Abstract:A novel hyperbranced azo polymer with terminal diazonium groups was synthesized by step-growth polymerization of 4,4'-diamino diphenyl sulphone's diazonium salts (A(2)) and benzene-1,3,5-triearboxylic acid tri2-(N-ethylanilino) ethyl ester (B-3) through azo-coupling reaction. 4, 4'-diamino diphenyl sulphone (0.248 g, I mmol) was dissolved in a hot homogeneous mixture of glacial acetic acid (7.5 mL) and sulfuric acid ( I mL). Aqueous solution of sodium nitrite (0.166 g, 2.4 mmol) in 0.5 mL water was added dropwise into the solution at 0 degrees C and kept at this temperature for 5 min. The diazonium salt solution of 4,4'-diamino diphenyl sulphone was then added dropwise into the solution of benzene-1, 3, 5-tricarboxylic acid tri-2-( N-ethylanilino) ethyl ester (0.326 g, 0.5 mmol) in 50 mL DMF at 0 degrees C. After the reaction was carried out at 0 degrees C for 8 h, the solution containing the diazonium-hyperbranched azo polymer was directly used as the polyeation solution. The purchased sodium polystrene sulfonate (PSSA) was used as polyanion. Then the multilayer films were prepared by an electrostatic layer-by-layer deposition method. The self-assembly processes and morphologies of surfaces were characterized by UV-Vis spectra, ellipsometer and AFM. A linear increase of absorbance and thickness was observed as the number of the bilayers increased. Dichroism was optically induced in the self-assembly film under the irradiation of a polarized Ar+ laser beam at 488 nm. After 15 min irradiation of the laser beam at an intensity of 80 mW/cm(2) the orientation order parameter of the multilayer film obtained was about 0.02. With interfering illumination of Ar+ laser beams for 30 min, significant surface relief gratings formed on the self-assembly multilayer film were observed. The spatial period and height of the obtained SRGs were about 744 nm and 20 nm. respectively.

Self‐assembled Second Order Nonlinear Optical Multilayer Azo Polymer

Azo Chromophore-Functionalized Polyelectrolytes. 2. Acentric Self-Assembly Through a Layer-by-Layer Deposition Process

Epoxy-Based Nonlinear Optical Polymers from Post Azo Coupling Reaction

Synthesis and application of a stable nonlinear optical polymer

Self-Assembly and Optical Properties of Poly(Acrylic Acid)-Based Azo Polyelectrolyte

Synthesis of A Photo-Crosslinked Stable Nonlinear Optical Polymer and Application to External Electro-Optic Measurement

Preparation of a Novel Self-Assembling Nonlinear Optical (NLO) Polymer Film

Preparation and Second-Order Optical Nonlinearity of Inorganic–organic Hybrid Films

SPIN SELF-ASSEMBLY OF A POLYACRYLATE-BASED AZO POLYELECTROLYTE AND MULTILAYER PHOTORESPONSIVE BEHAVIOR

Layer-by-layer deposited organic/inorganic hybrid multilayer films containing noncentrosymmetrically orientated azobenzene chromophores.

NONLINEAR OPTICAL AZO POLYIMIDE FROM POST-POLYMERIZATION AZO-COUPLING REACTION

Synthesis and Characterization of Sterically Stabilized Second-Order Nonlinear Optical Chromophores

Synthesis and Properties of Nonlinear Optical Side Chain Liquid Crystalline Polymalonate

Poly(P-Diethynylbenzene) Derivatives for Nonlinear Optics

Optical Nonlinearity and Photoinduced Anisotropy of an Azobenzene‐containing Ionic Liquid Crystalline Polymer

Heteroaromatic Chromophore Functionalized Epoxy-Based Nonlinear Optical Polymers

Inorganic-Organic Hybrid Nonlinear Optical Films Containing Bulky Alkoxysilane Dyes

Design and synthesis of a thermally stable second-order nonlinear optical chromophore and its poled polymers

Layer-By-Layer Self-Assembly and Photo-Induced Dichroism of A Novel Side-Chain Azo Polyelectrolyte

Polymers With Enhanced Second-Order Optical Nonlinearities

FABRICATION OF PHOTORESPONSIVE ELECTROSTATIC MULTILAYERS CONTAINING DIAZONIUM-HYPERBRANCHED AZO POLYMER