ELECTROSTATIC LAYER-BY-LAYER SELF-ASSEMBLY ON COLLOIDAL SPHERES AND CAPSULES COMPOSED OF AZO POLYELECTROLYTES
Liu Bin,Li Xinyang,He Yaning,Wang Xiaogong
DOI: https://doi.org/10.3724/sp.j.1105.2008.00148
2008-01-01
Acta Polymerica Sinica
Abstract:In recent years, core-shell micro-particles and hollow capsules have aroused great research interests as new useful microstructures for many potential applications. In this work, core-shell spheres and hollow capsules containing azo polyelectrolytes were prepared by electrostatic layer-by-layer self-assembly and core- dissolution after the multiplayer deposition. In the electrostatic layer-by-layer self-assembling process, a side-chain azo, polyelectrolytes (PEAPE) as polyanion was alternately adsorbed onto surfaces of polystyrene (PS) colloidal spheres together with a polycation of poly ( diallyldimethylammonium chloride) ( PDAC). PEAPE is a random copolymer composed of acrylic and azobenzene-containing acrylate units. PEAPE samples with degree of functionalization (DF) of 9. 3 % and 41.4 % were used. Solutions of the polyelectrolytes ( PEAP E and PDAC) in water and an aqueous medium of 0. 1 mol/L NaCl were alternately added into the diluted suspension of PS latex for electrostatic layer-by-layer adsorption. After 15 min, PS spheres were separated and washed by high-speed centrifuge ( ultracentrifuge, Hitachi CR 22G). Then the sediment was dispersed in Milli-Q water again for further experiment. The experiment steps were repeated several times until the required layer number was reached. The resulted core-shell particles were characterized by transmission electron microscopy (TEM, JEM-1200EX) and dynamic light scattering (DLS, Malvern Zetasizer 3000 HS). The layer-by-layer adsorption of PEAPE and PDAC was evidenced by the diameter increase from the TEM images and DLS measurements. The oscillation of Zete-potenctial after each adsorption step, which indicates the over charge compensation, also confirmed the successive self-assembly of azo polyelectrolytes. Changing the ionic strength of PDAC solution, (in water or in aqueous medium of 0. 1 mol/L NaCl could obviously shift the Zete-potenctial of the colloids, but had little influence on the diameter increasing of the colloidal spheres. The photoisomerization of the azobenzenes was studied by UV-Vis spectroscopy. These azobenzene- containing core-shell particles show typical photochromic effect upon UV light irradiation. After adsorbed to colloidal surfaces, the H-aggregation of azobenzene groups decreased in certain degree and resulted in red shifts in UV-Vis spectrum. As a consequence, the azobenzene chromophores exhibited quickly photo-response behavior upon UV irradiation. To obtain hollow capsules with stable shells, a photosensitive cinnamate- containing polyelectrolyte ( PAAEH, DF = 27 %), synthesized in authors' lab, was applied to induce covalent crosslinking in the shells of colloidal spheres. In the process, PAAEH was adsorbed onto the core-shell particles of PS/ ( PDAC/PEAPE), through electrostatic self-assembly together with PDAC. In the process, PAAEH was dissolved in Milli-Q water with a concentration of I mg/ mL and used as polyanions. After two or three layers of PDAC/PAAEH adsorbed, the core-shell colloidal spheres were exposed to UV light ( 18 mW/cm(2)) for 30 min. The photosensitive shells were cross-linked upon UV-light radiation. Then PS core of colloidal spheres was removed by dissolving with tetrahydrofuran/ H2O ( V: V = I : I). Finally, hollow capsules containing azo chromophores were obtained. Due to their photoresponsive composition, the core-shell particles and hollow capsules may have potential applications in areas such as bio-medicine and photoelectronics.