Abstract:Porous magnesium hydroxide nanoplates were prepared directly from commercial bulk magnesium oxide crystals by a simple hydrothermal treatment. These thin plates would aggregate into large spherical particles. The platelike morphology was retained after calcination, and porous magnesium oxide nanoplates were obtained. These plates have a wormhole-like porous structure with high surface area. The obtained materials exhibit bimodal pore size distributions in the mesoporous domain. The aggregation of the nanoplates gives rise to large mesopores with a size of about 36 rim. In addition, each plate has small wormhole mesopores with a size of about 3.7 nm. The growth of magnesium hydroxide nanoplates occurred through a dissolution-recrystallization process. X-ray diffraction and electron diffraction, transmission electron microscopy, scanning electron microscopy, and nitrogen sorption have been employed to characterize these nanoplates. Such porous nanoplates with high surface area and high crystallinity have many promising applications. Moreover, bismuth oxide nanoplates were also produced following a similar method. The formation mechanism of such mesostructures without the use of a template is also discussed.

Fabrication and Characterization of One Dimention Magnesium Hydroxide Nanomaterials

Effect of Organic Substance on the Microcrystalline Structure of Magnesium Hydroxide

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Synthesis of MgO nanotube bundles

Synthesis And Characterization Of Nanosized Mgfe2o4 Powders By Hydrothermal Method

Composite-hydroxide-assisted hydrothermal synthesis of magnesium silicate nanotube

Morphology Transformation of Nanoscale Magnesium Hydroxide: from Nanosheets to Nanodisks

Synthesis And Characterization Of Porous Magnesium Hydroxide And Oxide Nanoplates

Microwave-assisted synthesis of fibre-like Mg(OH)2 nanoparticles in aqueous solution at room temperature

Structural Characteristics and Flame-Retardant Properties of Nanosized Magnesium Hydroxide

Synthesis And Characterization Of Boehmite Alooh Nanotubes

Hydrothermal formation and characterization of magnesium oxysulfate whiskers

Influence of Solvents on the Hydrothermal Formation of One‐dimensional Magnesium Hydroxide

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Morphology-tunable Synthesis and Characterizations of Mg(OH)2 Films Via a Cathodic Electrochemical Process

Magnesium Nitrate As Additive for Synthesis of Mg(OH)2 Nanoparticles

Synthesis and characterisation of magnesium hydrate microspheres