Mechanical Properties of the Nano-Caco3 and GB Co-Reinforced CF/PA6 Composites
Yue Qin,Hongfeng Yin,Yun Tang,Jinshi Bian,Yan Li,Hudie Yuan
DOI: https://doi.org/10.1088/2053-1591/ab33a8
IF: 2.025
2019-01-01
Materials Research Express
Abstract:In this work, ternary nano-CaCO3/carbon fiber (CF)/PA6 composites and quaternary glass beads (GB)/nano-CaCO3/carbon fiber/PA6 were fabricated by melt-extrusion and laminating method. The effect of nano-CaCO3 content on the mechanical properties of nano-CaCO3/CF/PA6 composites was evaluated. It was found that the addition of nano-CaCO3 at 10 wt% could make a remarkable improvement of 15.1%, 53.2%, 8.5% and 76.0% in flexural strength and modulus, shear and impact strength respectively contrasted to CF/PA6 composites. The mechanical properties of nano-CaCO3 and glass beads co-reinforced carbon fiber/PA6 composites were enhanced obviously. In particular, the flexural strength and modulus, shear and impact strength reached 427.9 MPa, 19.8 GPa, 51.6 MPa and 87.4 kJ m−2 respectively when the glass beads content of 8 wt% and nano-CaCO3 content of 10 wt%, which were increased by 40.8%, 74.7%, 18.0% and 143.4% respectively compared with CF/PA6 composites, the strengthening and toughening effects of GB/nano-CaCO3/CF/PA6 composites were realized by the synergistic action of multi-scale reinforcements.