Abstract:A novel hyperbranced azo polymer with terminal diazonium groups was synthesized by step-growth polymerization of 4,4'-diamino diphenyl sulphone's diazonium salts (A(2)) and benzene-1,3,5-triearboxylic acid tri2-(N-ethylanilino) ethyl ester (B-3) through azo-coupling reaction. 4, 4'-diamino diphenyl sulphone (0.248 g, I mmol) was dissolved in a hot homogeneous mixture of glacial acetic acid (7.5 mL) and sulfuric acid ( I mL). Aqueous solution of sodium nitrite (0.166 g, 2.4 mmol) in 0.5 mL water was added dropwise into the solution at 0 degrees C and kept at this temperature for 5 min. The diazonium salt solution of 4,4'-diamino diphenyl sulphone was then added dropwise into the solution of benzene-1, 3, 5-tricarboxylic acid tri-2-( N-ethylanilino) ethyl ester (0.326 g, 0.5 mmol) in 50 mL DMF at 0 degrees C. After the reaction was carried out at 0 degrees C for 8 h, the solution containing the diazonium-hyperbranched azo polymer was directly used as the polyeation solution. The purchased sodium polystrene sulfonate (PSSA) was used as polyanion. Then the multilayer films were prepared by an electrostatic layer-by-layer deposition method. The self-assembly processes and morphologies of surfaces were characterized by UV-Vis spectra, ellipsometer and AFM. A linear increase of absorbance and thickness was observed as the number of the bilayers increased. Dichroism was optically induced in the self-assembly film under the irradiation of a polarized Ar+ laser beam at 488 nm. After 15 min irradiation of the laser beam at an intensity of 80 mW/cm(2) the orientation order parameter of the multilayer film obtained was about 0.02. With interfering illumination of Ar+ laser beams for 30 min, significant surface relief gratings formed on the self-assembly multilayer film were observed. The spatial period and height of the obtained SRGs were about 744 nm and 20 nm. respectively.

Self-Assembly and Optical Properties of Poly(Acrylic Acid)-Based Azo Polyelectrolyte

Synthesis, self-assembly and photoinduced surface-relief gratings of a polyacrylate-based Azo polyelectrolyte

Synthesis, Photoresponsive Behavior, and Self-Assembly of Poly(Acrylic Acid)-Based Azo Polyelectrolytes

SPIN SELF-ASSEMBLY OF A POLYACRYLATE-BASED AZO POLYELECTROLYTE AND MULTILAYER PHOTORESPONSIVE BEHAVIOR

Self-assembly of a polyacrylate-based azo polyelectrolyte and its photoinduced surface relief gratings

Layer-By-Layer Self-Assembly and Photo-Induced Dichroism of A Novel Side-Chain Azo Polyelectrolyte

Synthesis and Characterization of a Novel Azo Polyelectrolyte with Surface Relief Structures

Azo Chromophore-Functionalized Polyelectrolytes. 2. Acentric Self-Assembly Through a Layer-by-Layer Deposition Process

FABRICATION OF PHOTORESPONSIVE ELECTROSTATIC MULTILAYERS CONTAINING DIAZONIUM-HYPERBRANCHED AZO POLYMER

SYNTHESIS,LAYER-BY-LAYER SELF-ASSEMBLY AND OPTICALLY INDUCED BIREFRINGENCE OF A NOVEL BRANCHED SIDE-CHAIN AZO POLYELECTROLYTE

Self‐assembled Second Order Nonlinear Optical Multilayer Azo Polymer

Azo Chromophore-Functionalized Polyelectrolytes. 1. Synthesis, Characterization, and Photoprocessing

SYNTHESIS OF A MAIN-CHAIN PHOTO-RESPONSIVE AZO POLYMER THROUGH AZO-COUPLING REACTION

Study on Photodynamic and Photoresponsive Azo Polyelectrolytes

PHOTOINDUCED SELF-STRUCTURED SURFACE PATTERNS ON FILMS OF EPOXY-BASED POLYMERS CONTAINING TRIFLUOROMETHYLSUBSTITUTED AZO CHROMOPHORES

Synthesis and Properties of A Novel Side-Chain Azo Polyelectrolyte

Sequentially adsorbed electrostatic multilayers of branched side-chain polyelectrolytes bearing donor-acceptor type azo chromophores

Azobenzene Functionalized Poly(diphenylacetylene): Polymer Synthesis and Tunable Fluorescent Emission

Photo-Induced Dichroism and Surface Relief Gratings of Two Novel Branched Side-Chain Azo Polyelectrolytes

Poly(acrylic Acid)-Bearing Photoreactive Azido Groups for Stabilizing Multilayer Films.

Synthesis and Photoresponsive Behaviors of Well-Defined Azobenzene-Containing Polymers Via Raft Polymerization