Abstract:Intergranular fatigue crack nucleation has been reported to occur commonly at high angle grain boundaries (HAGBs) but seldom at low angle GBs (LAGBs) during persistent slip band (PSB)-GB interactions. However, the mechanistic understanding of the role of GB misorientation angles in affecting the GB fatigue cracking remains limited due to the lack of quantitative descriptions. Here a theoretical framework based on the competition between dislocation transmission across GB and GB cracking is established for investigating the GB fatigue crack nucleation. We show that, HAGBs usually provide higher resistances to dislocation transmissions compared with LAGBs, causing a more significant dislocation pile-up and stress concentration, which facilitates the GB crack nucleation. But the quantitative analysis indicates that even at HAGBs with poor plastic compatibility, the critical stress of GB cracking is much larger than the critical transmission stress. This demonstrates the crucial role of GB fatigue damage accumulation, which is associated with PSB extrusion growth, in promoting GB crack nucleation. In this study, the critical stress of dislocation transmission is derived in terms of the energy balance, and the nucleation criterion of GB crack is formulated using the fracture theory, both of which display the dependence on GB misorientation angles and grain sizes. It is found that the GB fatigue cracks preferentially nucleate at HAGBs with poor plastic compatibility and large grain sizes. The competition between dislocation transmission and GB cracking at varying fatigue cycles are also discussed. This theoretical framework offers quantitative analyses for the GB crack nucleation during PSB–GB interactions, clarifies the role of microstructures in affecting the critical cycles of GB cracking, and might offer important guidelines for designing fatigue-resistant metallic materials.

A Microscopic Mechanism of Fatigue Crack Growth Based on the Dislocation-Free Zone

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

Mechanistic Modeling of Fatigue Crack Growth in Asphalt Fine Aggregate Matrix under Torsional Shear Cyclic Load

Fatigue fracture mechanism of amorphous materials from a density-based coarse-grained model

Insights on low cycle fatigue crack formation and propagation mechanism: A microstructurally-sensitive modeling

Towards Fully Automatic Modelling of the Fracture Process in Quasi-Brittle and Ductile Materials: a Unified Crack Growth Criterion

Microstructure-based Intergranular Fatigue Crack Nucleation Model: Dislocation Transmission Versus Grain Boundary Cracking

Accumulated crystal plasticity dissipation energy driven continuum damage two-scale model for fretting fatigue initiation life

Towards a general damage law for interior micro-defect induced fatigue cracking in martensitic steels

Prediction of Low Cycle Fatigue Crack Growth under Mixed-mode Loading Conditions Using Cohesive Zone Models

Rate dependent cohesive zone model for fatigue crack growth

Micro-crack Damage in Strip of Fracture Process Zone

Computational Monitoring of an Initial Fatigue Crack Incubation and Growth in a Smooth Specimen

Cohesive zone modelling of low cycle fatigue cracks in cracked and notched specimens

A New Damage Model for Microcrack-Weakened Brittle Solids

Micromechanical Modeling of Strain-Softening in Microcrack-Weakened Quasi-Brittle Materials

An engineering model of fatigue crack growth under variable amplitude loading

Fatigue Crack Propagation in Heterogeneous Materials under Remote Cyclic Loading

Computational Boundary Layer Approaches for Fatigue Crack Propagation under Mixed‐mode Loading Conditions

A Simple Engineering Approach in the Prediction of the Effect of Stress Ratio on Fatigue Threshold

Computer simulation of fatigue under diametrical compression