Abstract:Mordenite and ZSM-5 seeds could grow on the surface of an asymmetric α-Al2O3 support using an identical organic-free aluminosilicate solution under the same hydrothermal conditions. It suggests that the phase of zeolite can be controlled by varying the type of seed. Continuous mordenite and ZSM-5 membranes were prepared by the secondary growth method using corresponding seeds under appropriate conditions. The water content in the secondary growth mixture strongly influenced the growth of zeolite crystals. ZSM-5 seeds grew at a smaller rate and showed a habit of thin hexagonal plate in a concentrated mixture, while the crystals with a habit of rectangular parallelepiped were formed from a diluted secondary growth mixture. ZSM-5 crystals had poor intergrowth in the former case, whereas the crystals were highly intergrown in the latter case. ZSM-5 crystals in either membrane have a random orientation. In contrast to ZSM-5 zeolite, the crystal orientation in the secondary grown mordenite membranes strongly depended on the water content in the secondary growth mixture. The crystals in the mordenite membrane developed in a diluted secondary growth mixture were oriented with the (150) face parallel to the support surface, whereas the crystals in the membrane grown in a concentrated mixture were oriented with the (002) face parallel to the support surface. These results suggest that the crystal orientation in mordenite membranes can be manipulated only by changing the water content in a secondary growth mixture. The formation of the preferred crystal orientation in the secondary grown mordenite membrane is discussed in terms of an “evolutionary selection” process.

A Novel Method for the Growth of ZSM-5 Zeolite Membrane on the Surface of Stainless Steel

The Preparation of ZSM-5 Zeolite@cu/stainless Steel As a Dual Functional Material

Influence of Alkali Treatment on Structure and Catalytic Performance of ZSM-5 Films

Hydrothermal Synthesis of ZSM-5 Coatings Strongly-Adhered on Stainless Steel Supports

Influence of Surface Modification of Metallic Substrate on In-Situ Growth and Adhesion Strength of ZSM-5 Films

In-situ Growth of ZSM-5 Crystals on the Surface of High Temperature Alloy Substrates

EFFECT OF LONG CHAIN CATIONIC SURFACTANT ON ZSM-5 SYNTHESIS AND METHANOL TO OLEFIN REACTION

The control of phase and orientation in zeolite membranes by the secondary growth method

Preparation of Zeolite X Membrane on Porous Stainless Steel Substrate

A Facile Preparation of High Flux NaA Zeolite Membranes by Direct Secondary Growth of Wet Gel Layer

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Ultrasonic-assisted Fabrication of High Flux T-type Zeolite Membranes on Alumina Hollow Fibers

Induction of Zeolite Membrane Formation by Implanting Zeolite Crystals into the Precursor of Ceramic Supports

Synthesis of Corrosion-Resistant MFI-type Zeolite Coatings by Solid-Conversion Secondary Growth Without Solvent

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

The Factors in the Secondary Growth Process Fabricating ZSM-5 Zeolite Membrane

SYNTHESIS AND CHARACTERIZATION OF A-TYPE ZEOLITE MEMBRANES ON ALUMINA PARTICLES SURFACE

Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting–rubbing seeding method: Role of wetting agent

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Effects of porogen EDTA on morphology of porous silica support and preparation of MFI zeolite membrane

Fabrication of Zeolite Naa Membranes on Hollow Fibers Using Nano-Sized Seeds Exfoliated from Mesoporous Zeolite Crystals