Mechanical Properties and Morphology of Poly(L-Lactic Acid)/Nano-Caco3 Composites

J. Z. Liang,D. R. Duan,C. Y. Tang,C. P. Tsui,D. Z. Chen,S. D. Zhang

DOI: https://doi.org/10.1007/s10924-014-0661-z

IF: 4.705

2014-01-01

Journal of Polymers and the Environment

Abstract:The tensile and impact properties of poly(l-lactic acid) composites filled with nanometer calcium carbonate (nano-CaCO3) were measured at room temperature. The results showed that the tensile elastic modulus increased roughly linearly while the tensile yield strength, tensile fracture strength and tensile elongation at break (δ b ) decreased nonlinearly with increasing the nano-CaCO3 weight fraction (W f ); when W f was constant, the δ b increased with increasing tensile rates. Both the V-notched Izod impact strength and V-notched Charpy impact strength showed the non-linear increase with increasing W f . The impact fracture surface was observed by means of a scanning electronic microscope to understand the toughening mechanisms.