Abstract:The main objective of this research was to investigate the effect of adding CuO (2 wt.%) nanoparticles and changing the cooling rate on the microstructure and mechanical properties of Al (2 wt.%) Si. The addition of CuO nanoparticles to Al-2wt.%Si (alloy A) resulted in a composite alloy (alloy B). Optical microscopy (OM), scanning electron microscopy (SEM) connected to an energy-dispersive spectrometer (EDS), x-ray diffraction (XRD), and positron annihilation Doppler broadening spectroscopy (PADBS) were used to examine the microstructure of alloys. Moreover, Vickers hardness and tensile tests were used to investigate the mechanical properties of the tested alloys. The G1 samples were cooled in the air to ~ 300 K and quenched G2 samples in cold water at 0 °C. The results showed that increasing the strain rate from 0.004 to 0.02 min −1 or decreasing the temperature from 503 to 423 K could increase the hardening parameters, yield stress ( σ y ), ultimate strength ( σ M ), and Young's modulus ( Y ) of all samples. Moreover, H V decreased as the aging temperature climbed from 423 to 503 K. Adding nano-sized CuO or cooling samples resulted in smaller grains. Furthermore, alloy B exhibited the formation of intermetallic compounds (IMCs) CuAl 2 and Cu 3 Si. The XRD data indicated the formation of phases in both alloys at 423, 463, and 503 K. In addition, the dislocation density, lattice strain, and average crystallite size were calculated. It can be seen from the activation energies and stress exponents that dislocation climbs through core diffusion as a control mechanism for both alloys. A significant positive relationship was observed between the value ( H v ) and PADBS parameters for all examined samples. The investigation showed that nano-sized CuO and a rapid cooling rate increased composite specimen hardness. This finding confirms that aluminum and its alloys play a crucial role in various technical applications.

DSC Analysis of the Effect of Processing Technique on the Dissolution/precipitation Reactions in a Hypereutectic Al−Si Alloy

The Effect of Heat Treatments on the Microstructural Evolution of Twin-Roll-Cast Al-Fe-Si Alloys

Effect of Scandium on Grain refinement mechanism and Mechanical Properties of Al-7Si-0.6Mg alloy at Different Cooling Rates

Effect of Microstructure on the Precipitation of β-Mg2Si during Cooling after Homogenisation of Al-Mg-Si Alloys

Grain Refinement of Al–Si Alloy (A356) by Melt Thermal Treatment

Investigating Thermal and Mechanical Characteristics of Die-Casting Aluminum Alloys: A Comprehensive Investigation via Thermal Analysis

Processing and Thermal Diffusivity Measurements of Compositionally Graded Al-12Si to Al2O3 Structures

Microstructure evolution of a novel low-silicon cast aluminum alloy modified with Mn and Cr during solution treatment

Effect of CuO Nanostructure Addition and Cooling Rate on the Microstructure and Mechanical Characteristics of Hypoeutectic Al-2wt.%Si Alloy

Effect of Casting Process and Thermal Exposure on Microstructure and Mechanical Properties of Al-Si-Cu-Ni Alloy

Continuous cooling and isothermal solidification analysis of AlSi10Mg using differential fast scanning calorimetry

Effect of solution heat treatment on the internal architecture and compressive strength of an AlMg4.7Si8 alloy

Study on the Effect of Pre-Refinement and Heat Treatment on the Microstructure and Properties of Hypoeutectic Al-Si-Mg Alloy

Control of High-Temperature Static and Transient Thermomechanical Behavior of SiMo Ductile Iron by Al Alloying

Influence of heat treatment on morphology and quantity of eutectic phases of Al alloys with different cooling rates

Microstructure and Thermal Conductivity of Hypereutectic Al-High Si Produced by Casting and Spray Deposition

Effect of Si addition on the precipitation and mechanical/electrical properties of dilute Al-Zr-Sc alloys

Primary phase evolution of rheo-processed ADC12 aluminum alloy

Effect of cooling rates and heat treatment time on Si phase of AlSi10Mg alloy manufactured by selective laser melting: Microstructure evolution and strengthening mechanism

DSC Study on the Age -Precipitation Behaviorof Al-4.5 Cu Alloy and Mullite-fiber Reinforced Al-4.5 Cu Composite

Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe Alloy