Synthesis, growth mechanism and magnetic properties of SiO2-coated Co nanocapsules

X ZHANG,X DONG,H HUANG,B LV,X ZHU,J LEI,S MA,W LIU,Z ZHANG
DOI: https://doi.org/10.1016/j.actamat.2007.02.019
IF: 9.4
2007-01-01
Acta Materialia
Abstract:The growth mechanism and magnetic properties of SiO2-coated Co nanocapsules synthesized by the arc-discharge method were investigated. Most of the as-prepared products were nanocapsules with a core/shell structure consisting of a Co core and a SiO2 shell, while some of them displayed a rod-like configuration. The formation of the SiO2 nanorods was governed by an extended vapor–liquid–solid (VLS) mechanism and Co nanoparticles acted as a catalyst for the growth of the nanorods. The Co/SiO2 nanocapsules were annealed at 300, 400 and 500°C, respectively, for 30min in air, in order to observe their oxidation behavior. The crystalline grains of the Co/SiO2 nanocapsules clearly grew during annealing. After annealing at 500°C, the ferrimagnetic Co3O4 phase appeared. The grain size effect, oxidation behavior and magnetic properties are discussed in detail for the nanocapsules.
What problem does this paper attempt to address?