforced silica aerogels are complex, arduous and costly, requiring multiple washing and soaking steps for the infiltration of the polymer precursors after gelation and supercritical drying. Additionally, diffusion problems can result in heterogeneity in aerogel monoliths due to the use of various cross-linked polymers and the autoclave-limited dimensions of aerogels. In this study, a facile sol–gel route was developed to fabricate a large (500 cm3) polymer–silica aerogel monolith that was stable under atmospheric conditions and suitable for machining. The synthesis of the polymer–silica aerogels began with a facile one-pot reaction involving resorcinol (R), formaldehyde (F), methyltrimethoxysilane (MTMS), and N-(β-aminoethyl)-γ-aminopropyl-trimethoxysilane (AEAPTES), followed by an ambient-pressure drying process. The resulting aerogels were characterised by nitrogen adsorption–desorption, scanning electron microscopy (SEM), contact angle, and thermal conductivity measurements, and the aerogel mechanical properties were evaluated by a unidirectional compression test. The Young's modulus of compression of the aerogels was observed to increase from 3.95 to 34.88 MPa with an increase in the density of the aerogels from 0.14 to 0.26 g cm−3. Simultaneously, the aerogels were observed to be superhydrophobic, with a contact angle as high as 168°, and exhibited low thermal conductivity (0.038 W m−1 K−1) and good absorption for organic liquids, which are critical characteristics for the practical application of aerogels, especially in energy-saving and oil-/chemical-cleanup practices.

Sol-Gel Method Fabricate SiO2 Aerogel Used in Function of Wood Modification

Preparation of SiO2 aerogels with sol-gel method and the study of their properties

Preparation and characterization of monolithic TiO2/SiO2 aerogels obtained by non-supercritical drying method

Preparation of Silica Aerogels Via Non-supercritical Drying and Their Formation Process

Preparation and Characterization of Composite SiO2 Aerogel by a Novel One-step Modified Process

Preparation of Fe2O3-SiO2 Aerogels by Supercritical Drying Technique

Directional-Freezing-Assisted In Situ Sol–Gel Strategy to Synthesize High-Strength, Fire-Resistant, and Hydrophobic Wood-Based Composite Aerogels for Thermal Insulation

Preparation of Silica Aerogels by Non-Supercritical Drying

CHARACTERIZATION OF SiO2 AEROGELS/FIBER COMPOSITES PREPARED BY THE SOL-GEL METHODS

Methods of Modification of SiO2 Aerogels

Ambient-pressure drying synthesis of large resorcinol–formaldehyde-reinforced silica aerogels with enhanced mechanical strength and superhydrophobicity

Preparation and Thermo-Mechanical Properties of Modified Gelatin Reinforced SiO2 Aerogels

Microstructure and Properties of the Si3N4/silica Aerogel Composites Fabricated by the Sol–gel Method Via Ambient Pressure Drying

Highly Compressible, Anisotropic Aerogel with Aligned Cellulose Nanofibers

Synthesis and Characterization of Silica Aerogel and Its Composite Materials

Synthesis and Structure of Carbon/Silica Hybrid Aerogels

Highly elastic and fatigue resistant wood/silica composite aerogel operated at extremely low temperature

Robust Silica–Agarose Composite Aerogels with Interpenetrating Network Structure by in Situ Sol–Gel Process

Effect of SiO2 Sol Proportion on the Mechanical Properties of Aerogel Insulation Composites

Study on Silica Aerogel Modified by Trimethylchlorosilane

Preparation, mechanical, acoustic and thermal properties of silica composite aerogel using wet-laid glass fiber felt as scaffold