Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Synthesis and luminescence properties of YVO4:Dy3+ nanorods

Synthesis and Enhanced Luminescence of Uniform and Well-Dispersed Quasispherical Yvo4:Ln(3+) (ln = Eu, Dy) Nanoparticles by A Solvothermal Method

Uniform YVO4:Ln3+ (Ln = Eu, Dy, and Sm) nanocrystals: Solvothermal synthesis and luminescence properties

In situ hydrothermal synthesis of YVO4 nanorods and microtubes using (NH4)0.5V2O5 nanowires templates

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles: Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles

Controlled Synthesis of Ln(3+) (ln = Tb, Eu, Dy) and V5+ Ion-Doped Ypo4 Nano-/Microstructures with Tunable Luminescent Colors

Synthesis and Photoluminescent Properties of Nanoerythrocyte-Shaped Ytterbium Orthovanadate and Erbium Ion-Doped Ytterbium Orthovanadate Powders

Morphological Control and Luminescent Properties of Yvo4 : Eu Nanocrystals

Growth and research on photoluminescence and radiation-induced luminescence properties of Dy-doped YVO 4 single crystals

Hydrothermal Synthesis of Nd3+-doped Orthoborate Nanoparticles That Emit in the Near-Infrared

Na(Y1.5 Na0.5)F6 single-crystal nanorods as multicolor luminescent materials.

Synthesis Process and Luminescence Properties of Ln3+ Doped NaY(WO4)2 Nanoparticles

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Na(Y<sub>1.5</sub>Na<sub>0.5</sub>)F<sub>6</sub>Single-Crystal Nanorods as Multicolor Luminescent Materials

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Gastrointestinal complications after radiation therapy in patients with hepatocellular carcinoma.

Controllable Synthesis and Size-Dependent Luminescent Properties of Yvo4:Eu3+ Nanospheres and Microspheres

Preparation and Luminescent Properties of 1d Lu2o2s:Eu3+ Nanorods

Facile Synthesis and Luminescence Properties of Octahedral Yvo4:Eu3+ Microcrystals