Effect of low-temperature transverse field annealing on domain structure and soft magnetism of Fe53-xCo7Ni20Si4B16Crx (x = 0, 1, 2, 3) amorphous alloys
Peixin Fu,Hongze Ou,Junlei Shi,Xiaoling Fu,Yuanzheng Yang
DOI: https://doi.org/10.1007/s10854-024-13560-x
2024-10-04
Journal of Materials Science Materials in Electronics
Abstract:In this paper, Fe 53-x Co 7 Ni 20 Si 4 B 16 Cr x ( x = 0, 1, 2, 3) amorphous ribbons were prepared using a rapid cooling method. The effects of Cr doping on the thermal stability, soft magnetic properties and magnetic domain structure of the amorphous ribbons in the melt-spun state and after low-temperature transverse magnetic field annealing (LTA) were investigated. Results indicate that the addition of Cr enhances the thermal stability of the amorphous alloy. After LTA at 100 °C below the initial crystallization temperature, all strips retained their amorphous structure. The coercivity ( H c ) of the Cr-free and 3% Cr-containing ribbons decreased from 15.1 to 6.3 A/m and from 13.0 to 1.7 A/m, respectively. The effective permeability ( μ e ) remained stable across the frequency range of 100 kHz to 1000 kHz. The μ e of the ribbons with 3at% Cr increased from 2.14 × 10 3 (at 100 kHz)—2.07 × 10 3 (at 1000 kHz) to 2.78 × 10 3 (at 100 kHz)—2.65 × 10 3 (at 1000 kHz). The attenuation rate in the frequency range of 100 kHz to 1000 kHz is 4.85%. Finally, the addition of Cr element can play a role in refining the magnetic domains. After LTA, the magnetic domains of Cr-free ribbons were still broad irregular domain areas, and obvious domain wall movement processes were observed in the magnetization process. The magnetic domain structure of the Cr ribbons containing 3 at% Cr was characterized by alternating bright and dark striped domains. The distribution of magnetic domains was more uniform and regular, and the rotation of magnetic domains was mainly dominated in the magnetization process.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied