DSC Study on the Age -Precipitation Behaviorof Al-4.5 Cu Alloy and Mullite-fiber Reinforced Al-4.5 Cu Composite

Jian Long

2002-01-01

Abstract:The age _ precipitation behavior of Al-4.5 Cu alloy and mullite _ fiber reinforced Al-4.5 Cu composite has been studied by the differential scanning calorimetry (DSC). It is shown that the DSC thermogram of the quenched composite differs from that of the quenched monolithic base alloy. Onset of GP zone formation and dis_solution can clearly be observed on the DSC curves of the Al-4.5 Cu alloy, but can hardly be confirmed on the DSC curves of the mullite _ fiber reinforced Al-4.5 Cu composite. It implies that mullite fibers delay or suppress the formation of the GP zone. The precipitation of θ″ and θ′ phases is greatly accelerated due to the introduction of mullite fibers. It results in a descent of peak temperature, a decrease in activation energy, and an acceleration of ageing precipitation. However, it should be emphasized that age _ precipitation sequence could be misjudged, if scanning parameters are not properly chosen with much caution.