Influence of Melting Temperature on the Luminescence Properties of Bismuth-doped Barium Aluminosilicate Glasses
BAO Jia-xing,ZHOU Shi-feng,FENG Gao-feng,WANG Xi,LIN Geng,QIU Jian-rong
2007-01-01
Chinese Journal of Luminescence
Abstract:The influence of melting temperature on the luminescence properties of bismuth-doped barium alu- minosilicate glasses was studied.Bismuth-doped barium aluminosilicate glasses were prepared at various melt- ing temperatures.Absorption spectra,visible luminescence,infrared luminescence and fluorescent lifetime of the infrared luminescence of the glass samples were measured.There were two absorption peaks,one strong peak is at about 320 nm,and the other is at about 450 urn.The absorbance increased with increasing melting temperature.Visible luminescence was observed at about 420 nm,440 nm and 475 nm when excited by 380 nm ultraviolet light.The infrared luminescence was observed at about 1330 nm when excited by 808 nm laser diode (LD).The intensity of the visible luminescence decreased with increasing melting temperature,while the intensity of the infrared luminescence increased at first,and then decreased with a further increase of melt- ing temperature.But the fluorescent lifetime of the infrared luminescence decreased at first,and then in- creased with a further increase of melting temperature.The broadband infrared luminescence originates from bismuth ions,but is not due to high valence state ion of bismuth as suggested by Fujimoto et al.We attribute the visible and infrared luminescence to Bi~(3+) and Bi~+,respectively.The melting temperature may greatly in- fluence the broadband infrared luminescence of bismuth-doped glasses.It is necessary to choose best melting temperature for the preparation of bismuth-doped glasses.