Abstract:A composite of silica hydrogel with ceramic fibers (15% in mass fraction) was synthesized with sodium silicate as a precursor and deionized water as a solvent by a sol?gel method, and the composite was subsequently modified with a solution of ethanol/trimethylchlorosilane/n-hexane via one-step solvent exchange and surface modification, thus obtaining the crack-free and high hydrophobic composite aerogel monoliths. The composite aerogel has a low density of 0.216 g/cm3 and a superior formability. The ceramic fibers can be dispensed into the sample and combined with the silica aerogel network. There is a spongy meshwork structure on the surface of the aerogel. The aerogel samples were characterized by microstructure, analysis, specific surface area measurement, thermogravimetric analysis, hydrophobicity, elastic modulus and thermal conductivities test, respectively. The results show that the specific surface area of the composite aerogel is 743 m2/g, the contact angle with water is 146°, and the elastic modulus is 5.1 MPa. After a thermal process in the temperature range from room temperature to 400 ℃, the hydrophobicity remains unchanged (about 138°), and the thermal conductivity of composite aerogel monoliths changes from 0.026 3 W/(m·K) to 0.051 2 W/(m·K). In addition, the mechanisms of solvent exchange and surface modification were also discussed.

Methods of Modification of SiO2 Aerogels

Preparation of SiO2 aerogels with sol-gel method and the study of their properties

SiO2 Aerogels Prepared with Ambient Pressure Drying and Its Properties

The Microwave-Assisted Preparation and Properties of Sio2 Aerogels by Fractional Modification

Preparation and characterization of monolithic TiO2/SiO2 aerogels obtained by non-supercritical drying method

Surface modification and properties of SiO2 nano porous aerogels

Surface Modification and Adsorption Properties of SiO2 Nanoporous Aerogels

Preparation and Hydrophobic Modification of SiO_2 Aerogels

Atmospheric Drying Process and Properties of SiO2 Aerogels

Preparation and Hydrophobic Modification of SiO; Aerogels

Study on Silica Aerogel Modified by Trimethylchlorosilane

Preparation and Surface Modification Mechanism of Silica Aerogels Via Ambient Pressure Drying

Hydrophobic SiO2 Aerogels Prepared with Polyethoxydisiloxanes

Chemical Modification and Characterization of Nanoporous Super Thermal Insulation Material——Silica Aerogel

Hydrophobie SiO2 aerogels prepared with polyethoxydisiloxanes

Preparation and Characterization of Composite SiO2 Aerogel by a Novel One-step Modified Process

Synthesis Of Nanoporous Sio2 Areogel Microsphere Materials

Preparation and Properties of Al2O3-SiO2 Aerogels

Preparation and Thermo-Mechanical Properties of Modified Gelatin Reinforced SiO2 Aerogels

EFFECT OF PREPARATION CONDITIONS ON STRUCTURE AND PROPERTIES OF HYDROPHOBIC SiO2 AEROGEL