Coproduction of Belite Q-phase Cement Clinker in a Pulverized Coal Combustion Boiler and Its Hydration Performance
Youzhou JIAO,Zhenglun SHI,Zhongyang LUO,Xiang GAO,Jingsong ZHOU,Shurong WANG,Kefa CEN
DOI: https://doi.org/10.3321/j.issn:0253-2468.2009.07.018
2009-01-01
Abstract:Using high-sulphur Changguang coal as experimental coal and analytically pure CaO and MgO as additives.,cogeneration experiments were carried out on a Quaternary phase(Q-phase) cement clinker with a two-stage polyphase reaction setup.The collected clinker samples were analyzed by X-ray diffraction(XRD),scanning electron microscope(SEM),and energy dispersive spectroscopy(EDS),and the results showed that the main minerals of Q-phase cement clinker were 2CaO·SiO2,Q-phase and 3CaO·3Al2O3·Ca SO4.Measurements of hydration strength,swelling,soundness,setting time and hydration performance of the Q-phase cement clinker were carried out.The results revealed that the compressive strength and bending strength of mortar samples at different ages were close to the national standard of 32.5 grade Portland cement.,When 30 percent Portland cement clinker was added to the Q phase cement clinker,the compressive strength and bending strength of the mortar samples at different ages meet the national standards for 32.5 grade Portland cement,and the swelling property,soundness and setting time of Q phase cement clinker all satisfied the national standards.Apart from 2CaO·SiO2,2CaO·Al2O3·8H2O crystal,3CaO·Al2O3·3CaSO4· 32H2O,xCaO·SiO2·yH2O gel,and Al2O3·3H2O gel appeared in the 3 d hydration sample.As hydration developed,2CaO·Al2O3·8H2O,3CaO·Al2O3·CaSO4·12H2O,3CaO·Al2O3·6H2O gradually enriched in hydration sample.