High-performance LaFe11.6Si1.4H /Al composites for magnetic refrigeration: A good combination of magnetocaloric effect, mechanical properties, and thermal conductivity
Mingxiao Zhang,Yanyan Shao,Chunhui Li,Yifei Zhang,Wen Sun,Zhiyang Wei,Konstantin P. Skokov,Jian Liu,Aru Yan
DOI: https://doi.org/10.1016/j.jallcom.2023.171123
IF: 6.2
2023-06-01
Journal of Alloys and Compounds
Abstract:Bulk LaFe11.6Si1.4H y /Al composites with the saturated hydrogen content were prepared by hot pressing and subsequent hydrogenation. Al particles were dramatically deformed when pressed at 773 K, and a reaction of La(Fe,Si)13 and Al phases took place at 873 K. The reinforced skeleton structure consisting of malleable Al phases in the composites allows brittle La(Fe,Si)13H y particles to be well bonded after hydrogen absorption. As a result, these LaFe11.6Si1.4H y /Al hydrides show a good comprehensive performance for magnetic refrigeration, i.e., large entropy changes of 9.8–12.5 J/kg K under 2 T, large adiabatic temperature changes of 3.36–3.97 K under 1.9 T, high thermal conductivity of 11.4–45.6 W/m K, and high bending strength of 16.8–48.2 MPa. Particularly, the 20 wt% Al composite possesses a compressive strength of 122 MPa and plastic deformation of 4.6 %.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering