Synthesis and Analysis of Zn-Substituted CoCr2O4 Spinel Oxide
Yuliang Xu,Xiansong Liu,Xucai Kan,Shuangjiu Feng,Wei Wang,Chaocheng Liu,Yong Li
DOI: https://doi.org/10.1007/s10948-021-06099-z
2022-01-29
Journal of Superconductivity and Novel Magnetism
Abstract:A series of Zn-substituted CoCr2O4 spinel powders were prepared by solid-state reaction method. On this basis, the crystal structure and magnetic properties of CoCr2O4 powders were studied. By comparing the X-ray diffraction (XRD) pattern with the CoCr2O4 spinel standard card, it can be seen that the position of the main peak changes with the increase of zinc content and moves to the direction of higher Angle. In other words, with the increase of Zn displacement, the average grain size and lattice parameters also change. The crystal structure and magnetic properties of the materials were studied using the following instruments: scanning electron microscope (SEM) image can clearly see the uniform grain distribution. The chemical valence states of zinc, cobalt, and chromium ions fitted by X-ray photoelectron spectroscopy (XPS) are consistent with those reported in previous literature. The formation of spinel chromite can be clearly seen in the Fourier transformer infrared (FTIR) image. The hysteresis loop at 5 K shows that the saturation magnetization and coercivity decrease with the increase of Zn2+ content. At room temperature (300 K), the hysteresis loops of the five samples are linear. When x = 0.1 and 0.3, ZFC curve shows negative magnetization behavior across the temperature axis. The paramagnetic behavior also confirmed the pure spinel phase shown in the powder XRD profile.
physics, condensed matter, applied