Abstract:The influence of melting temperature on the luminescence properties of bismuth-doped barium alu- minosilicate glasses was studied.Bismuth-doped barium aluminosilicate glasses were prepared at various melt- ing temperatures.Absorption spectra,visible luminescence,infrared luminescence and fluorescent lifetime of the infrared luminescence of the glass samples were measured.There were two absorption peaks,one strong peak is at about 320 nm,and the other is at about 450 urn.The absorbance increased with increasing melting temperature.Visible luminescence was observed at about 420 nm,440 nm and 475 nm when excited by 380 nm ultraviolet light.The infrared luminescence was observed at about 1330 nm when excited by 808 nm laser diode (LD).The intensity of the visible luminescence decreased with increasing melting temperature,while the intensity of the infrared luminescence increased at first,and then decreased with a further increase of melt- ing temperature.But the fluorescent lifetime of the infrared luminescence decreased at first,and then in- creased with a further increase of melting temperature.The broadband infrared luminescence originates from bismuth ions,but is not due to high valence state ion of bismuth as suggested by Fujimoto et al.We attribute the visible and infrared luminescence to Bi~(3+) and Bi~+,respectively.The melting temperature may greatly in- fluence the broadband infrared luminescence of bismuth-doped glasses.It is necessary to choose best melting temperature for the preparation of bismuth-doped glasses.

Luminescence properties of nickel and bismuth co-doped barium aluminosilicate glasses

Infrared Luminescence Properties of Bismuth-Doped Barium Silicate Glasses

Luminescence properties of bismuth-doped lime silicate glasses

Effect of Various Alkaline-Earth Metal Oxides on the Broadband Infrared Luminescence from Bismuth-Doped Silicate Glasses

Influence of Melting Temperature on the Luminescence Properties of Bismuth-doped Barium Aluminosilicate Glasses

Influence of SiO2 on the Luminous Properties of Nd3+-Doped Barium Silicophosphate Nanostructured Glasses

Bismuth-doped zinc aluminosilicate glasses and glass-ceramics with ultra-broadband infrared luminescence

Inhomogeneous broadening, luminescence origin and optical amplification in bismuth-doped glass.

Effect of Si doping on near-infrared emission and energy transfer of Bismuth in silicate glasses

Abnormal Luminescence Behavior in Bi-Doped Borosilicate Glasses

White Luminescence of Tm–Dy Ions Co-Doped Aluminoborosilicate Glasses under UV Light Excitation

Infrared Broadband Emission of Bismuth-Doped Barium-Aluminum-borate Glasses.

Effect of SiO 2 on optical properties of bismuth-doped B 2 O 3 –GeO 2 –SiO 2 glasses

Effect of SiO2 on Optical Properties of Bismuth-Doped B2O3–GeO2–SiO2 Glasses

Tunable broadband luminescence of Bi‐ion‐doped glasses via Gd2O3 co‐doping

Near Infrared Broadband Emission of Bismuth-Doped Aluminophosphate Glass

Influence of B 2O 3 on broad infrared emissions from aluminosilicophosphate glass

Broadband Infrared Luminescence of Bismuth-Doped Borosilicate Glasses

Unusual luminescence quenching and reviving behavior of Bi-doped germanate glasses.

Investigation on the Spectral Characteristics of Bismuth Doped Silica Fibers

Ultra-broadband Infrared Luminescence of Bi-doped Thin-Films for Integrated Optics.