Unlubricated Sliding Wear Mechanism of Fine Ceramics Al2O3 and ZrO2 Against High Chromium Cast Iron

L ZHOU,YM GAO,JE ZHOU,QD ZHOU
DOI: https://doi.org/10.1016/0043-1648(94)90195-3
IF: 4.695
1994-01-01
Wear
Abstract:The unlubricated sliding wear behaviour of hot-pressed ceramics Al2O3 and ZrO2 against high chromium cast iron with various matrices was studied. The wear micro-mechanism of Al2O3 and ZrO2 was discussed. The results showed the following: (1) The wear of Al2O3 depends on the formation of transfer film coming from the cast iron; the austenite in the matrix of the cast iron promotes the formation of transfer film which can reduce simultaneously the wear of both Al2O3 and cast iron; (2) the direct factor controlling the formation of transfer film on ceramics is the adhesive energy; (3) the wear couple Al2O3/austenite cast iron is a promising combination, because it possesses minimum wear of both sides; (4) the wear of ZrO2 depends on transfer film and phase transformation; (5) the EDAX analysis can be used to determine roughly the relative thickness of the transfer film; (6) the hardness of martensitic cast irons does not affect the wear of ceramics.
What problem does this paper attempt to address?