Abstract:<p>Laser shock peening (LSP) is an emerging technique for effectively forming metal sheets due to its ability to produce higher and deeper compressive residual stress than conventional shot peening. Because it is crucial to understand the evolution of through-thickness residual stress in peening formed components, the purpose of this research was to investigate the correlation between forming deformation and altered residual stress fields in laser-peened Al7055-T7751 plates of distinct thickness. The effect of geometry thickness on global deformation and through-thickness residual stress was investigated experimentally. First, the global deformation and surface residual stress were measured and compared quantitatively. Additionally, the through-thickness of the residual stress was determined using the slitting technique, and the measurements were validated using X-ray diffraction (XRD). The experimental results indicated that the spatial distribution of the residual stress in the laser-peened plate was the superposition of the LSP-induced elastoplastic stress and the elastic bending stress. Geometry thickness not only affected bending stiffness and macroscopic deformation but also played a significant role in the evolution of residual stress across the entire section. Under the identical peening conditions, a 3-mm plate inherited a 0.5-mm compression layer with approximately 180–280 MPa stress magnitude, whereas a 9-mm plate inherited a 1-mm compression layer with approximately 340–480 MPa of stress magnitude. Further analysis revealed that the elastic bending across the section had a certain compensation effect on the compressive stress of the peened surface. Thick plates (6–9 mm) tended to inherit consistent plane stress states because they demonstrated a relatively small deformation compatibility due to the high stiffness.</p>

Experimental Study of Tensile Behavior of LY12 Aluminium Alloy Processed by Laser Shot Peening and Laser Irradiation

Microstructural evolution and mechanical behaviors of Al-Cu-Li alloy processed by laser shock peening

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Comprehensive Analysis of Laser Peening Forming Effects on 5083 Aluminum Alloy

Analysis of microstructure and high-temperature tensile properties of 2060 Al-Li alloy strengthened by laser shock peening

In-Situ Tensile Deformation Behavior Of As-Built Laser Direct Metal Deposited Ti-6al-4v Alloy At 200 Degrees C

Influence of Process Parameters on the Interlaminar Shear Strength of CF/PEEK Composites In-Situ Consolidated by Laser-Assisted Automated Fiber Placement

On the Microstructure, Residual Stress and Fatigue Performance of Laser Metal Deposited TC17 Alloy Subjected to Laser Shock Peening

Laser shock peened Ti-6Al-4 V alloy: Experiments and modeling

Microstructural and texture evolution investigation of laser melting deposited TA15 alloy at 500?C using in-situ EBSD tensile test

Experimental and Numerical Studies of Fatigue Behavior of Ti6Al4V Alloy Treated by Laser Shock Peening

Microstructure evolution and mechanical properties of a lamellar near-α titanium alloy treated by laser shock peening

Laser shock peening regulating aluminum alloy surface residual stresses for enhancing the mechanical properties: Roles of shock number and energy

The effect of laser shock processing on the microstructures and properties of 2060 Al Li alloys

Strain rate dependence of tensile properties and strengthening mechanism of Ti6Al4V alloy undergoing different coverage layers of laser shock peening

Mechanical properties and strengthening mechanisms of Ti-6Al-4V treated by electro-pulsing assisted laser shock peening

Experimental research on global deformation and through-thickness residual stress in laser peen formed aluminum plates

The effect of laser shock peening on surface integrity and high and very high cycle fatigue properties of 2024-T351 aluminum alloy

Microstructure and residual stress modulation of 7075 aluminum alloy for improving fatigue performance by laser shock peening

Laser shock peening induced mechanical properties enhancement of 50CrVA alloy

Study of Anti-Laser Irradiation Performance of Shot-Peened 40crnimoa Alloy Steel