Abstract:An A_2+B_3 method of preparing hyperbranched azo polymers by azo-coupling reactions was described.The hyperbranched precursor with diazonium salt groups on the periphery was prepared by step-growth polymerization of A_2(diazonium salts of 4,4′-diamino diphenyl sulphone)/B_3(benzene-1,3,5-tricarboxylic acid tri-2-(N-ethylanilino)ethyl ester)monomers through azo-coupling reaction.Benzene-1,3,5-tricarboxylic acid tri-2-(N-ethylanilino)ethyl ester was prepared by Schotten-Baumann reactions between 1,3,5-benzenetricarbonyl chloride and N-ethyl-N-hydroxyethyl-aniline.Then the hyperbranched precursor with diazonium salt groups on the periphery was further reacted with N,N-diethyl aniline by azo-coupling reaction to obtain the final hyperbranched azo polymer.The azo polymer was characterized by the spectroscopic methods and thermal analysis.The phase transition behavior of the hyperbranched azo polymer was studied by using the differential scanning calorimetry (DSC).The hyperbranched polymer showed a second-order phase transition of typical amorphous substances.The T_g of the hyperbranched azo polymer was about 161℃.As containing the donor-acceptor type azo chromophores,the polymer showed typical spectral characteristics of the pseudo-stilbene type azo chromophores.The λ_ max value of the hyperbranched azo polymer,corresponding to the π-π transition,was about 465 nm.Spin-coated thin films of the hyperbranched azo polymer were used to carry out the SGR inscription experiments.Two p-polarized Ar~+ laser beams (488 nm) with an intensity 80 mW/cm~2 were used to produce the interference pattern on the polymer film.After irradiated for 1000 s at room temperature,the surface modulation depth was about 100 nm,and the grating spacing was about 730 nm.The modulation depth depended on the irradiation energy,and the spatial period depended on both the angle between the two interfering beams and the wavelength of the writing beams.Complex patterns could be inscribed when two gratings were recorded orthogonally to each other at the same location.

SYNTHESIS,LAYER-BY-LAYER SELF-ASSEMBLY AND OPTICALLY INDUCED BIREFRINGENCE OF A NOVEL BRANCHED SIDE-CHAIN AZO POLYELECTROLYTE

Layer-By-Layer Self-Assembly and Photo-Induced Dichroism of A Novel Side-Chain Azo Polyelectrolyte

Sequentially adsorbed electrostatic multilayers of branched side-chain polyelectrolytes bearing donor-acceptor type azo chromophores

Photo-Induced Dichroism and Surface Relief Gratings of Two Novel Branched Side-Chain Azo Polyelectrolytes

Synthesis, Photoresponsive Behavior, and Self-Assembly of Poly(Acrylic Acid)-Based Azo Polyelectrolytes

Self-Assembly and Optical Properties of Poly(Acrylic Acid)-Based Azo Polyelectrolyte

A Novel Polyelectrolyte with Branched Azo Side Chains: Synthesis, Characterization and Self-Assembled Nanostructures

FABRICATION OF PHOTORESPONSIVE ELECTROSTATIC MULTILAYERS CONTAINING DIAZONIUM-HYPERBRANCHED AZO POLYMER

SYNTHESIS OF A MAIN-CHAIN PHOTO-RESPONSIVE AZO POLYMER THROUGH AZO-COUPLING REACTION

Synthesis, self-assembly and photoinduced surface-relief gratings of a polyacrylate-based Azo polyelectrolyte

Azobenzene Functionalized Poly(diphenylacetylene): Polymer Synthesis and Tunable Fluorescent Emission

Azo Chromophore-Functionalized Polyelectrolytes. 1. Synthesis, Characterization, and Photoprocessing

Azo Chromophore-Functionalized Polyelectrolytes. 2. Acentric Self-Assembly Through a Layer-by-Layer Deposition Process

SPIN SELF-ASSEMBLY OF A POLYACRYLATE-BASED AZO POLYELECTROLYTE AND MULTILAYER PHOTORESPONSIVE BEHAVIOR

HYPERBRANCHED AZO POLYMERS SYNTHESIZED BY AZO-COUPLING REACTION OF A_2/B_3 MONOMERS

Synthesis and Characterization of Polyelectrolyte Containing Azo Chromophore in the Side-chain

Surface-Relief-Grating Formation Behavior of Two Hyperbranched Azo Polymers

Synthesis and Photoresponsive Behaviors of Well-Defined Azobenzene-Containing Polymers Via Raft Polymerization

Synthesis and characterization of a novel photoprocessible hyperbranched azo polymer

Synthesis and Properties of A Novel Side-Chain Azo Polyelectrolyte

Light and Temperature as Dual Stimuli Lead to Self-Assembly of Hyperbranched Azobenzene-Terminated Poly(N-isopropylacrylamide)